Fe–35Ni–25Cr–0.4C alloys with different compositions are aged between 750 and 1150°C up to ∼10,000 h. As-cast microstructure contains interdendritic carbides of type M7C3 (‘Cr7C3’) and MC (‘NbC’). At service temperatures, M7C3 transform into M23C6 (‘Cr23C6’) within hours. Then, a hardening precipitation of secondary intragranular M23C6 occurs over hundreds of hours, the nose of the ‘temperature-time-hardening’ curve being around 1000°C. G phase forms after long aging; its solvus temperature and formation kinetics depend on silicon content. Z phase is observed after long aging at 950°C or above. G and Z phases form at the expense of MC. Very long aging causes nitridation under air, with first a transformation of M23C6 into chromium-rich M2X carbonitrides (X = C,N), then of MC into chromium-rich MX carbonitrides.
SullivanCP, DonachieMJ.Some effects of microstructure on the mechanical properties of nickel-base superalloys. Met Eng Q. 1967;7:36–45.
2.
Wen-TaiH, HoneycombeRWK.Structure of centrifugally of cast austenitic stainless steels: part 1 HK40 as cast and after creep between 750 and 1000°C. Mater Sci Technol. 1985;1:385–397. doi: 10.1179/mst.1985.1.5.385
3.
ZhuSJ, WangY.Influence on creep crack growth of a cast HP alloy. Mater Sci Eng A. 1990;127:L7–L10. doi: 10.1016/0921-5093(90)90320-3
4.
Soares GDDA, Almeida LHD, Silveira TLD, Niobium additions in HP heat-resistant cast stainless steels, materials characterization. Mater Charact. 1992;29:387–396. doi: 10.1016/1044-5803(92)90045-J
5.
WangF, NorthwoodDO.The effect of carbon content on the microstructure of an experimental heat-resistant steel. Mater Charact. 1993;31:3–10. doi: 10.1016/1044-5803(93)90039-X
6.
Almeida LHD, RibeiroAF.Microstructural characterization of modified 25Cr-35Ni centrifugally cast steel furnace tubes. Mater Charact. 2002;49:219–229. doi: 10.1016/S1044-5803(03)00013-5
7.
MuralidharanG, EvansND, LiuKC, Effect of precipitation on creep properties of certain cast H-series austenitic stainless steels. Proc MS&T’04 Conf. 2004;1:651–661.
8.
VoicuR, LacazeJ, AndrieuE, Creep and tensile behaviour of austenitic Fe–Cr–Ni stainless steels. Mater Sci Eng A. 2009;510–511:185–189. doi: 10.1016/j.msea.2008.04.098
9.
LiuCJ, ChenY.Variations of the microstructure and mechanical properties of HP40Nb hydrogen reformer tube with time at elevated temperature. Mater Des. 2011;32:2507–2512. doi: 10.1016/j.matdes.2010.08.031
10.
AndradeAR, BolfariniC, FerreiraLAM, Influence of niobium addition on the high temperature mechanical properties of a centrifugally cast HP alloy. Mater Sci Eng A. 2015;628:176–180. doi: 10.1016/j.msea.2015.01.049
11.
LaigoJ, TancretF, Le GallR, ChristienF, FurtadoJ.The influence of phase transformations on creep resistance in Fe-Ni-Cr alloys for reformer tube applications. In: 2007 Proceedings of the ASME Pressure Vessel & Piping Conference/CREEP8 Conference, ISBN 0791838048, paper number CREEP2007-26720.
12.
RoachDB, Van EchoJA.Comparison of the properties of the HK-40 and HP-45 cast heat resistant alloys. Stainless Steel Castings, ASTM STP. 1982;756:275–312. doi: 10.1520/STP28447S
13.
IbanezRAP, De Almeida SoaresGD.Effect of Si content on the microstructure of modified HP austenitic steels. Mater Charact. 1993;30:243–249. doi: 10.1016/1044-5803(93)90071-3
14.
ChenQZ, ThomasCW.Characterization of20Cr32Ni1Nb alloys in as-cast and ex-service conditions by SEM, TEM, EDX. Mater Sci Eng A. 2004;374:398–408. doi: 10.1016/j.msea.2004.03.038
15.
LaigoJ, ChristienF, Le GallR, SEM, EDS, EPMA-WDS and EBSD characterization of carbides in HP type heat resistant alloys. Mater Charact. 2008;59:1580–1586. doi: 10.1016/j.matchar.2008.02.001
16.
BuchananKG, KralMV.Crystallography and morphology of niobium carbide in as-cast HP-niobium reformer tubes. Metall Mater Trans A. 2012;43:1760–1769. doi: 10.1007/s11661-011-1025-0
17.
BuchananKG, KralMV, BishopCM.Crystallography and morphology of MC carbides in niobium-titanium modified as-cast HP alloys. Metall Mater Trans A. 2014;45:3373–3385. doi: 10.1007/s11661-014-2285-2
18.
SwaminathanJ, PrasadP, GunjanMK, Mechanical strength and microstructural observations for remaining life assessment of service exposed 24Ni-24Cr-1.5Nb cast austenitic steel reformer tubes. Eng Failure Anal. 2008;15:723–735. doi: 10.1016/j.engfailanal.2007.06.009
19.
GhatakA, RobiPS.Effect of temperature on the microstructure and hardness of service exposed25Cr35NiNb reformer tubes. Trans Indian Inst Met. 2016;69:823–827. doi: 10.1007/s12666-015-0552-6
20.
