An ingenious experimental programme by combining artificially thickened oxide layer as marker material and ‘stop-action’ welding were used to study the material flow and defect formation in friction stir welding of aluminium alloys. The results showed that material flow around the pin on the advancing side (AS) was severer than that on the retreating side (RS) and the fastest velocity of material flow in the middle stir zone (SZ) was 43.9 mm s−1. Moreover, the material under the RS shoulder included extruded metal only and the material under the AS shoulder included extruded and rotated metal. Lastly, instantaneous void occurrence and insufficient inflow material were reasons for the preferential formation of void defects in the top SZ on the AS.
HajihashemiM, ShamanianM, NiroumandB.Microstructure and mechanical properties of Al-6061-T6 alloy welded by a new hybrid FSW/SSW joining process. Sci Technol Weld Join. 2016; 21:493–503. doi: 10.1080/13621718.2015.1138019
2.
MishraRS, MaZY.Friction stir welding and processing. Mater Sci Eng R. 2005; 50:1–78. doi: 10.1016/j.mser.2005.07.001
ZengXH, XueP, WangD, Realising equal strength welding to parent metal in precipitation-hardened Al–Mg–Si alloy via low heat input friction stir welding. Sci Technol Weld Join. 2018. DOI:10.1080/13621718.2017.1415249.
6.
ZhangZ, XiaoBL, WangD, Effect of Alclad layer on material flow and defect formation in friction-stir-welded 2024 aluminum alloy. Metall Mater Trans A. 2011; 42:1717–1726. doi: 10.1007/s11661-010-0545-3
7.
MahmoudTS.Surface modification of A390 hypereutectic Al–Si cast alloys using friction stir processing. Surf Coat Tech. 2013; 228:209–220. doi: 10.1016/j.surfcoat.2013.04.031
8.
ZhangH, LinSB, WuL, Defects formation procedure and mathematic model for defect free friction stir welding of magnesium alloy. Mater Des. 2006; 27:805–809. doi: 10.1016/j.matdes.2005.01.016
9.
ArbegastWJ.A flow-partitioned deformation zone model for defect formation during friction stir welding. Scr Mater. 2008; 58:372–376. doi: 10.1016/j.scriptamat.2007.10.031
10.
LiuXC, WuCS, PadhyGK.Characterization of plastic deformation and material flow in ultrasonic vibration enhanced friction stir welding. Scr Mater. 2015; 102:95–98. doi: 10.1016/j.scriptamat.2015.02.022
11.
XuS, DengXM.A study of texture patterns in friction stir welds. Acta Mater. 2008; 56:1326–1341. doi: 10.1016/j.actamat.2007.11.016
12.
ArbegastWJ.Modeling friction stir joining as a metalworking process. In: Jin Z, Beaudoin A, Bieler TA, Radhakrishnan B, editor. Hot Deformation of Aluminum Alloys III; The Minerals, Metals and Materials Society Annual Meeting, San Diego, CA, March 2–6. Warrendale, PA: Minerals, Metals & Materials Society, 2003. p. 313–327.
13.
LiuXC, WuCS.Elimination of tunnel defect in ultrasonic vibration enhanced friction stir welding. Mater Des. 2016; 90:350–358. doi: 10.1016/j.matdes.2015.10.131
14.
HeurtierP, JonesMJ, DesrayaudC, Mechanical and thermal modelling of friction stir welding. J Mater Process Tech. 2006; 171:348–357. doi: 10.1016/j.jmatprotec.2005.07.014
15.
MehtaM, AroraA, DeA, Tool geometry for friction stir welding—optimum shoulder diameter. Metall Mater Trans A. 2011; 42:2716–2722. doi: 10.1007/s11661-011-0672-5
16.
ChenZW, PasangT, QiY.Shear flow and formation of Nugget zone during friction stir welding of aluminium alloy 5083-O. Mater Sci Eng A. 2008; 474:312–316. doi: 10.1016/j.msea.2007.05.074
17.
GerlichA, SuP, YamamotoM, Material flow and intermixing during dissimilar friction stir welding. Sci Technol Weld Join. 2008; 13:254–264. doi: 10.1179/174329308X283910
18.
