In this research, the hypereutectic Al–20Si alloy, containing an optimised amount of 4 wt-% γ-Al2O3 and 0.1 wt-% strontium, was successfully synthesised through the suction casting process. The cooling rate (563 K s−1) involved during solidification was estimated by measuring secondary dendritic arm spacing. As a result, a significant change in the morphology of silicon was observed and also led to the formation of a small fraction of refined α-Al throughout the microstructure. The work demonstrates that high tensile properties in hypereutectic Al–20Si alloys can be achieved without the use of conventional inoculants (such as phosphorus). The suction cast Al–20Si alloy exhibits remarkably enhanced tensile properties of average ultimate tensile strength of 355 MPa and average ductility of 7.1%.
HaoYGaoBTuGFSurface modification of Al-20Si alloy by high current pulsed electron beam. Appl Surf Sci. 2011; 257:3913–3919. doi: 10.1016/j.apsusc.2010.11.118
2.
GuptaMLingS.Microstructure and mechanical properties of hypo/hyper-eutectic Al–Si alloys synthesized using a near-net shape forming technique. J Alloys Compd. 1999; 287:284–294. doi: 10.1016/S0925-8388(99)00062-6
3.
MandalAAcharyaM.Effect of strontium and Misch metal on Al–14Si–3Mg alloy. Trans Indian Inst Met. 2015; 68:1181–1185. doi: 10.1007/s12666-015-0673-y
4.
ShiWXGaoBTuGFEffect of Nd on microstructure and wear resistance of hypereutectic Al–20%Si alloy. J Alloys Compd. 2010; 508:480–485. doi: 10.1016/j.jallcom.2010.08.098
5.
LiQXiaTLanYEffect of rare earth cerium addition on the microstructure and tensile properties of hypereutectic Al–20%Si alloy. J Alloys Compd. 2013; 562:25–32. doi: 10.1016/j.jallcom.2013.02.016
6.
LiQXiaTLanYEffect of in situ γ-Al2O3 particles on the microstructure of hypereutectic Al–20%Si alloy. J Alloys Compd. 2013; 577:232–236. doi: 10.1016/j.jallcom.2013.04.043
7.
LiQXiaTLanYEffects of rare earth Er addition on microstructure and mechanical properties of hypereutectic Al–20% Si alloy. Mater Sci Eng A. 2013; 588:97–102. doi: 10.1016/j.msea.2013.09.017
8.
FengHKYuSRLiYLEffect of ultrasonic treatment on microstructures of hypereutectic Al–Si alloy. J Mater Process Technol. 2008; 208:330–335. doi: 10.1016/j.jmatprotec.2007.12.121
9.
VijeeshVPrabhuKN.Review of microstructure evolution in hypereutectic Al–Si alloys and its effect on wear properties. Trans Indian Inst Met. 2014; 67:1–18. doi: 10.1007/s12666-014-0379-6
10.
SunJZhangLWuGRefinement of primary Si in Al – 20% Si alloy by MRB through phosphorus additions. J Mater Process Technol. 2015; 225:485–491. doi: 10.1016/j.jmatprotec.2015.06.031
11.
LiBWangHJieJEffects of yttrium and heat treatment on the microstructure and tensile properties of Al–7.5Si–0.5Mg alloy. Mater Des. 2011; 32:1617–1622. doi: 10.1016/j.matdes.2010.08.040
12.
JeonJHShinJHBaeDH.Si phase modification on the elevated temperature mechanical properties of Al–Si hypereutectic alloys. Mater Sci Eng A. 2019; 748:367–370. doi: 10.1016/j.msea.2019.01.119
13.
ChokemorhPPandeePLimmaneevichitrC.Role of scandium additions in primary silicon refinement of hypereutectic Al–20Si alloys. Int J Cast Met Res. 2018; 0461:1–10. doi: 10.1080/13640461.2018.1436214
14.
Zhong-WeiCWan-QiJRui-JieZ.Superheat treatment of Al–7Si–0.55Mg alloy melt. Mater Lett. 2005; 59:2183–2185. doi: 10.1016/j.matlet.2004.08.047
15.
WardPJAtkinsonHVAndersonPRGSemi-solid processing of novel MMCs based on hypereutectic aluminium-silicon alloys. Acta Mater. 1996; 44:1717–1727. doi: 10.1016/1359-6454(95)00356-8
16.
JungHKSeoPKKangCG.Microstructural characteristics and mechanical properties of hypo-eutectic and hyper-eutectic Al–Si alloys in the semi-solid forming process. J Mater Process Technol. 2001; 113:568–573. doi: 10.1016/S0924-0136(01)00708-7
17.
LuDJiangYGuanGRefinement of primary Si in hypereutectic Al–Si alloy by electromagnetic stirring. J Mater Process Technol. 2007; 189:13–18. doi: 10.1016/j.jmatprotec.2006.12.008
18.
GeLLLiuRPLiGSolidification of Al–50 at.%Si alloy in a drop tube. Mater Sci Eng A. 2004; 385:128–132. doi: 10.1016/S0921-5093(04)00865-2
19.
PierantoniMGremaudMMagninPThe coupled zone of rapidly solidified AlSi alloys in laser treatment. Acta Metall Mater. 1992; 40:1637–1644. doi: 10.1016/0956-7151(92)90106-O
20.
UzunOKaraaslanTGogebakanMHardness and microstructural characteristics of rapidly solidified Al–8–16 wt.%Si alloys. J Alloys Compd. 2004; 376:149–157. doi: 10.1016/j.jallcom.2004.01.017
21.
CaiZWangRZhangCCharacterization of rapidly solidified Al–27 Si hypereutectic alloy: effect of solidification condition. J Mater Eng Perform. 2015; 24:1226–1236. doi: 10.1007/s11665-015-1386-4
22.