GugulothK, SwaminathanJ, BaguiS, Remnant life assessment and microstructural studies on service exposed primary reformer tubes of a catalytic converter of an ammonia plant. High Temp Mater Proc. 2012;31:759–767. doi: 10.1515/htmp-2012-0016
21.
Kondrat'evSY, SviatyshevaEV, AnastasiadiGP, Fragmented structure of niobium carbide particles in as-cast modified HP alloys. Acta Mater. 2017;127:267–276. doi: 10.1016/j.actamat.2017.01.043
22.
AlvinoA, AntoniniA, LegaD, MennutiC, TontiA.Damage characterization of heat resistant steels after long service in reforming plants. In: ASME 2016 Pressure Vessels and Piping Conference – Volume 6B: Materials and Fabrication, ISBN 978-0-7918-5043-5, paper number PVP2016-63555, pp. V06BT06A032.
23.
VoicuR, AndrieuE, PoquillonD, Microstructure evolution of HP40-Nb alloys during aging under air at 1000 °C. Mater Charact. 2009;60:1020–1027. doi: 10.1016/j.matchar.2009.04.007
24.
MostafaeiM, ShamanianM, PurmohamadH, Microstructural degradation of two cast heat resistant reformer tubes after long term service exposure. Eng Failure Anal. 2011;18:164–171. doi: 10.1016/j.engfailanal.2010.08.017
25.
McLeodAC, BishopCM, StevensKJ, Microstructural characterization and image analysis in ex-service HP alloy stainless steel tubes for ethylene pyrolysis. Metallogr Microstruct Anal. 2016;5:178–187. doi: 10.1007/s13632-016-0274-0
26.
XieJY, ChenNX, TengLD, Atomistic study on the site preference and thermodynamic properties for Cr23-xFexC6. Acta Mater. 2005;53:5305–5312. doi: 10.1016/j.actamat.2005.07.039
27.
ErnemanJ, SchwindM, LiuP, Precipitation reactions caused by nitrogen uptake during service at high temperatures of a niobium stabilised austenitic stainless steel. Acta Mater. 2004;52:4337–4350. doi: 10.1016/j.actamat.2004.06.001
28.
BeckittFR, ClarkBR.The shape and mechanism of formation of M23C6 carbide in austenite. Acta Metall. 1967;15:113–129. doi: 10.1016/0001-6160(67)90159-9
29.
RodriguezJ, HaroS.A metallographic study of aging in a cast heat-resisting alloy. Mater Charact. 2000;45:25–32. doi: 10.1016/S1044-5803(00)00047-4
30.
BarbabelaGD, De AlmeidaLH.Role of niobium in modifying the microstructure of heat-resistant cast HP steel. Mater Charact. 1991;26:193–197. doi: 10.1016/1044-5803(91)90053-7
31.
SpiegelFX, BardosD.Ternary G and E silicides and germanides of transition elements. Trans Metall Soc AIME. 1963;227:575–579.
32.
GoldschmidtHJ.Interstitial alloys, Butterwoths, London, England, 1967, p. 330.
33.
EcobRC, LobbRC.The formation of G-phase in 20/25Nb stainless steelAGR fuel cladding alloy and its effect on creep properties. J Mater Sci. 1987;22:2867–2880. doi: 10.1007/BF01086484
34.
PowellDJ, PilkingtonR.The precipitation characteristics of 20Cr25NiNb stabilised stainless steel. Acta Metall. 1988;36:713–724. doi: 10.1016/0001-6160(88)90105-8
35.
PiekarskiB.Effect of Nb and Ti additions on microstructure, and identification of precipitates in stabilized Ni-Cr cast austenitic steels. Mater Charact. 2001;47:181–186. doi: 10.1016/S1044-5803(01)00166-8
36.
KenikEA, MaziaszPJ.Structure and phase stability in a cast modified HP austenite after long-term ageing. Scr Mater. 2003;49:117–122. doi: 10.1016/S1359-6462(03)00238-0
WilliamsTM.A nickel and silicon rich phase in irradiated FV548 steel. J Nucl Mater. 1979;82:199–201. doi: 10.1016/0022-3115(79)90055-2
39.
BinderWO.Some notes on the structure and impact resistance of columbium-bearing 18-8 steels after exposure to elevated temperatures. Symposium on the nature, occurrence and effects of sigma-phase, ASTM STP110, 1950, p. 146–164.
40.
StrangA, VodarekV.The effect of nickel on M23C6 coarsening rates in 12CrMoVNb steels. Mater Sci Technol. 1996;12:552–556. doi: 10.1179/mst.1996.12.7.552
41.
RaghavanA, KleinCF, MarzinskiCN.Instabilities in stabilized austenitic stainless steels. Metall Trans A. 1992;23:2455–2467. doi: 10.1007/BF02658049
42.
RobinsonPW, JackDH.New developments in stainless steel technology. In: LulaR, editor. American Society for Metals. Metals Park ( Ohio): ASM; 1985. p. 71–76.
AndrénHO, HenjeredA, KarlsonL.MX precipitation in stabilised austenitic stainless steels. Proc Int Conf Stainless Steels. 1984;84:91–96.
45.
LaigoJ.Microstructure, transformations de phases et durabilité à haute température des alliages de la série HP [Microstructure, high temperature phase transformations and durability of HP series alloys], PhD thesis, Université de Nantes, France, 2007.
46.
KayaAA, KrauklisP, YoungDJ.Microstructure of HK40 alloy after high temperature service in oxidizing/carburizing environment: I. Oxidation phenomena and propagation of a crack. Mater Charact. 2002;49:11–21. doi: 10.1016/S1044-5803(02)00249-8