CuCrZr alloy (Cu-0.8wt-%Cr-0.1wt-%Zr) and 316L stainless steel (Fe-0.03wt-%C-16wt-%Cr-10wt-%Ni) plates were successfully friction stir lap welded resulting in significant mechanical mixing of the two matrix elements, Cu and Fe, in the stir zone. The severe mixing not only led to improved load bearing response but also leads to form Cu-rich and Fe-rich regions in the weld nugget. The formation of these phases governs the failure mechanism of the joint. Tensile properties of the weld showed promising response when compared with joints made for the similar alloy pair by other welding techniques. This suggests strong feasibility of applying FSW for joining Cu and steel for nuclear applications.
MishraRS, MaZY.Friction stir welding and processing. Mater Sci Eng R Reports. 2005; 50:1–78. doi: 10.1016/j.mser.2005.07.001
2.
DavisJW, KalininGM.Material properties and design requirements for copper alloys used in ITER. J Nucl Mater. 1998; 258–263:323–328. doi: 10.1016/S0022-3115(98)00270-0
3.
LipaM, DurocherA, TiveyR, The use of copper alloy CuCrZr as a structural material for actively cooled plasma facing and in vessel components. Fusion Eng Des. 2005; 75–79:469–473. doi: 10.1016/j.fusengdes.2005.06.056
4.
IvanovAD, SatoS, Le MaroisG.Evaluation of hot isostatic pressing for joining of fusion reactor structural components. J Nucl Mater. 2000; 283–287:35–42. doi: 10.1016/S0022-3115(00)00329-9
5.
GoodsSH, PuskarJD.Solid state bonding of CuCrZr to 316L stainless steel for ITER applications. Fusion Eng Des. 2011; 86:1634–1638. doi: 10.1016/j.fusengdes.2010.12.051
6.
WeiR, ZhaoSX, DongH, Enhancing the CuCrZr/316L HIP-joint by Ni electroplating. Fusion Eng Des. 2017; 117:58–62. doi: 10.1016/j.fusengdes.2017.02.039
7.
DurgutluA, GülençB, FindikF.Examination of copper/stainless steel joints formed by explosive welding. Mater Des. 2005; 26:497–507. doi: 10.1016/j.matdes.2004.07.021
8.
GervashA, MazulI, YablokovN.Study of alternative SS / Cu-alloy joining methods for ITER. Fusion Eng Des. 2001; 56-57:381–384. doi: 10.1016/S0920-3796(01)00333-7
9.
BatraIS, KaleGB, SahaTK, Diffusion bonding of a Cu-Cr-Zr alloy to stainless steel and tungsten using nickel as an interlayer. Mater Sci Eng A. 2004; 369:119–123. doi: 10.1016/j.msea.2003.10.296
10.
SinghKP, PatelA, BhopeK, Optimization of the diffusion bonding parameters for SS316L/CuCrZr with and without nickel interlayer. Fusion Eng Des. 2016; 112:274–282. doi: 10.1016/j.fusengdes.2016.09.004
11.
WangP, ChenJ, LiQ, Study on the microstructure and properties evolution of CuCrZr/316LN-IG explosion bonding for ITER first wall components. Fusion Eng Des. 2017; 124:1135–1139. doi: 10.1016/j.fusengdes.2017.02.030
12.
SahlotP, JhaK, DeyGK, Quantitative wear analysis of H13 steel tool during friction stir welding of Cu-0.8%Cr-0.1%Zr alloy. Wear. 2017; 378–379:82–89. doi: 10.1016/j.wear.2017.02.009
13.
WangT, ShuklaS, Nene SSMF, Towards obtaining sound butt joint between metallurgically immiscible pure Cu and stainless steel through friction stir welding. Met Mater Trans A. 2018; 49A:2578–2582. doi: 10.1007/s11661-018-4637-9
14.
PalanivelS, AroraA, DohertyKJ, A framework for shear driven dissolution of thermally stable particles during friction stir welding and processing. Mater Sci Eng A. 2016; 678:308–314. doi: 10.1016/j.msea.2016.10.015