LiaoHSunYSunG.Correlation between mechanical properties and amount of dendritic α-Al phase in as-cast near-eutectic Al–11.6% Si alloys modified with strontium. Mater Sci Eng A. 2002; 335:62–66. doi: 10.1016/S0921-5093(01)01949-9
23.
DahleAKNogitaKMcDonaldSDEutectic modification and microstructure development in Al–Si alloys. Mater Sci Eng A. 2005; 413–414:243–248. doi: 10.1016/j.msea.2005.09.055
24.
LuSZHellawellA.The mechanism of silicon modification in aluminum-silicon alloys: impurity induced twinning. Metall Trans A. 1987; 18:1721–1733. doi: 10.1007/BF02646204
25.
JenkinsonDCHoganLM.The modification of aluminium-silicon alloys with strontium. J Cryst Growth. 1975; 28:171–187. doi: 10.1016/0022-0248(75)90233-X
26.
HenghuaZHailiDGuangjieSMicrostructure and mechanical properties of hypereutectic A1–Si alloy modified with Cu–P. Rare Met. 2008; 27:59–63. doi: 10.1016/S1001-0521(08)60031-5
27.
JungJGAhnTYChoYHSynergistic effect of ultrasonic melt treatment and fast cooling on the refinement of primary Si in a hypereutectic Al–Si alloy. Acta Mater. 2018; 144:31–40. doi: 10.1016/j.actamat.2017.10.039
28.
DaiHLiuX.Effects of individual and combined additions of phosphorus, boron and cerium on primary and eutectic silicon in an Al–30Si alloy. Rare Met. 2009; 28:651–655. doi: 10.1007/s12598-009-0124-1
29.
KyffinWJRainforthWMJonesH.Effect of treatment variables on size refinement by phosphide inoculants of primary silicon in hypereutectic Al–Si alloys. Mater Sci Technol. 2001; 17:901–905. doi: 10.1179/026708301101510870
30.
FarajiMKhalilpourHFarajiMEffect of phosphorous inoculation on creep behavior of a hypereutectic Al–Si alloy. J Mater Eng Perform. 2014; 23:3467–3473. doi: 10.1007/s11665-014-1152-z
31.
RaghukiranNKumarR.A effect of scandium addition on the microstructure, mechanical and wear properties of the spray formed hypereutectic aluminum–silicon alloys. Mater Sci Eng A. 2015; 641:138–147. doi: 10.1016/j.msea.2015.06.027
32.
ShiWGaoBTuGEffect of neodymium on primary silicon and mechanical properties of hypereutectic Al–15Si alloy. J Rare Earths. 2010; 28:367–370. doi: 10.1016/S1002-0721(10)60363-8
33.
LiQLiBLiJEffect of yttrium addition on the microstructures and mechanical properties of hypereutectic Al–20Si alloy. Mater Sci Eng A. 2018; 722:47–57. doi: 10.1016/j.msea.2018.03.015
34.
LiQLiJLiBEffect of samarium (Sm) addition on the microstructure and tensile properties of Al–20%Si casting alloy. Int J Met. 2018; 12:554–564.
35.
ChoiHKonishiHLiX.Al2O3 nanoparticles induced simultaneous refinement and modification of primary and eutectic Si particles in hypereutectic Al–20Si alloy. Mater Sci Eng A. 2012; 541:159–165. doi: 10.1016/j.msea.2012.01.131
36.
AcharyaMMandalA.An investigation on individual and synergistic effect of gamma alumina (γ-Al2O3) and strontium on microstructure and mechanical properties of Al–20Si alloy. Trans Nonferrous Met Soc China. 2019; 29:1353–1364. doi: 10.1016/S1003-6326(19)65042-9
37.
KirkwoodDH.A simple model for dendrite arm coarsening during solidification. Mater Sci Eng. 1985; 73:7–10. doi: 10.1016/0025-5416(85)90319-2
38.
KurzWFisherDJ.Fundamentals of solidification. 3rd ed. Aedermannsdorf, Switzerland: Trans Tech Publications Ltd.; 1989. p. 85–86.
39.
EastonMDavidsonCJohnDST.Effect of alloy composition on the dendrite arm spacing of multicomponent aluminum alloys. Metall Mater Trans A. 2010; 41:1528–1538. doi: 10.1007/s11661-010-0183-9
40.
RajabiMVahidiMSimchiAMicrostructural evolution of Al–20Si–5Fe alloy during rapid solidification and hot consolidation. Rare Met. 2009; 28:639–645. doi: 10.1007/s12598-009-0122-3
41.
PawlikPPawlikKPrzybłA.Investigation of the cooling rate in the suction casting process. Rev Adv Mater Sci. 2008; 18:81–84.
42.
HongSJSuryanarayanaC.Mechanical properties and fracture behavior of an ultrafine-grained Al–20 wt pct Si alloy. Metall Mater Trans A. 2005; 36:715–723. doi: 10.1007/s11661-005-1003-5
43.
JiangQCXuCLLuMEffect of new Al–P–Ti–TiC–Y modifier on primary silicon in hypereutectic Al–Si alloys. Mater Lett. 2005; 59:624–628. doi: 10.1016/j.matlet.2004.10.042
44.
KayaHGündüzMÇadirliEDependency of microindentation hardness on solidification processing parameters and cellular spacing in the directionally solidified Al based alloys. J Alloys Compd. 2009; 478:281–286. doi: 10.1016/j.jallcom.2008.11.164
45.
JiangWXuXZhaoYEffect of the addition of Sr modifier in different conditions on microstructure and mechanical properties of T6 treated Al–Mg2Si in-situ composite. Mater Sci Eng A. 2018; 721:263–273. doi: 10.1016/j.msea.2018.02.100