In order to reduce critical impact velocity and enlarge weldability window of aluminium/steel explosive welding, a chemical copper plating layer as interlayer was proposed to carry out aluminium/steel explosive welding. The results showed that the interface of the 1060/Q235 composite plate had good bonding performance, and no obvious defects such as cracks and pores were found. Copper plating as intermediate layer could enlarge aluminium/steel weldability window. The thickness of solidified melt was much thicker than that of diffusion zone. The molten copper particles participated in the formation of re-entry jet, which rotated under the action of initial jet. The presence of the Cu layer reduces the occurrence of excessive melting during welding and improves the properties of the interface.
ZhangHJiaoKXZhangJLComparisons of the microstructures and micro-mechanical properties of copper/steel explosive-bonded wave interfaces. Mater Sci Eng A. 2019;756:430–441.
2.
YangMMaHHShenZWDissimilar material welding of tantalum foil and Q235 steel plate using improved explosive welding technique. Mater Des. 2020;186:108348.
3.
ZahediADarianiBMMirniaMJ.Experimental determination and numerical prediction of necking and fracture forming limit curves of laminated Al/Cu sheets using a damage plasticity model. Int J Mech Sci. 2019;153–154:341–358.
4.
LiangHLLuoNShenTExperimental and numerical simulation study of Zr-based BMG/Al composites manufactured by underwater explosive welding. J Mater Res Technol. 2020;9:1539–1548.
5.
BorońskiDSkibickiAMaćkowiakPModeling and analysis of thin-walled Al/steel explosion welded transition joints for shipbuilding applications. Mar Struct. 2020;74:102843.
6.
ZengXYWangYXLiXQEffect of inert gas-shielding on the interface and mechanical properties of Mg/Al explosive welding composite plate. J Manuf Process. 2019;45:166–175.
7.
LiangHLNingLLiXJJoining of Zr60Ti17Cu12Ni11 bulk metallic glass and aluminum 1060 by underwater explosive welding method. J Manuf Process. 2019;45:115–122.
8.
YangMXuJFMaHHMicrostructure development during explosive welding of metal foil: morphologies, mechanical behaviors and mechanisms. Composites Part B. 2021;212:108685.
9.
YangMMaHHShenZWMicrostructure and mechanical properties of Al−Fe meshing bonding interfaces manufactured by explosive welding. Trans Nonferrous Met Soc China. 2019;29:680–691.
10.
ZhouGAXuJFShenZWMicrostructure and mechanical properties of simultaneously explosively-welded steel/Cu pipes and Al/Cu pipe/rod. J Manuf Process. 2019;47:244–253.
11.
ParchuriPKotegawaSYamamotoHBenefits of intermediate-layer formation at the interface of Nb/Cu and Ta/ Cu explosive clads. Mater Des. 2019;166:107610.
12.
LiuKYChenPWChunRInvestigation on the interfacial microstructure and mechanical properties of the W-Cu joints fabricated by hot explosive welding. J Mater Process Technol. 2022;300:117400.
13.
PaulHChulistRBobrowskiPMicrostructure and properties of the interfacial region in explosively welded and post-annealed titanium-copper sheets. Mater Charact. 2020;167:110520.
14.
PaulHSkuzaWChulistRThe effect of interface morphology on the electro-mechanical properties of Ti/Cu clad composites produced by explosive welding. Metall Mater Trans A. 2020;51A:750–766.
15.
BiXZLiXJYangKExperimental and numerical studies of titanium foil/steel explosively welded clad plate. Def Technol. 2022; doi:10.1016/j.dt.2022.05.001.
16.
CarvalhoGHSFLGalvãoIMendesRExplosive welding of aluminium to stainless steel using carbon steel and niobium interlayers. J Mater Process Technol. 2020;283:116707.
17.
PaulHChulistRLityńska-DobrzyńskaLInterfacial reactions and microstructure related properties of explosively welded tantalum and steel sheets with copper interlayer. Mater Des. 2021;208:109873.
18.
ChenXInaoDTanakaSExplosive welding of Al alloys and high strength duplex stainless steel by controlling energetic conditions. J Manuf Process. 2020;58:1318–1333.
19.
KwaśniakPGarbaczH.Ab initio study of the influence of alloying elements on stability and mechanical properties of selected tixaly intermetallic compounds and their TixAly/Al, TixAly/Ti interfaces in explosively welded metal–metal composites. Metall Mater Trans A. 2021;52A:5032–5042.
20.
ZhangTTWangWXYanZFInterfacial morphology and bonding mechanism of explosive weld joints. Chin J Mech Eng. 2021;34:8.
21.
RoostaeiMDarabiR.Investigation on formability of three-layer joined Al/Cu/Al sheets annealed at different temperature. Mater Sci Technol. 2020;36:1476–1486.
22.
WuZZongLSunL.A mie- Grüneisen mixture Eulerian model for underwater explosion. Eng Computation. 2014;31:425–452.
23.
AbdulazeemMS.Shock and detonation properties of solid explosives with gaseous products. Hazard Mater. 2010;177:372–376.
24.
ZhangXLuoBWuGYield behavior of polystyrene at strain rate 106/s under quasi-isentropic compression. Mech Mater. 2018;124:1–6.
25.
YohJJMcClellandMAMaienscheinJLTest-based thermal explosion model for HMX. Proc Combust Inst. 2007;31:2353–2359.
26.
SwiftDCSeifterAHoltkampDBShock and release temperatures in molybdenum: experiment and theory. Phys Rev B. 2007;76:54122.
27.
MousaviSAAARiahiMParastAH.Experimental and numerical analyses of explosive free forming. J Mater Process Technol. 2007;187–188:512–516.
28.
RushtonNSchleyerGKClaytonAMInternal explosive loading of steel pipes. Thin Wall Struct. 2008;46:870–877.
29.
WalshJMShrefflerRGWilligFJ.Limiting conditions for jet formation in high velocity collisions. J Appl Phys. 1953;24:349–359.
30.
YangMMaHHShenZW.Study on the effects of explosive covering on explosive welding of stainless steel to steel. Propellants Explos Pyrotech. 2019;44:609–616.
31.
YangMMaHHShenZW.Study on self-restrained explosive welding with high energy efficiency. Int J Adv Manuf Tech. 2018;99:3123–3132.
32.
DeribasAAKudinovMFlM.Effect of the initial parameters on the process of wave formation in explosive welding. Combust Explos Shock Waves. 1967;3:344–348.
33.
ZhouQLiuRZouQMicrostructure characterization and tensile shear failure mechanism of the bonding interface of explosively welded titanium-steel composite. Mater Sci Eng, A. 2021;820:141559.
34.
ZhangTWangWZhouJMolecular dynamics simulations and experimental investigations of atomic diffusion behavior at bonding interface in an explosively welded Al/Mg alloy composite plate. Acta Metall Sin. 2017;30:983–991.
35.
PaulHPetrzakPChulistREffect of impact loading and heat treatment on microstructure and properties of multi-layered AZ31/AA1050 plates fabricated by single-shot explosive welding. Mater Des. 2022;214:110411.
36.
FuYSLuoKXZhaoPLDynamic behavior of Cu/Al-laminated metal with impedance mismatch. J Mater Eng Perform. 2022: 1–10.
37.
LiHZYangYLiangXPEffect of annealing temperature and time on the microstructure, mechanical properties and conductivity of cold-rolled explosive Cu/Al composite sheets. Mater Res Express. 2020;7:106502.