Joining feasibility of aluminium alloy to polypropylene sheets via friction stir lap joining was examined. Effects of heat-input on microstructure and mechanical behaviour of the joints were investigated. A covering plate was used to confine flow of molten polymer. The results showed a distinctive interaction layer at polymer/aluminium interface, consisted mainly of C, O and Al. Shear strength of the joints decreased by enhancement of the heat-input due to increase in the thickness of the interaction layer as well as the gap width between this layer and both aluminium and polymer matrices. Maximum shear-tensile strength of 5.1MPa (∼20% of polymer shear strength) was obtained, which was higher than or comparable to that of the joints produced by other processes.
Amancio-FilhoS. and dos SantosJ.: ‘Joining of polymers and polymer–metal hybrid structures: recent developments and trends’, Polym. Eng. Sci., 2009, 49, 1461–1476. doi: 10.1002/pen.21424
2.
LiuF. C., LiaoJ. and NakataK.: ‘Joining of metal to plastic using friction lap welding’, Mater. Des., 2014, 54, 236–244. doi: 10.1016/j.matdes.2013.08.056
3.
KhodabakhshiF., HaghshenasM., SahraiinejadS., ChenJ., ShalchiB., LiJ. and GerlichA.: ‘Microstructure-property characterization of a friction-stir welded joint between AA5059 aluminum alloy and high density polyethylene’, Mater. Charact., 2014, 98, 73–82. doi: 10.1016/j.matchar.2014.10.013
4.
LiuF. C., NakataK., LiaoJ., HirotaS. and FukuiH.: ‘Reducing bubbles in friction lap welded joint of magnesium alloy and polyamide’, Sci. Technol. Weld. Join., 2014, 19, 578–587. doi: 10.1179/1362171814Y.0000000228
RamarathnamG., LibertucciM., SadowskiM. M. and NorthT. H.: ‘Joining of polymers to metal’, Weld. J., 1992, 71, 483–490.
7.
Amancio-FilhoS., BuenoC., dos SantosJ., HuberN. and HageE.Jr.: ‘On the feasibility of friction spot joining in magnesium/fiber-reinforced polymer composite hybrid structures’, Mater. Sci. Eng. A, 2011, 528, 3841–3848. doi: 10.1016/j.msea.2011.01.085
8.
NagatsukaK., YoshidaS., TsuchiyaA. and NakataK.: ‘Direct joining of carbon-fiber-reinforced plastic to an aluminum alloy using friction lap joining’, Composites Part B, 2015, 73, 82–88. doi: 10.1016/j.compositesb.2014.12.029
9.
KrügerS., WagnerG. and EiflerD.: ‘Ultrasonic welding of metal/composite joints’, Adv. Eng. Mater., 2004, 6, 157–159. doi: 10.1002/adem.200300539
10.
BalleF., WagnerG. and EiflerD.: ‘Ultrasonic metal welding of aluminium sheets to carbon fibre reinforced thermoplastic composites’, Adv. Eng. Mater., 2009, 11, 35–39. doi: 10.1002/adem.200800271
11.
YusofF., MiyashitaY., SeoN., MutohY. and MoshwanR.: ‘Utilising friction spot joining for dissimilar joint between aluminium alloy (A5052) and polyethylene terephthalate’, Sci. Technol. Weld. Join., 2012, 17, 544–549. doi: 10.1179/136217112x13408696326530
12.
ChenY. C. and NakataK.: ‘Friction stir lap joining aluminum and magnesium alloys’, Scr. Mater., 2008, 58, 433–436. doi: 10.1016/j.scriptamat.2007.10.033
13.
RatanathavornW. and MelanderA.: ‘Dissimilar joining between aluminum alloy (AA 6111) and thermoplastics using friction stir welding’, Sci. Technol. Weld. Join., 2015, 20, 222–228. doi: 10.1179/1362171814Y.0000000276
14.
BooneM. J.: ‘Mechanical testing of epoxy adhesives for naval applications’, MSc Thesis, University of Maine, Orono, Maine, USA, 2002, 40–88.
15.
ASTM D1002-05: ‘Standard test method for apparent shear strength of single-lap-joint adhesively bonded metal specimens by tension loading (metal-to-metal)’, 2014, ASTM International, West Conshohocken, PA, USA.
16.
CallejaF. J. B. and FakirovS.: ‘Microhardness of polymers’, 238; 2000, Cambridge, Cambridge University Press.
17.
MishraR. and MahoneyM.: ‘Friction stir welding and processing’, 53–64; 2007, Materials Park, OH, ASM International.
18.
ArbegastW. J. and HartleyP. J.: ‘Friction stir weld technology development at lockheed martin michoud space systems – an overview’, Proc. 5th Int. Conf. on ‘Trends in welding research’, Pine Mountain, GA, USA, June 1998, 541–546.
19.
CheonJ. and NaS. J.: ‘Relation of joint strength and polymer molecular structure in laser assisted metal and polymer joining’, Sci. Technol. Weld. Join., 2014, 19, 631–637. doi: 10.1179/1362171814Y.0000000236