Controlling centre segregation and shrinkage cavities without internal crack in as-cast bloom of steel GCr15 induced by soft reduction technologies

Abstract

To investigate the alleviation technology of internal cracks, center shrinkage cavities and center segregation of as-cast bloom simultaneously, a three-dimensional finite element model was developed to calculate and analyze the strain fields and deformation behavior of as-cast bloom induced by soft reduction process. In the present work, a multi-stage mechanical soft reduction (MSR) has been developed to simultaneously alleviate center segregation and shrinkage cavities without internal cracks, which aims to provide theoretical basis for improving the internal quality of high carbon as-cast blooms induced by soft reduction technologies. According to the experimental results, the internal cracks were effectively alleviated and center shrinkage cavities were nearly eliminated by optimum designed experiments, the homogeneity and compactness of as-cast bloom can been remarkably improved in comparison with that induced by the conventional soft reduction process. The carbide size and bandwidth of the carbides in the hot-rolled wire were both decreased.

Get full access to this article

View all access options for this article.

References

Bhadeshia

HKDH.

Steels for bearings. Prog Mater Sci. 2012;57(2):268–435.

Domitner

Kharicha

et al. Modeling the effects of strand surface bulging and mechanical soft reduction on macrosegregation formation in steel continuous casting. Metall Mater Trans A. 2014;45(3):1415–1434.

Zong

Zhang

Liu

et al. Analysis of the off-corner subsurface cracks of continuous casting blooms under the influence of soft reduction and controllable approaches by a chamfer technology. Metall Res Technol. 2019;116:310–322.

Zong

Zhang

Wang

et al. Application of a chamfer slab technology to reduce internal cracks of continuous casting bloom during soft reduction process. Metall Res Technol. 2019;116:608–617.

Luo

Zhu

MY.

Analysis and application of soft reduction amount for bloom continuous casting process. ISIJ Int. 2014;54(3):504–510.

Zong

Liu

et al. A review of chamfer technology in continuous casting process. Metall Res Technol. 2020;117:204–219.

Sun

Wang

et al. Coordinating optimisation of F-EMS and soft reduction during bloom continuous casting process for special steel. Ironmak Steelmak. 2018;45(8):708–713.

Ludlow

Normanton

Anderson

et al. Strategy to minimise central segregation in high carbon steel grades during billet casting. Ironmak Steelmak. 2005;32(1):68–74.

Sun

Cheng

et al. Reduction in macrosegregation on 380 mm×490 mm bloom caster equipped combination M + F-EMS by optimising casting speed. Ironmak Steelmak. 2015;42(6):439–449.

10.

Arakere

Gigacycle rolling contact fatigue of bearing steels: a review. Int J Fatigue. 2016;93(2):238–249.

11.

Won

Yeo

Seol

et al. A new criterion for internal crack formation in continuously cast steels. Metall Mater Trans B. 2000;31(4):779–794.

12.

Ding

Tang

et al. Formation of internal cracks during soft reduction in rectangular bloom continuous casting. Int J Miner Metall Mater. 2012;19(1):21–29.

13.

Zhu

Thermo-mechanical behavior of the continuous casting bloom in the heavy reduction process. JOM. 2016;68(2):3107–3115.

14.

et al. Design and application of CSC-roll for heavy reduction of the bloom continuous casting process. Metall Mater Trans B. 2019;50B:110–122.

15.

Zhu

Closure of internal porosity in continuous casting bloom during heavy reduction process. Metall Mater Trans B. 2019;50B:2867–2882.

16.

Zong

Zhang

Liu

et al. Analysis on morphology and stress concentration in continuous casting bloom to learn the formation and propagation of internal cracks induced by soft reduction technology. Ironmak Steelmak. 2019;46(9):872–885.

17.

Wang

et al. Constitutive modeling of the flow stress of GCr15 continuous casting bloom in the heavy reduction process. Metall Mater Trans B. 2018;49:767–782.