It is challenging to obtain successful bonding between cemented tungsten carbide and steel due to the large differences in their physical and mechanical properties. We used spark plasma sintering (SPS) technique and successfully bonded WC-10Co and AISI4340 high-strength steel at a low temperature. The effects of sintering time (5–20 min with a gap of 5 min) on their diffusion bonding were examined. The microstructure of the bonded composite materials was evaluated, and formed phases were identified. The mechanical properties were investigated, and the importance of processing parameters of SPS was discussed. The results show a crack-free continuous metallurgical bonding achieved at 1000°C, and the bonding strength increased with increasing holding times of 5, 10, 15, and 20 min. The sintered WC-10Co powders obtained nearly full density (99.07%) with an average maximum hardness of 1763 HV5. A special arrangement was used to determine the tensile bonding-strength with maximum average of 152 MPa at 20 min.
HasanMZhaoJJiangZ.Micromanufacturing of composite materials: a review. Int J Extreme Manuf. 2019;1(1):012004.
2.
PascalCThomazicAAntoni-ZdziobekAPressureless co-sintering behaviour of a steel/cemented carbide component: model bimaterial. Int J Mater Res. 2012;103(3):296–308.
3.
HasanMZhaoJJiaFOptimisation of sintering parameters for bonding nanocrystalline cemented tungsten carbide powder and solid high strength steel. Compos Interfaces. 2020: 1–16.
4.
HaghshenasMSParvinNAmirnasiriA.Effect of bonding temperature on microstructure and mechanical properties of WC–Co/steel diffusion brazed joint. Trans Indian Inst Met. 2018;71(3):649–658.
5.
LeeWBKwonBDJungSB.Effect of bonding time on joint properties of vacuum brazed WC – Co hard metal/carbon steel using stacked Cu and Ni alloy as insert metal. Mater Sci Technol. 2004;20(11):1474–1478.
6.
GassmannRC.Laser cladding with (WC + W2C)/Co–Cr–C and (WC + W2C)/Ni–B–Si composites for enhanced abrasive wear resistance. Mater Sci Technol. 1996;12(8):691–696.
7.
PascalCChaixJ-MDoréFDesign of multimaterial processed by powder metallurgy: processing of a (steel/cemented carbides) bilayer material. J Mater Process Technol. 2009;209(3):1254–1261.
8.
WuT-FLeeS-LChenM-HEffects of tungsten carbide and cobalt particles on corrosion and wear behaviour of copper matrix composite. Mater Sci Technol. 2005;21(3):295–304.
9.
FengKChenHXiongJInvestigation on diffusion bonding of functionally graded WC–Co/Ni composite and stainless steel. Mater Des. 2013;46:622–626.
10.
JungY-IHIP joining of tungsten armor to ferritic-martensitic steel with a zirconium interlayer. Fusion Sci Technol. 2017;72(3):523–529.
11.
HasanMZhaoJHuangZAnalysis of sintering and bonding of ultrafine WC powder and stainless steel by hot compaction diffusion bonding. Fusion Eng Des. 2018;133:39–50.
12.
HasanMZhaoJHuangZEffects of holding time on the sintering of cemented tungsten carbide powder and bonding with high-strength steel wire. J Mater Eng Perform. 2019;28(7):4074–4085.
13.
HasanMHuangZZhaoJMicrostructural evaluation of WC and steel dissimilar bilayered composite obtained by spark plasma sintering. Int J Adv Manuf Technol. 2020;111(9):2405–2418.
14.
ZafarSSharmaAK.Development and characterisations of WC–12Co microwave clad. Mater Charact. 2014;96:241–248.
15.
ThomazicAPascalCChaixJM. Fabrication of (cemented carbides/steel) bilayered materials by powder metallurgy. Materials Science Forum. 2010. Trans Tech Publ.
16.
LeeW-BKwonB-DJungS-B.Effects of Cr3C2 on the microstructure and mechanical properties of the brazed joints between WC–Co and carbon steel. Int J Refract Met Hard Mater. 2006;24(3):215–221.
17.
BaoJNewkirkJWBaoS.Wear-resistant WC composite hard coatings by brazing. J Mater Eng Perform. 2004;13(4):385–388.
