An approach was developed to calculate the crack susceptibility under various levels of pressure, and the corresponding numerical method was presented. The binary Al–Si alloy system was selected for study because the effect of high pressure on its phase diagram has been reported. The results showed a higher pressure can lead to a higher crack susceptibility and shift the most crack susceptible composition to higher solute contents. It was found a higher pressure can increase the effect of back diffusion on the solidification path and hence the crack susceptibility. This study provides a new understanding of the effect of pressure on solidification cracking susceptibility and can be a relevant starting point for studying solidification cracking under high pressures.
KouS.Welding Metallurgy. 2nd ed.Hoboken: Wiley; 2013; p. 257–300.
2.
CrossCE.On the origin of weld solidification cracking/hot cracking phenomena in welds. Berlin (Heidelberg): Springer; 2005; 3–18.
3.
LiuJ, KouS.Effect of diffusion on susceptibility to cracking during solidification. Acta Mater. 2015; 100:359–368. doi: 10.1016/j.actamat.2015.08.064
4.
FeurerU.Quality control of engineering alloys and the role of metals science. Delft: Delft University of Technology; 1977; 131–45.
5.
PelliniWS.Strain theory of hot tearing. Foundry. 1952; 80(11):125–133.
6.
ClyneTW, DaviesGJ.Proc. Conf. on Solidification and Castings of Metals, Metals Society, London, 1979; 275–278.
7.
KatgermanL.A mathematical model for hot cracking of aluminum alloys during DC casting. JOM. 1982; 34(2):46–49. doi: 10.1007/BF03339110
8.
ProkhorovNN.Resistance to hot tearing of cast metals during solidification. Russ Cast Prod. 1962; 2(2):172–175.
9.
NovikovII.Hot cracking of nonferrous metals and alloys. Moscow: Nauka; 1966.
10.
MagninB, KatgermanL, HannartB. In: CrossM, CampbellJ, editors. Modeling of casting welding and Advanced solidification Processes VII. Warrendale (PA): TMS; 1995. p. 303–310.
11.
RappazM, DrezetJM, GremaudM.A new hot-tearing criterion. Metall Mater Trans A. 1999; 30(2):449–455. doi: 10.1007/s11661-999-0334-z
12.
KouS.A criterion for cracking during solidification. Acta Mater. 2015; 88:366–374. doi: 10.1016/j.actamat.2015.01.034
13.
GengS, JiangP, ShaoX, Effects of back-diffusion on solidification cracking susceptibility of Al-Mg alloys during welding: a phase-field study. Acta Mater. 2018; 160:85–96. doi: 10.1016/j.actamat.2018.08.057
14.
GengS, JiangP, ShaoX, Comparison of solidification cracking susceptibility between Al-Mg and Al-Cu alloys during welding: a phase-field study. Scr Mater. 2018; 150:120–124. doi: 10.1016/j.scriptamat.2018.03.013
15.
YangZ, WangK, FuP, Influence of alloying elements on hot tearing susceptibility of Mg–Zn alloys based on thermodynamic calculation and experimental. J Magnes Alloy. 2018; 6(1):44–51. doi: 10.1016/j.jma.2018.01.001
16.
Pandat. Phase diagram calculation software package for multicomponent systems. Madison (WI): Computherm LLC; 2001; p. 53719.
LiuJ, KouS.Crack susceptibility of binary aluminum alloys during solidification. Acta Mater. 2016; 110:84–94. doi: 10.1016/j.actamat.2016.03.030
19.
LiuJ, KouS.Susceptibility of ternary aluminum alloys to cracking during solidification. Acta Mater. 2017; 125:513–523. doi: 10.1016/j.actamat.2016.12.028
20.
KouS.A simple index for predicting the susceptibility to solidification cracking. Weld J. 2015; 94(94):374s–388s.
21.
LiuJ, DuarteHP, KouS.Evidence of back diffusion reducing cracking during solidification. Acta Mater. 2017; 122:47–59. doi: 10.1016/j.actamat.2016.09.037
22.
ŁabanowskiJ, FydrychD, RogalskiG.Underwater welding – a review. Adv Mater Sci. 2008; 8(3):11–22.
23.
OhkuboM, TokisueH, AndoS, The effects of casting pressure applied during squeeze casting of aluminium alloys on the properties of welds made by electron beam welding. Weld Inter. 1992; 6(2):96–103. doi: 10.1080/09507119209548153
24.
BerryJT, LuckR, ZhangB, The effect of applied pressure during feeding of critical cast aluminum alloy components with particular reference to fatigue resistance. Starkville: Mississippi State University (US); 2003.
MinaminoY, YamaneT, SatoT, Phase diagram of Al-Si system under 21,000 bar. J Jpn Inst Light Metals. 1988; 38(12):800–806. doi: 10.2464/jilm.38.800
27.
KurzW, FisherDJ.Fundamentals of solidification. 4th ed. Aedermannsdorf: Trans Tech Publications; 1998; p.234–235.
28.
SchmitzJ, HallstedtB, BrilloJ, Density and thermal expansion of liquid Al–Si alloys. J Mater Sci. 2012; 47(8):3706–3712. doi: 10.1007/s10853-011-6219-8
29.
LiuX, OikawaK.Assessment of temperature and pressure dependence of molar volume and phase diagrams of binary Al–Si Systems. Mater Trans. 2014; 55(11):1673–1682. doi: 10.2320/matertrans.MAW201407
30.
DörnerP, HenigET, KriegH, Optimization and calculation of the binary system Al-Si. Calphad. 1980; 4(4):241–254. doi: 10.1016/0364-5916(80)90010-3