KumarK, KailasSV.The role of friction stir welding tool on material flow and weld formation. Mater Sci Eng A. 2008; 485:367–374. doi: 10.1016/j.msea.2007.08.013
19.
LiWY, LiJF, ZhangZH, Metal flow during friction stir welding of 7075-T651 aluminum alloy. Exp Mech. 2013; 53:1573–1582. doi: 10.1007/s11340-013-9760-3
20.
LiY, MurrLE, McClureJC.Flow visualization and residual microstructures associated with the friction-stir welding of 2024 aluminum to 6061 aluminum. Mater Sci Eng A. 1999; 271:213–223. doi: 10.1016/S0921-5093(99)00204-X
21.
LiuHJ, ZhangHJ, YuL.Effect of welding speed on microstructures and mechanical properties of underwater friction stir welded 2219 aluminum alloy. Mater Des. 2011; 32:1548–1553. doi: 10.1016/j.matdes.2010.09.032
22.
MukherjeeS, GhoshAK.Flow visualization and estimation of strain and strain-rate during friction stir process. Mater Sci Eng A. 2010; 527:5130–5135. doi: 10.1016/j.msea.2010.04.091
23.
PalanivelR, MathewsPK, MuruganN.Optimization of process parameters to maximize ultimate tensile strength of friction stir welded dissimilar aluminum alloys using response surface methodology. J Cent South Univ. 2013; 20:2929–2938. doi: 10.1007/s11771-013-1815-1
24.
TruebaL, HerediaG, RybickiD, Effect of tool shoulder features on defects and tensile properties of friction stir welded aluminum 6061-T6. J Mater Process Tech. 2015; 219:271–277. doi: 10.1016/j.jmatprotec.2014.12.027
25.
ZhangZ, XiaoBL, MaZY.Influence of water cooling on microstructure and mechanical properties of friction stir welded 2014Al-T6 joints. Mater Sci Eng A. 2014; 614:6–15. doi: 10.1016/j.msea.2014.06.093
26.
ZhaoYH, LinSB, WuL, The influence of pin geometry on bonding and mechanical properties in friction stir weld 2014 Al alloy. Mater Lett. 2005; 59:2948–2952. doi: 10.1016/j.matlet.2005.04.048
27.
BalasubramanianV.Relationship between base metal properties and friction stir welding process parameters. Mater Sci Eng A. 2008; 480:397–403. doi: 10.1016/j.msea.2007.07.048
28.
ColliganK.Material flow behavior during friction stir welding of aluminum. Weld J. 1999; 78:229–237.
29.
KadianAK, BiswasP.A comparative study of material flow behavior in friction stir welding using laminar and turbulent models. J Mater Eng Perform. 2015; 24:4119–4127. doi: 10.1007/s11665-015-1520-3
30.
PashazadehH, TeimournezhadJ, MasoumiA.Numerical investigation on the mechanical, thermal, metallurgical and material flow characteristics in friction stir welding of copper sheets with experimental verification. Mater Des. 2014; 55:619–632. doi: 10.1016/j.matdes.2013.09.028
31.
MorisadaY, FujiiH, KawahitoY, Three-dimensional visualization of material flow during friction stir welding by two pairs of X-ray transmission systems. Scr Mater. 2011; 65:1085–1088. doi: 10.1016/j.scriptamat.2011.09.021
32.
SchmidtHNB, DickersonTL, HattelJH.Material flow in butt friction stir welds in AA2024-T3. Acta Mater. 2006; 54:1199–1209. doi: 10.1016/j.actamat.2005.10.052
33.
MorisadaY, ImaizumiT, FujiiH.Clarification of material flow and defect formation during friction stir welding. Sci Technol Weld Join. 2015; 20:130–137. doi: 10.1179/1362171814Y.0000000266
34.
PrangnellPB, HeasonCP.Grain structure formation during friction stir welding observed by the ‘stop action technique’. Acta Mater. 2005; 53:3179–3192. doi: 10.1016/j.actamat.2005.03.044
35.
ShiL, WuCS, LiuHJ.Modeling the material flow and heat transfer in reverse dual-rotation friction stir welding. J Mater Eng Perform. 2014; 23:2918–2929. doi: 10.1007/s11665-014-1042-4