The weldability of a newly developed stainless steel was investigated by comparing with hot-dipped galvanised dual phase and low carbon steels in a two-sheet stack-up of similar metal. The weld lobes, mechanical properties, weld morphology, microstructures and microhardness profiles of the welds made with the three materials were comparatively discussed. Results showed that significant softening was observed in the stainless steel weld nugget. Compared to the dual phase steel and low carbon steel, the stainless steel has a very narrow weld lobe but requires lower welding current and shorter welding time, and the stainless steel weld performed better mechanical properties in the case of welds with same nugget size, but it tended to exhibit interfacial fracture in tensile shear tests.
Technical Transfer Dispatch #6 – body structure materials, ULSAB-AVC Consortium, 2001.
2.
De MoorE, GibbsPJ, SpeerJG, Strategies for third-generation advanced high-strength steel development. AIST Trans. 2010; 7(3):1–13.
3.
TumuluruMD.Resistance spot welding of coated high-strength dual phase steels. Weld J. 2006; 85(8):31–37.
4.
RashidMS.Dual phase steels.Annu Rev Mater Sci. 1981; 11:245–266. doi: 10.1146/annurev.ms.11.080181.001333
5.
RashidMS, RaoBVN.Tempering characteristics of a vanadium containing dual-phase steel. In: KotRA, BramfittBL, editors. Fundamentals of dual-phase steels. Warrendale (PA): TMS-AIME; 1981. p. 246–264.
6.
BrookeL, EvansH.Lighten Up!Autom Eng Int. 2009; 316–22.
7.
SachdevAK.Effect of retained austenite on the yielding and deformation behavior of a dual phase steel. Acta Metall. 1983; 31(12):2037–2042. doi: 10.1016/0001-6160(83)90021-4
8.
ShenQ, LiYB, LinZQ, Effect of external constant magnetic field on weld nugget of resistance spot welded dual-phase steel DP590. IEEE Trans Magn. 2011; 47(10):4116–4119. doi: 10.1109/TMAG.2011.2157316
9.
Saha PodderA, BhanjaA.Applications of stainless steel in automobile industry. Adv Mat Res. 2013; 794:731–740.
10.
OlsonDL.Prediction of austenitic weld metal microstructure and properties. Weld J. 1985; 10:281–295.
11.
AslanlarS.The effect of nucleus size on mechanical properties in electrical resistance spot welding of sheets used in automotive industry. Mater Des. 2006; 27(2):125–131. doi: 10.1016/j.matdes.2004.09.025
12.
AslanlarS, Effect of welding current on mechanical properties of galvanized chromided steel sheets in electrical resistance spot welding. Mater Des. 2007; 28(1):2–7. doi: 10.1016/j.matdes.2005.06.022
13.
PouranvariM, Alizadeh-ShM, MarashiSP.Welding metallurgy of stainless steels during resistance spot welding part I: fusion zone. Sci Technol Weld Joining. 2015; 20(6):502–511. doi: 10.1179/1362171815Y.0000000015
14.
Alizadeh-ShM, PouranvariM, MarashiSP.Welding metallurgy of stainless steels during resistance spot welding part II–heat affected zone and mechanical performance. Sci Technol Weld Joining. 2015; 20(6):512–521. doi: 10.1179/1362171815Y.0000000010
15.
Alizadeh-ShM, MarashiSPH, PouranvariM.Resistance spot welding of AISI 430 ferritic stainless steel: phase transformations and mechanical properties. Mater Des. 2014; 56:258–263. doi: 10.1016/j.matdes.2013.11.022
16.
Alizadeh-ShM, FalsafiF, MarashiSPH, Laser spot welding of AISI 304L: metallurgical and mechanical properties. Ironmaking Steelmaking. 2014; 41(3):161–165. doi: 10.1179/1743281213Y.0000000112
17.
VashishthaH, TaiwadeRV, KhatirkarRK, Effect of austenitic fillers on microstructural and mechanical properties of ultra-low nickel austenitic stainless steel. Sci Technol Weld Joining. 2016; 21(4):331–337. doi: 10.1080/13621718.2015.1112604
18.
PouranvariM, RanjbarnoodehE.Effect of welding current on energy absorption of AISI304 resistance spot welds. Res J App Sci Eng Technol. 2012; 4(17):2911–2914.
KumarS, ShahiAS.Effect of heat input on the microstructure and mechanical properties of gas tungsten arc welded AISI 304 stainless steel joints. Mater Des. 2011; 32:3617–3623. doi: 10.1016/j.matdes.2011.02.017
21.
LiHB, JiangZH, FengH, Microstructure, mechanical and corrosion properties of friction stir welded high nitrogen nickel-free austenitic stainless steel. Mater Des. 2015; 84:291–299. doi: 10.1016/j.matdes.2015.06.103
22.
SocietyAW.Recommended practices for test methods for evaluating the resistance spot welding behavior of automotive sheet steel materials. ANSI/AWS/SAE/D89-97. Miami (ML): AWS; 1997.
23.
LippoldJC, KoteckiDJ.Welding metallurgy and weldability of stainless steels. Hoboken (NJ): John Wiley & Sons; 2005.
24.
DavidSA.Ferrite morphology and variations in ferrite content in austenitic stainless steel welds. Weld J.1981; 60(4):63–71.
25.
ElmerJW, AllenSM, EagarTW.The influence of cooling rate on the ferrite content of stainless steel alloys. Proceedings of the 2nd International Conference on Trends in Welding Research, 1989, Gatlinburg (TN).
26.
MaryaM, GaydenXQ.Development of requirements for resistance spot welding dual-phase (DP600) steels part I – the causes of interfacial fracture. Weld J. 2005; 84(11):172–182.
27.
PouranvariM, MarashiSPH.Failure mode transition in AISI 304 resistance spot welds. Welding and Joining. 2012; 91(11):303-s–309-s.