Effect of precipitates on properties of cold-rolled Al–Mg–Si–Sc–Zr alloy with higher temperature aging

Abstract

The aging hardening behaviours of the cold-rolled Al–Mg–Si–Sc–Zr alloy were investigated. The microstructure, hardness and electrical conductivity (EC) of the Al–Mg–Si–Sc–Zr alloy were measured. The relationship between the microstructure and the properties of the Al–Mg–Si–Sc–Zr alloy with cold-rolling and aging processes was studied. The result shows that the addition of Sc and Zr elements significantly refines the grains of the Al–Mg–Si alloy during casting. The cold rolling promotes the Al–Sc(Zr) precipitation. The precipitate strengthening increases with increasing roll reduction. The EC of the cold rolling + aging Al–Mg–Si–Sc–Zr alloy increases with increasing rolling reductions. The combination effects of the precipitation hardening and DRX softening during the aging process lead to the similar peak hardness values of around 70 HV of the rolled Al–Mg–Si–Sc–Zr alloy with the different reductions.