The paper addresses the process–microstructure–performance relationships in resistance spot welding of a martensitic advanced high strength steel. Significant softening was observed in the heat affected zone (HAZ) due to allotriomorphic ferrite formation in the inter-critical HAZ and tempering of martensite in sub-critical HAZ (SCHAZ), with the latter plays more important role in mechanical properties of the spot welds. The strain concentration associated with the HAZ softening promotes initiation of pullout failure from the soft SCHAZ. While, the peak load in the interfacial failure mode is governed by the fusion zone size, that of the pullout mode is significantly affected by the HAZ softening. To improve weldability of martensitic steels, the HAZ softening should be minimised via modifications in welding process or steel chemistry.
CoomanBCD. Structure-properties relationship in TRIP steels containing carbide-free bainite. Curr Opin Solid State Mater Sci. 2004; 8:285–303. doi: 10.1016/j.cossms.2004.10.002
2.
KuziakR, KawallaR, WaeglerS. Advanced high strength steels for automotive industry. Arch Civ Mech Eng. 2008; 8:103–117. doi: 10.1016/S1644-9665(12)60197-6
3.
ZuidemaBK. Bridging the design–manufacturing–materials data gap: material properties for optimum design and manufacturing performance in light vehicle steel-intensive body structures. JOM. 2012; 64:1039–1047. doi: 10.1007/s11837-012-0405-2
4.
TamarelliCM. The evolving use of advanced high-strength steels for automotive applications. Southfield (MI): Steel Market Development Institute (SMDI); 2011.
WeiST, LiuRD, LvD, . Effect of joint configuration on resistance spot weldability of galvanised DP780 steel sheets. Sci Technol Weld Join. 2016; 21:178–185. doi: 10.1179/1362171815Y.0000000081
7.
UijlNJD, SmithS. Resistance spot welding of advanced high strength steels for the automotive industry. In: ZhangW, EderA, editors. Proceedings of the 4th international seminar on advances in resistance welding. Wels, Austria: SWANTEC Software and Engineering ApS and FRONIUS International GmbH; 2006. p. 30–60.
8.
GouldJE, KhuranaSP, LiT. Predictions of microstructures when welding automotive advanced high-strength steels. Weld J. 2006; 85:111s–116s.
9.
YangYP, GouldJ, PetersonW, . Development of spot weld failure parameters for full vehicle crash modelling. Sci Technol Weld Join. 2013; 18:222–231. doi: 10.1179/1362171812Y.0000000082
PouranvariM. Susceptibility to interfacial failure mode in similar and dissimilar resistance spot welds of DP600 dual phase steel and low carbon steel during cross-tension and tensile-shear loading conditions. Mater Sci Eng A. 2012; 546:129–138. doi: 10.1016/j.msea.2012.03.040
12.
PouranvariM, MarashiSPH, MousavizadehSM. Failure mode transition and mechanical properties of similar and dissimilar resistance spot welds of DP600 and low carbon steels. Sci Technol Weld Join. 2010; 15:625–631. doi: 10.1179/136217110X12813393169534
13.
DancetteS, Massardier-JourdanV, FabregueD, . HAZ microstructures and local mechanical properties of high strength steels resistance spot welds. ISIJ Int. 2011; 51:99–107. doi: 10.2355/isijinternational.51.99
PouranvariM, MarashiSPH. Failure mode transition in AHSS resistance spot welds. Part I. Controlling factors. Mater Sci Eng A. 2011; 528(29):8337–8343. doi:doi: 10.1016/j.msea.2011.08.017
JongY, LeeY, KimD, . Microstructural evolution and mechanical properties of resistance spot welded ultra high strength steel containing boron. Mater Trans. 2011; 52:1330–1333. doi: 10.2320/matertrans.M2011005
18.
Lopez-CortezVH, Reyes-ValdesFA. Understanding resistance spot welding of advanced high-strength steels. Weld J. 2008; 87(12):36–40.
19.
VignierS, BiroE, HervéM. Predicting the hardness profile across resistance spot welds in martensitic steels. Weld World. 2014; 58:297–305. doi: 10.1007/s40194-014-0116-0
20.
SafanamaDS, MarashiSPH, PouranvariM. Similar and dissimilar resistance spot welding of martensitic advanced high strength steel and low carbon steel: metallurgical characteristics and failure mode transition. Sci Technol Weld Join. 2012; 17:288–94. doi: 10.1179/1362171812Y.0000000006
21.
BlondeauR, MaynierPh, DolletJ, . Estimation of hardness, strength and elastic limit of c- and low-alloy steels from their composition and heat treatment. Memoires Scientifiques Rev Metallurg. 1975; 72:759–769.
22.
KitaharaH, UejiR, TsujiN, . Crystallographic features of lath martensite in low-carbon steel. Acta Mater. 2006; 54:1279–1288. doi: 10.1016/j.actamat.2005.11.001
KraussG.Steels: processing, structure and performance. Materials Park, OH: ASM International; 2005.
25.
NayakSS, Baltazar HernandezVH, ZhouY. Effect of chemistry on nonisothermal tempering and softening of dual-phase steels. Metall Mater Trans A. 2011; 42:3242–3248. doi: 10.1007/s11661-011-0868-8
26.
Baltazar HernandezVH, PandaSK, OkitaY, . A study on heat affected zone softening in resistance spot welded dual phase steel by nanoindentation. J Mater Sci. 2010; 45:1638–1647. doi: 10.1007/s10853-009-4141-0
27.
Baltazar HernandezVH, NayakSS, ZhouY. Tempering of martensite in dual-phase steels and its effects on softening behavior. Metall Mater Trans A. 2011; 42:3115–3129. doi: 10.1007/s11661-011-0739-3