Feeding distances have been calculated for an Al–7%Si alloy by using first principles, i.e. Darcy's law for flow through porous a medium. Pressure drop needed for liquid metal flow through the interdendritic network has been varied between approximately 1 atm and the intrinsic fracture pressure of liquid aluminium. Results have shown that aluminium alloys are capable of feeding themselves via either interdendritic or solid feeding when liquid metal is not weakened extrinsically.
BishopHF, PelliniWS.The contribution of risers and chill-edge effects to soundness of cast steel plates. AFS Trans. 1950;58:185–197.
2.
MyskowskiET, BishopHF, PelliniWS.Feeding range of joined sections. AFS Trans. 1953;61:302–308.
3.
PelliniWS.Factors which determine riser adequacy and feeding range. AFS Trans. 1953;61:61–80.
4.
JacobS, DrouzyM. (1974). 41st International Foundry Congress, Paper no. 6, Liege, Belgium, June 1974.
5.
CampbellJ.Complete casting handbook: metal casting processes, metallurgy, techniques and design. Oxford: Butterworth-Heinemann; 2015.
6.
YousefianP, TiryakioğluM.Pore formation during solidification of aluminum: reconciliation of experimental observations, modeling assumptions, and classical nucleation theory. Metall Mater Trans A. 2018;49:563–575. doi: 10.1007/s11661-017-4438-6
7.
TiryakioğluM.On the intrinsic fracture pressure of liquid and solid aluminum around its melting temperature. Metall Mater Trans A. 2018;49:5953–5955. doi: 10.1007/s11661-018-4969-5
8.
CampbellJ.Entrainment defects. Mater Sci Technol. 2006;22:127–145. doi: 10.1179/174328406X74248
9.
TiryakioğluM, YousefianP, EasonPD.Quantification of entrainment damage in A356 aluminum alloy castings. Metall Mater Trans A. 2018;49:5815–5822. doi: 10.1007/s11661-018-4865-z
10.
MartienssenW, WarlimontH.Springer handbook of condensed matter and materials data. Berlin: Springer Science & Business Media; 2006.
11.
MagnussonT, ArnbergL.Density and solidification shrinkage of hypoeutectic aluminum–silicon alloys. Metall Mater Trans A. 2001;32:2605–2613. doi: 10.1007/s11661-001-0050-9
12.
DarcyH.Les fontaines publiques de la ville de Dijon: exposition et application. Paris: Victor Dalmont; 1856.
13.
CarmanPC.Fluid flow through granular beds. Trans Inst Chem Eng.1937;15:150–166.
14.
PlevachukY, SklyarchukV, YakymovychA, Density, viscosity, and electrical conductivity of hypoeutectic Al–Cu liquid alloys. Metall Mater Trans A. 2008;39:3040–3045. doi: 10.1007/s11661-008-9659-2
15.
SklyarchukV, PlevachukY, YakymovychA, Structure sensitive properties of liquid Al–Si alloys. Int J Thermophys. 2009;30:1400–1410. doi: 10.1007/s10765-009-0585-3
16.
BardesBP, FlemingsMC.AFS Trans. 1966;74:406–412.
17.
KirkwoodDH.A simple model for dendrite arm coarsening during solidification. Mater Sci Eng. 1985;73:L1–L4. doi: 10.1016/0025-5416(85)90319-2
18.
LiebKC, HorstmanRT, PowerB, Tensile properties of A357-T6 aluminum castings. J Test Eval. 1980;8:170–176. doi: 10.1520/JTE11609J
19.
AgarwalG, AmirthalingamM, MoonSC, Experimental evidence of liquid feeding during solidification of a steel. Scr Mater. 2018;146:105–109. doi: 10.1016/j.scriptamat.2017.11.003
20.
CampanellaT, CharbonC, RappazM.Grain refinement induced by electromagnetic stirring: a dendrite fragmentation criterion. Metall Mater Trans A. 2004;35:3201–3210. doi: 10.1007/s11661-004-0064-1
21.
GeHH, LiJ, HanXJ, Dendritic model for macrosegregation prediction of large scale castings. J Mater Process Technol. 2016;227:308–317. doi: 10.1016/j.jmatprotec.2015.08.020
22.
BridgeMR, RogersGD.Structural effects and band segregate formation during the electromagnetic stirring of strand-cast steel. Metall Trans B. 1984;15:581–589. doi: 10.1007/BF02657390