Improvement of centre segregation in continuous casting bloom and the resulting carbide homogeneity in bearing steel GCr15

Abstract

In the present work, solidification structure and centre segregation in continuously cast bearing steel GCr15 blooms with 220mm×260 mm were obtained by different casting conditions (M-EMS, M + F-EMS, M + F-EMS + MSR), which were systematically optimized by numerical simulation and experiments. The relationship between centre segregation in continuously cast GCr15 bloom, heredity in hot-rolled steel and carbide inhomogeneity of hot-rolled steel with was investigated comprehensively. Results showed that compared with M-EMS, centre carbon segregation ratio in the bloom decreased from 1.1∼1.4 to 1.04∼1.22 by M + F-EMS, and could be reduced to 0.96∼1.08 by MSR in combination with M + F-EMS. Moreover, centre segregation in hot-rolled steel decreased with the decrease of centre segregation in bloom. Grade of network and banded carbide in hot-rolled steel decreased accordingly, especially for centre carbon segregation ratio with 0.96∼1.08, grade of network and banded carbide could be significantly reduced to 1. It was important to control centre segregation in as-cast steel to improve the resulting carbide homogeneity of as-rolled steel. According to the experimental results, higher casting speed in bloom with M + F-EMS and MSR integrated process was preferred to effectively reduce centre segregation ratio and further decreased the occurrence of network and banded carbide in as-rolled bearing steel GC15.

Get full access to this article

View all access options for this article.

References

Bhadeshia

HKDH.

Steels for bearings. Prog Mater Sci. 2012;57(2):268–435. doi: 10.1016/j.pmatsci.2011.06.002

Bhattacharyya

Subhash

Arakere

Evolution of subsurface plastic zone due to rolling contact fatigue of M-50NiL case hardened bearing steel. Int J Fatigue. 2014;59:102–113. doi: 10.1016/j.ijfatigue.2013.09.010

Mosleh

Bradshaw

Belk

et al. Fatigue failure of all-steel and steel–silicon nitride rolling ball combinations. Wear. 2011;271(9):2471–2476. doi: 10.1016/j.wear.2010.12.051

Mosleh

Bradshaw

Role of component configuration in evaluation of accelerated rolling contact fatigue of ball bearings. Wear. 2011;271(10):2681–2686. doi: 10.1016/j.wear.2011.01.092

Failure analysis of GCr15SiMn steel bearing sleeve. Eng Fail Anal. 2006;13(5):857–865. doi: 10.1016/j.engfailanal.2005.02.020

Wang

Zhou

Micro-crack initiation and propagation in a high strength aluminum alloy during very high cycle fatigue. Mater Sci Eng A. 2018;715:404–413. doi: 10.1016/j.msea.2018.01.008

Guan

Wang

Zhang

et al. Effects of non-metallic inclusions on the crack propagation in bearing steel. Tribol Int. 2017;106:123–131. doi: 10.1016/j.triboint.2016.10.030

Guan

Wang

Zhang

Fatigue crack nucleation and propagation at clustered metallic carbides in M50 bearing steel. Tribol Int. 2018;119:165–174. doi: 10.1016/j.triboint.2017.10.016

Bao

Gan

An experimental study on the impact of deoxidation methods on the fatigue properties of bearing steels. Steel Res Int. 2018;89:1–8.

10.

Zhang

Effect of banded carbide structure on the rolling contact fatigue of GCr15 bearing steel. Adv Eng Res. 2017;141:528–535.

11.

Kim

Park

Kim

et al. Role of spheroidized carbides on the fatigue life of bearing steel. Met Mater Int. 2012;18(6):917–921. doi: 10.1007/s12540-012-7002-3

12.

Stickels C

Carbide refining heat treatments for 52100 bearing steel. Metall Trans. 1974;5:865–874. doi: 10.1007/BF02643140

13.

Liu

Cui

Shang

et al. Comparative study on the microstructure characteristics and enhanced mechanical properties of spray formed GCr15 bearing steel. Steel Res Int. 2018;89:1–7.

14.

Sun

Cheng

et al. Reduction in macro segregation on 380 mm×490mm bloom caster equipped combination M + FEMS by optimizing casting speed. Ironmak Steelmak. 2015;42(6):439–449. doi: 10.1179/1743281214Y.0000000247

15.

Bao

Wang

et al. Electromagnetic torque detecting for optimization of in-mold electromagnetic stirring in the billet and bloom continuous casting. Ironmak Steelmak. 2018. doi: 10.1080/03019233.2018.1522755

16.

Ludlow

Normanton

Anderson

et al. Strategy to minimize central segregation in high carbon steel grades during billet casting. Ironmak Steelmak. 2005;32(1):68–74. doi: 10.1179/174328105X23978

17.

Demons

Lorraine

Taylor

et al. Effects of heat treatments on steels for bearing applications. Mater Eng Perform. 2007;16:592. doi: 10.1007/s11665-007-9075-6

18.

Sun

Effect of ultra-fast cooling on microstructure of large section rods of bearing steel. J Iron Steel Res Int. 2009;16:61. doi: 10.1016/S1006-706X(10)60012-X

19.

Lee

Hong

Kang

et al. Grain refinement in bearing steels using a double-quenching heat-treatment process. Int J Automot Technol. 2009;10:697. doi: 10.1007/s12239-009-0082-5

20.

Han

Zhao

et al. Effect of proeutectoid carbide on heredity in microstructure mechanical properties and fatigue life of GCr15 bearing steel. Metall Res Technol. 2017;114:1–8.

21.

Bao

Wang

et al. Reducing macro segregation of high carbon steel in continuous casting bloom by final electromagnetic stirring and mechanical soft reduction integrated process. Metall Res Technol. 2017;114(405):1–12.

22.

Mao

Tao

Jiang

A few important problems of electromagnetic stirring for continuous casting of billet. Steelmaking. 2008;24(4):16–20.

23.

Bode

Schwerdtfeger

Geck

HG.

Influence of casting parameters on void volume and center segregation in continuously cast 100Cr6 blooms. Ironmak Steelmak. 2008;35(2):137–145. doi: 10.1179/030192307X233511