The effect of Ti content on the microstructure and mechanical properties of heat-treated Al–Si–Cu–Mn–Fe alloys was investigated. It was found that the mechanical properties increased with the increase of Ti content. This was attributed to the refinement of grain size, the increased amount of T (Al20Cu2Mn3), the α-Fe (Al15(FeMn)3(CuSi)2) precipitated particles, and the decrease in Al2Cu. At an elevated temperature of 300°C, the heat-treated Al–Si–Cu–Mn–Fe alloy with 0.5% Ti demonstrated the best mechanical properties, which are superior to those of commercial aluminium alloys. The yield strength contribution at 300°C was quantitatively evaluated based on the dispersoid, solid solution, and matrix contributions. It was confirmed that the main strengthening mechanism in the experimental alloys was the dispersoid strengthening.
ShahaSKCzerwinskiFKasprzakWAgeing characteristics and high-temperature tensile properties of Al-Si-Cu-Mg alloys with micro-additions of Cr, Ti, V and Zr. Mater Sci Eng A. 2016; 652:353–364. doi: 10.1016/j.msea.2015.11.049
2.
FarkooshARJavidaniMHoseiniMPhase formation in as-solidified and heat-treated Al-Si-Cu-Mg-Ni alloys: thermodynamic assessment and experimental investigation for alloy design. J Alloys Compd. 2013; 551:596–606. doi: 10.1016/j.jallcom.2012.10.182
3.
RahimianMAmirkhanlouSBlakePNanoscale Zr-containing precipitates; a solution for significant improvement of high-temperature strength in Al-Si-Cu-Mg alloys. Mater Sci Eng A. 2018; 721:328–338. doi: 10.1016/j.msea.2018.02.060
4.
WangERHuiXDChenGL.Eutectic Al-Si-Cu-Fe-Mn alloys with enhanced mechanical properties at room and elevated temperature. Mater Des. 2011; 32(8):4333–4340. doi: 10.1016/j.matdes.2011.04.005
5.
WangERHuiXDWangSSImproved mechanical properties in cast Al–Si alloys by combined alloying of Fe and Cu. Mater Sci Eng A. 2010; 527(29):7878–7884. doi: 10.1016/j.msea.2010.08.058
6.
ZuoLJYeBFengJEffect of Q-Al5Cu2Mg8Si6, phase on mechanical properties of Al-Si-Cu-Mg alloy at elevated temperature. Mater Sci Eng A. 2017; 693:26–32. doi: 10.1016/j.msea.2017.03.087
7.
GholizadehRShabestariSG.Investigation of the effects of Ni, Fe, and Mn on the formation of complex intermetallic compounds in Al-Si-Cu-Mg-Ni alloys. Metall Mater Trans A. 2011; 42(11):3447–3458. doi: 10.1007/s11661-011-0764-2
8.
LiYGYangYWuYYSupportive strengthening role of Cr-rich phase on Al-Si multicomponent piston alloy at elevated temperature. Mater Sci Eng A. 2011; 528(13–14):4427–4430. doi: 10.1016/j.msea.2011.02.047
9.
LiuKChenXG.Evolution of intermetallics, dispersoids, and elevated temperature properties at various Fe contents in Al-Mn-Mg 3004 alloys. Metall Mater Trans B. 2016; 47(6):3291–3300. doi: 10.1007/s11663-015-0564-y
10.
LiuKChenXG.Improvement in elevated-temperature properties of Al-13% Si piston alloys by dispersoid strengthening via Mn addition. J Mater Res. 2018; 33(20):3430–3438. doi: 10.1557/jmr.2018.117
11.
FarkooshARPekguleryuzM.The effects of manganese on the Τ-phase and creep resistance in Al-Si-Cu-Mg-Ni alloys. Mater Sci Eng A. 2013; 582:248–256. doi: 10.1016/j.msea.2013.06.030
12.
ShahaSKCzerwinskiFKasprzakWAgeing characteristics and high-temperature tensile properties of Al-Si-Cu-Mg alloys with micro-additions of Mo and Mn. Mater Sci Eng A. 2017; 684:726–736. doi: 10.1016/j.msea.2016.12.044
13.