18.
GiménezSHuangSGVan der BiestOChemical reactivity of PVD-coated WC–Co tools with steel. Appl Surf Sci. 2007;253(7):3547–3556.
19.
ZhongZHinokiTNozawaTMicrostructure and mechanical properties of diffusion bonded joints between tungsten and F82H steel using a titanium interlayer. J Alloys Compd. 2010;489(2):545–551.
20.
BarrenaMDe SalazarJGMatesanzL.Interfacial microstructure and mechanical strength of WC–Co/90MnCrV8 cold work tool steel diffusion bonded joint with Cu/Ni electroplated interlayer. Mater Des. 2010;31(7):3389–3394.
21.
HasanMZhaoJHuangZAnalysis and characterisation of WC-10Co and AISI 4340 steel bimetal composite produced by powder–solid diffusion bonding. Int J Adv Manuf Technol. 2019;103(9):3247–3263.
22.
SivaprahasamDChandrasekarSSundaresanR.Microstructure and mechanical properties of nanocrystalline WC–12Co consolidated by spark plasma sintering. Int J Refract Met Hard Mater. 2007;25(2):144–152.
23.
MissiaenJMRaharijaonaJJAntoniADesign of a W/steel functionally graded material for plasma facing components of DEMO. J Nucl Mater. 2011;416(3):262–269.
24.
PascalC.ChaixJ.M.DuttA Elaboration of (steel/cemented carbide) multimaterial by powder metallurgy. Materials Science Forum. 2007. Trans Tech Publ.
25.
TakemotoSNitta‡HIijima§YDiffusion of tungsten in α-iron. Philos Mag. 2007;87(11):1619–1629.
26.
ErikssonMRadwanMShenZ.Spark plasma sintering of WC, cemented carbide and functional graded materials. Int J Refract Met Hard Mater. 2013;36:31–37.
27.
LiuXSongXZhangJTemperature distribution and neck formation of WC–Co combined particles during spark plasma sintering. Mater Sci Eng A. 2008;488(1):1–7.
HuangSGVanmeenselKLiLTailored sintering of VC-doped WC–Co cemented carbides by pulsed electric current sintering. Int J Refract Met Hard Mater. 2008;26(3):256–262.
30.
ChaSIHongSHKimBK.Spark plasma sintering behavior of nanocrystalline WC–10Co cemented carbide powders. Mater Sci Eng A. 2003;351(1–2):31–38.
31.
AsanoHBandoYNakanishiNOrder-disorder transformation of Fe–Co alloys in fine particles. Trans Jpn Inst Met. 1967;8(3):180–184.
32.
PerssonK. Materials Data on Fe3Co (SG:123) by Materials Project. 2016, LBNL Materials Project; Lawrence Berkeley National Lab. (LBNL), Berkeley, CA.
33.
LiuDSLiuRPWeiYH.Influence of tungsten on microstructure and wear resistance of iron base hardfacing alloy. Mater Sci Technol. 2014;30(3):316–322.
34.
McCammonCRingwoodAJacksonI.Thermodynamics of the system Fe–FeO–MgO at high pressure and temperature and a model for formation of the earth's core. Geophys J Int. 1983;72(3):577–595.
35.
CollinsGSMeevesBH.Formation of FeCo by mechanical alloying. Scr Metall Mater. 1993;29(10.
36.
Goren-MuginsteinGBergerSRosenA.Sintering study of nanocrystalline tungsten carbide powders. Nanostruct Mater. 1998;10(5):795–804.
37.
FangZZWangXRyuTSynthesis, sintering, and mechanical properties of nanocrystalline cemented tungsten carbide – a review. Int J Refract Met Hard Mater. 2009;27(2):288–299.
38.
AskouriNAFremlinJH.Hardening of tungsten carbide tools by charged particle irradiation. Metals Technology. 1975;2(1):538–541.
39.
HasanMZhaoJJiangZAnalysis and characterisation of WC-10Co and AISI 4340 steel bimetal composite produced by powder–solid diffusion bonding. Int J Adv Manuf Technol. 2019: 1–17.