This research examines the effects of using a combination of Ground Granulated Blast furnace Slag (GGBS) and Hydrated Lime (HL) as alternative cement ingredients on the mechanical and microstructural properties of ternary mixed concrete (Ordinary Portland Cement (OPC)+GGBS+HL). The OPC was replaced with GGBS in increments of 10% from 10% to 70%, while HL was substituted at levels ranging from 0% to 20% in increments of 10%. The results showed that the highest compressive strength (56.20 MPa), split tensile strength (4.25 MPa), and flexural strength (5.58 MPa) were observed for the ternary concrete mixture containing 60% OPC, 30% GGBS, and 10% HL with 0.36 water binder ratio after 28 days of curing.
OnerAAkyuzS.An experimental study on optimum usage of GGBS for the compressive strength of concrete. Cem Concr Compos. 2007;29(6):505–514.
2.
AliLAliBAliA.Combined effects of supplementary cementitious materials (silica fume, GGBS, fly ash and rice husk ash) and steel fiber on the hardened properties of recycled aggregate concrete. Constr Build Mater. 2023;263(2020):120636. doi:10.1016/j.conbuildmat.2020.120636.
3.
TaylorRRichardsonIGBrydsonRMD.Cement and concrete research composition and microstructure of 20-year-old ordinary Portland cement – ground granulated blast-furnace slag blends containing 0 to 100% slag. Cem Concr Res. 2010;40(7):971–983. doi:10.1016/j.cemconres.2010.02.012.
4.
NandanamKBiswalUSDinakarP.Effect of Fly Ash, GGBS, and Metakaolin on mechanical and durability properties of self-compacting concrete made with 100% coarse recycled aggregate. J Hazard Toxic Radioact Waste. 2021;25(2):1–15.
5.
PengYMaKLongGEffect of packing density according to CPM on the rheology of cement – fly ash – slag paste. J Mater Civ Eng. 2021;33(8):1–16.
6.
Lizarazo-marriagaJClaissePGanjianE.Effect of steel slag and Portland cement in the rate of hydration and strength of blast furnace slag pastes. J Mater Civ Eng. 2011;23(February):153–160.
7.
ElchalakaniMBasarirHKarrechA.Green concrete with high-volume fly ash and slag with recycled aggregate and recycled water to build future sustainable cities. J Mater Civ Eng. 2017;29(2):1–12.
8.
TangKBeattieGWilkinsonS. Effects of curing temperature on the hydration of GGBS concrete and the use of electron microscope particle analysis. 2017.
9.
ChaitanyaMManikandanPPrem KumarVPrediction of self-healing characteristics of GGBS admixed concrete using artificial neural network. J Phys: Conf Ser.2020;1716:012019. doi:10.1088/1742-6596/1716/1/012019.
10.
LalDChatterjeeADwivediA.Investigation of properties of cement mortar incorporating pond ash – an environmental sustainable material. Constr Build Mater. 2019;209:20–31. doi:10.1016/j.conbuildmat.2019.03.049.
11.
RahmanABaraiASarkerALight weight concrete from rice husk ash and glass powder. Bangladesh J Sci Ind Res. 2018;53(3):225–232.
12.
ManikandanPSelijaKVasugiVAn artificial neural network based prediction of mechanical and durability characteristics of sustainable geopolymer composite. Adv Civ Eng. 2022;2022:1–15.
13.
DadsetanSBaiJ.Mechanical and microstructural properties of self-compacting concrete blended with metakaolin, ground granulated blast-furnace slag and fly ash. Constr Build Mater. 2017;146:658–667. doi:10.1016/j.conbuildmat.2017.04.158.
14.
ManikandanPVasugiV.A critical review of waste glass powder as an aluminosilicate source material for sustainable geopolymer concrete production.Silicon. 2021;13:3649–3663.doi:10.1007/s12633-020-00929-w.
15.
RoychandRSilvaSDSetungeS.Nanosilica modified high-volume fly ash and slag cement composite: environmentally friendly alternative to OPC. J Mater Civ Eng. 2018;30(4):1–12.
GuoXPhDShiH.Utilization of steel slag powder as a combined admixture with ground granulated blast-furnace slag in cement based materials. J Mat Civ Eng. 2013;16(December):1990–1993.
18.
SiddiqueR.Utilization (recycling) of iron and steel industry by-product (GGBS) in concrete: strength and durability properties. J Mater Cycles Waste Manag. 2014;16:460–467.
19.
ErdemirMIbrahimH.Utilization and efficiency of ground granulated blast furnace slag on concrete properties – a review. Constr Build Mater. 2016;105:423–434.
20.
VasugiVManikandanP.The potential use of waste glass powder in slag based geopolymer concrete – an environmental friendly material. Int J Environ Waste Manag. 2022;1(1):1.