SadeghiIWellsMAEsmaeiliS.Effect of particle shape and size distribution on the dissolution behavior of Al2Cu particles during homogenization in aluminum casting alloy Al-Si-Cu-Mg. J Mater Process Technol. 2018; 251:232–240. doi: 10.1016/j.jmatprotec.2017.08.042
14.
ZerenM.Effect of copper and silicon content on mechanical properties in Al-Cu-Si-Mg alloys. J Mater Process Technol. 2005; 169:292–298. doi: 10.1016/j.jmatprotec.2005.03.009
15.
BjurenstedtAGhassemaliESeifeddineSThe effect of Fe-rich intermetallics on crack initiation in cast aluminium: an in-situ tensile study. Mater Sci Eng A. 2019; 756:502–507. doi: 10.1016/j.msea.2018.07.044
16.
TangQZhaoJWangTThe effects of neodymium addition on the intermetallic microstructure and mechanical properties of Al-7Si-0.3 Mg-0.3 Fe alloys. J Alloys Compd. 2018; 741:161–173. doi: 10.1016/j.jallcom.2018.01.138
17.
TashMSamuelFHMucciardiFEffect of metallurgical parameters on the hardness and microstructural characterization of as-cast and heat-treated 356 and 319 aluminum alloys. Mater Sci Eng A. 2007; 443:185–201. doi: 10.1016/j.msea.2006.08.054
18.
YuKLiWXLiSRMechanical properties and microstructure of aluminum alloy 2618 with Al3(Sc,Zr) phases. Mater Sci Eng A. 2004; 368(1–2):88–93. doi: 10.1016/j.msea.2003.09.092
19.
RaoKSRajuPNReddyGMMicrostructure and high temperature strength of age hardenable AA2219 aluminium alloy modified by Sc, Mg and Zr additions. Mater Sci Technol. 2009; 25(1):92–101. doi: 10.1179/174328408X259052
20.
LinBXuRLiHYFormation of Fe-rich intermetallics in Al-5.0Cu-0.5 Fe alloys with different Mn additions. Mater Sci Technol. 2018; 34(12):1447–1459. doi: 10.1080/02670836.2018.1460040
21.
LiGLiaoHSuoXCr-induced morphology change of primary Mn-rich phase in Al-Si-Cu-Mn heat resistant aluminum alloys and its contribution to high temperature strength. Mater Sci Eng A. 2018; 709:90–96. doi: 10.1016/j.msea.2017.10.049
22.
LiuKChenXG.Evolution of microstructure and elevated-temperature properties with Mn addition in Al-Mn-Mg alloys. J Mater Res. 2017; 32(13):2585–2593. doi: 10.1557/jmr.2017.239
23.
HwangJYDotyHWKaufmanMJ.The effects of Mn additions on the microstructure and mechanical properties of Al-Si-Cu casting alloys. Mater Sci Eng A. 2008; 488(1):496–504. doi: 10.1016/j.msea.2007.12.026
24.
LiZLimodinNTandjaouiAInfluence of Sr, Fe and Mn content and casting process on the microstructures and mechanical properties of AlSi7Cu3 alloy. Mater Sci Eng A. 2017; 689:286–297. doi: 10.1016/j.msea.2017.02.041
25.
SeifeddineSJohanssonSSvenssonIL.The influence of cooling rate and manganese content on the β-Al5FeSi phase formation and mechanical properties of Al-Si-based alloys. Mater Sci Eng A. 2008; 490(1):385–390. doi: 10.1016/j.msea.2008.01.056
26.
QianZLiuXZhaoDEffects of trace Mn addition on the elevated temperature tensile strength and microstructure of a low-iron Al-Si piston alloy. Mater Lett. 2008; 62:2146–2149. doi: 10.1016/j.matlet.2007.11.035
27.
LiaoHCTangYYSuoXJDispersoid particles precipitated during the solutionizing course of Al-12wt%Si-4wt%Cu-1.2wt%Mn alloy and their influence on high temperature strength. Mater Sci Eng A. 2017; 699:201–209. doi: 10.1016/j.msea.2017.04.091
28.
SuoXJLiaoHCHuYY.Formation of Al15Mn3Si2 phase during solidification of a novel Al-12% Si-4% Cu-1.2% Mn heat-resistant alloy and its thermal stability. J Mater Eng Perform. 2018; 27(6):2910–2920. doi: 10.1007/s11665-018-3133-0
29.
MondolfoLF.Aluminum alloys: structure and properties. London: Butterworths; 1976.
30.
LiYG.The study of elevated-temperature strengthening phase of Al-Si-Cu-Ni-Mg piston Alloys. Jinan: Shan Dong University; 2011.
31.
QianZ.Study on high strength heat-resistant Al-Si piston alloys. Jinan: Shan Dong University; 2009.
32.
BaiZQiuFLiuYSuperior strength and ductility of the Al–Cu alloys inoculated by Zr-based metallic glass at elevated temperatures. Mater Sci Eng A. 2015; 645:357–360. doi: 10.1016/j.msea.2015.08.013
33.
LinBXuRLiHYDevelopment of high Fe content squeeze cast 2A16 wrought Al alloys with enhanced mechanical properties at room and elevated temperatures. Mater Charact. 2018; 142:389–397. doi: 10.1016/j.matchar.2018.06.009
34.
LinBLiHYXuRPrecipitation of iron-rich intermetallics and mechanical properties of Al-Si-Mg-Fe alloys with Al-5Ti-B. Mater Sci Technol. 2018; 34(17):2145–2152. doi: 10.1080/02670836.2018.1519945
35.
GaoTLiPLiYInfluence of Si and Ti contents on the microstructure, microhardness and performance of TiAlSi intermetallics in Al-Si-Ti alloys. J Alloys Compd. 2011; 509(31):8013–8017. doi: 10.1016/j.jallcom.2011.05.032
36.
LiYJArnbergL.Quantitative study on the precipitation behavior of dispersoids in DC-cast AA3003 alloy during heating and homogenization. Acta Mater. 2003; 51:3415–3428. doi: 10.1016/S1359-6454(03)00160-5
37.
LiuKChenXG.Development of Al-Mn-Mg 3004 alloy for applications at elevated temperature via dispersoid strengthening. Mater Des. 2015; 84:340–350. doi: 10.1016/j.matdes.2015.06.140
38.
HanLSuiYWangQEffects of Nd on microstructure and mechanical properties of cast Al-Si-Cu-Ni-Mg piston alloys. J Alloys Compd. 2017; 695:1566–1572. doi: 10.1016/j.jallcom.2016.10.300
39.
SuiYJiDHanLCharacterization of the aging precipitates of Al-12Si-4Cu-2Ni-0.8 Mg-0.2 Gd piston alloy. JOM. 2019; 71(1):366–372. doi: 10.1007/s11837-018-3080-0
40.
OkazakiTAKariyaAI.Aluminum alloy for internal-combustion piston, and aluminum alloy piston. US Patent. 1999; 5996:471.
41.
DavisJR.ASM specialty handbook: aluminum and aluminum alloys. Materials Park ( OH): ASM International; 1993.
42.
TakasakiNYoshimuraY.Heat resistant Al die cast material. US Patent. 2003; 6706:242.
43.
BelovNAAksenovAAEskinDG.Iron in aluminium alloys: impurity and alloying element. London: CRC Press; 2002.
SamuelAMDotyHWValtierraSEffect of Fe, Sr, P, Ti and undercooling on the precipitation of β-Al5FeSi in A319.2 type alloys. Int J Metalcast. 2017; 11(4):675–687. doi: 10.1007/s40962-016-0116-5
46.
NarayananLASamuelFHGruzleskiJE.Dissolution of iron intermetallics in Al-Si alloys through nonequilibrium heat treatment. Metall Mater Trans A. 1995; 26(8):2161–2174. doi: 10.1007/BF02670687
47.
BacaicoaIDwivediPKLuetjeMEffect of non-equilibrium heat treatments on microstructure and tensile properties of an Al-Si-Cu alloy. Mater Sci Eng A. 2016; 673:562–571. doi: 10.1016/j.msea.2016.07.080
48.
SjölanderESeifeddineS.Optimisation of solution treatment of cast Al-Si-Cu alloys. Mater Des. 2010; 31:44–49. doi: 10.1016/j.matdes.2009.10.035
49.
CerriEEvangelistaESpigarelliSEffects of thermal treatments on microstructure and mechanical properties in a thixocast 319 aluminum alloy. Mater Sci Eng A. 2000; 284(1–2):254–260. doi: 10.1016/S0921-5093(00)00748-6
50.