21.
ManikandanPNatrayanLDuraimuruganSInfluence of waste glass powder as an aluminosilicate precursor in synthesizing ternary blended alkali-activated binder. Silicon. 2022;14:0123456789. doi:10.1007/s12633-021-01533-2.
22.
DaiJWangQXieCThe effect of fineness on the hydration activity index of ground granulated blast furnace slag. Materials. 2019;12:1–15.
23.
SamadSShahALimbachiyaMC.Strength development characteristics of concrete produced with blended cement using ground granulated blast furnace slag (GGBS) under various curing conditions. Sādhanā. 2017;42(7):1203–1213.
24.
AydınSTürkelSYazıcıHMechanical properties of reactive powder concrete containing high volumes of ground granulated blast furnace slag. Cem Concr Compos. 2010;32:639–648.
25.
SalujaSKaurKGoyalSLong-term drying shrinkage of GGBFS-incorporated RCC under various temperature exposures. J Mater Civ Eng. 2021;33(6):1–14.
26.
Al-oranAAASafieeNAMohdNA.Fresh and hardened properties of self-compacting concrete using metakaolin and GGBS as cement replacement. Eur J Environ Civ Eng. 2019;0(0):1–14. doi:10.1080/19648189.2019.1663268.
27.
BasumajumdarADasAKBandyopadhyayNSome studies on the reaction between fly ash and lime. Bull Mater Sci. 2005;28(2):131–136.
28.
ShahMUUsmanMHanifMUUtilization of solid waste from brick industry and hydrated lime in self-compacting cement pastes. Materials (Basel). 2021;14(5):1–23.
29.
KangSHKwonYHHongSGHydrated lime activation on byproducts for eco-friendly production of structural mortars. J Clean Prod. 2019;231:1389–1398. doi:10.1016/j.jclepro.2019.05.313.
30.
NetoAAMCincottoMARepetteW.Mechanical properties, drying and autogenous shrinkage of blast furnace slag activated with hydrated lime and gypsum. Cem Concr Compos. 2010;32(4):312–318. doi:10.1016/j.cemconcomp.2010.01.004.
31.
BIS:7320-1974. Specifications for concrete slump test apparatus. Bur Indian Stand New Delhi, India. 1974;(Reaffirmed 2008):1–14.
32.
IS 516:2014. Method of tests for strength of concrete. Bur Indian Stand New Delhi. 2004.
33.
KisanMSangathanSNehruJ 1999.
34.
CardosoFAFernandesHCPileggiRGCarbide lime and industrial hydrated lime characterization carbide lime and industrial hydrated lime characterization. Powder Technol. 2009;195(2):143–149. doi:10.1016/j.powtec.2009.05.017.
35.
Manikandan PVV.Potential utilization of waste glass powder as a precursor material in synthesizing ecofriendly ternary blended geopolymer matrix. J Clean Prod. 2022;355(August 2021):131860, doi:10.1016/j.jclepro.2022.131860.
36.
AdesinaPAOlutogeFA.Structural properties of sustainable concrete developed using rice husk ash and hydrated lime. J Build Eng. 2019;25(May):100804, doi:10.1016/j.jobe.2019.100804.
37.
BarbhuiyaAequzksaRussellPambmi.Properties of fly ash concrete modified with hydrated lime and silica fume. Constr Build Mater. 2009;23(10):3233–3239. doi:10.1016/j.conbuildmat.2009.06.001.
38.
PavíaSAlyM.Influence of aggregate and supplementary cementitious materials on the properties of hydrated lime (CL90s) mortars. Mater Construcc. 2016;66(324):1–10.
39.
NicholsANicholsJ. The use of hydrated lime in concrete as a cement replacement: Effect on Compressive Strength. 2012;(November 2018).
40.
MajhiRKNayakAN.Production of sustainable concrete utilising high-volume blast furnace slag and recycled aggregate with lime activator. J Clean Prod. 2020;255:120188, doi:10.1016/j.jclepro.2020.120188.
41.
GaoJMQianCXLiuHFITZ microstructure of concrete containing GGBS. Cem Concr Res. 2005;35(March 2004):1299–1304.
42.
KaradumpaCSPancharathiRK.Influence of particle packing theories on strength and microstructure properties of composite cement – based mortars. J Mat Civ Eng. 2021;33(10):1–15.
43.
GrovesGW.Microstructure and microanalysis of hardened cement pastes involving ground granulated blast-furnace slag. J Mater Sci. 1992;27:6204–6212.
44.
CheeCKokCRamliMThe engineering properties and microstructure development of cement mortar containing high volume of inter-grinded GGBS and PFA cured at ambient temperature. Constr Build Mater. 2016;122:683–693. doi:10.1016/j.conbuildmat.2016.06.105.