BasakCBBabuNH.Influence of Cu on modifying the beta phase and enhancing the mechanical properties of recycled Al-Si-Fe cast alloys. Sci Rep. 2017; 7(1):5779–5789. doi: 10.1038/s41598-017-05937-2
51.
ZerenMKarakulakE.Microstructural chracterisation of Al-Si-xTi cast alloys. Mater Sci Technol. 2009; 25(10):1211–1214. doi: 10.1179/174328408X382190
52.
ChenXGFortierM.TiAlSi intermetallic formation and its impact on the casting processing in Al-Si alloys. J Mater Process Technol. 2010; 210(13):1780–1786. doi: 10.1016/j.jmatprotec.2010.06.009
53.
ZhangZHosodaSKimISGrain refining performance for Al and Al-Si alloy casts by addition of equal-channel angular pressed Al-5 mass% Ti alloy. Mater Sci Eng A. 2006; 425(1–2):55–63. doi: 10.1016/j.msea.2006.03.018
54.
PandeCSCooperKP.Nanomechanics of Hall-Petch relationship in nanocrystalline materials. Prog Mater Sci. 2009; 54:689–706. doi: 10.1016/j.pmatsci.2009.03.008
55.
YangY.Study on the evolution and collaborative strengthing mechanism of heat-resistant phases in multicomponent Al-Si alloy. Jinan: Shandong University; 2013.
56.
LinBZhangWW.Evolution of iron-rich intermetallics and elevated temperature mechanical properties in gravity die cast 2A16 Al alloy. Int J Cast Met Res. 2018; 31(4):222–229.
57.
TsengCJLeeSLWuTFEffects of manganese on microstructure and mechanical properties of A206 alloys containing iron. J Mater Res. 2002; 17:2243–2250. doi: 10.1557/JMR.2002.0330
58.
ChanyathunyarojKPatakhamUKouSMicrostructural evolution of iron-rich intermetallic compounds in scandium modified Al-7Si-0.3 Mg alloys. J Alloys Compd. 2017; 692:865–875. doi: 10.1016/j.jallcom.2016.09.132
59.
BaiZHQiuFXueJXSimultaneously increasing strength and ductility of the Al–Cu alloys inoculated by Zr-based metallic glass. Mater Charact. 2015; 100:36–40. doi: 10.1016/j.matchar.2014.12.016
60.
ZhouDSQiuFJiangQC.Simultaneously increasing the strength and ductility of nano-sized TiN particle reinforced Al-Cu matrix composites. Mater Sci Eng A. 2014; 596:98–102. doi: 10.1016/j.msea.2013.12.049
61.
MuggerudAMFMørtsellEALiYDispersoid strengthening in AA3xxx alloys with varying Mn and Si content during annealing at low temperatures. Mater Sci Eng A. 2013; 567:21–28. doi: 10.1016/j.msea.2013.01.004
62.
HuskinsELCaoBRameshKT.Strengthening mechanisms in an Al-Mg alloy. Mater Sci Eng A. 2010; 527:1292–1298. doi: 10.1016/j.msea.2009.11.056
63.
RyenØHolmedalBNijsOStrengthening mechanisms in solid solution aluminum alloys. Metall Mater Trans A. 2006; 37:1999–2006. doi: 10.1007/s11661-006-0142-7
64.
KaufmanJG.Properties of aluminum alloys: tensile, creep, and fatigue data at high and Low temperatures. Materials Park ( OH): ASM International; 1999.
65.
QinJZhangZChenXG.Mechanical properties and strengthening mechanisms of Al-15 Pct B4C composites with Sc and Zr at elevated temperatures. Metall Mater Trans A. 2016; 47:4694–4708. doi: 10.1007/s11661-016-3606-4
66.
FullerCBSeidmanDNDunandDC.Mechanical properties of Al (Sc, Zr) alloys at ambient and elevated temperatures. Acta Mater. 2003; 51:4803–4814. doi: 10.1016/S1359-6454(03)00320-3
67.
LiYJMuggerudAMFOlsenAPrecipitation of partially coherentα-Al (Mn, Fe) Si dispersoids and their strengthening effect in AA 3003 alloy. Acta Mater. 2012; 60:1004–1014. doi: 10.1016/j.actamat.2011.11.003