The work aimed to develop surfaces that could resist wear at high temperatures, thus achieving a prolonged component life. Surface modification of a low-alloy steel by incorporating TiC particles has been undertaken by melting the surface using a tungsten inert gas torch. The dry sliding wear behaviour at 600°C of the original and modified surfaces was compared. Microscopic examination of both surfaces showed glazed layers across the wear tracks, with differing amounts of oxide and homogeneity. Extensive wear occurred on the steel surface, which showed deformation of the wear scar tracks and a steadily increased friction coefficient. The TiC addition reduced the wear loss, coinciding with a glazed layer 33% thinner than that on the low-alloy steel sample.
AyersJD. Particulate composite surfaces by laser processing. In: MukherjeeK, MajumderJ, editors. Laser in metallurgy. Warrendale ( PA): Metallugical Society of AIME; 1981. p. 115–125.
2.
StephensJR. Intermetallic and ceramic matrix composites for 815 to 1370°C (1500 to 2500°F) gas turbine engine application. Tech. Memo., 102326. CA, USA: NASA; 1990. p. 1–9.
3.
MridhaS, BakerTN. Metal matrix composite layers formed by laser processing of commercial purity Ti-SiCp in nitrogen environment. Mater Sci Technol. 1996;12:595–602. doi: 10.1179/026708396790165984
4.
TerauchiY, NadanoH, KohnoM, Scoring resistance of TiC- and TiN-coated gears. Tribol Int. 1987;20:248–254. doi: 10.1016/0301-679X(87)90024-7
5.
HoweAA. Wear resistant steels. Mater Sci Technol. 2016;32:255–256. doi: 10.1080/02670836.2016.1173435
6.
MridhaS, Md IdrissAN, BakerTN. Incorporation of TiC particulates on AISI 4340 low alloy steel surfaces via tungsten inert gas arc melting. Adv Mater Res. 2012;445:655–660. doi: 10.4028/www.scientific.net/AMR.445.655
7.
MridhaS, TaibNI, Md IdrissAN. Composite coating on steel surfaces by adding TiC and h-BN particulates under TIG torch melting. Adv Mater Res. 2012;576:463–466. doi: 10.4028/www.scientific.net/AMR.576.463
8.
Md IdrissAN, MridhaS. Microstructure of TIG melted composite coating on steel produced using 1.0 and 1.5 mg/mm2 TiC at an energy input of 2640 J/mm. Adv Mater Res. 2012;576:467–470. doi: 10.4028/www.scientific.net/AMR.576.467
9.
MridhaS, Md IdrissAN, MalequeMA, Effect of voltage on the consolidation of TiC particulates on steel substrate fused by TIG welding arc. Int J Mech Mater Eng. 2012;7:48–53.
10.
MridhaS, BakerTN. Overlapping tracks processed by TIG melting TiC preplaced powder on low alloy steel surfaces. Mater Sci Technol. 2015;31:355–360.
11.
MridhaS, Md IdrissAN, MalequeMA, Melting of multipass surface tracks in steel incorporating titanium carbide powders. Mater Sci Technol. 2015;31:1362–1369. doi: 10.1179/1743284714Y.0000000712
12.
Muñoz EscalonaP, MridhaS, BakerTN. Effect of shielding gas on the properties and microstructure of melted steel surface using a TIG torch. Adv Mater Proc Technol. 2015;1:435–443.
13.
SahooCK, SoniL, MasantaM. Evaluation of microstructure and mechanical properties of TiC/TiC-steel composite coating produced by gas tungsten arc (GTA) coating process. Surf Coat Technol. 2016;307:17–27. doi: 10.1016/j.surfcoat.2016.08.056
14.
ChenY, WangHM. High-temperature wear resistance of a laser clad TiC reinforced FeAl in situ composite coating. Surf Coat Technol. 2004;179:252–256. doi: 10.1016/S0257-8972(03)00821-1
15.
FontalvoGA, MittererC. The effect of oxide-forming alloying elements on the high temperature wear of a hot work steel. Wear. 2005;258:1491–1499. doi: 10.1016/j.wear.2004.04.014
16.
DegnanCC, ShipwayPH, WoodJV. Elevated temperature sliding wear behaviour of TiC-reinforced steel matrix composites. Wear. 2001;251:1444–1451. doi: 10.1016/S0043-1648(01)00772-4
17.
ZhangX, MaJ, FuL, High temperature wear resistance of Fe–28Al–5Cr alloy and its composites reinforced by TiC. Tribol Int. 2013;61:48–55. doi: 10.1016/j.triboint.2012.12.005
18.
InmanIA, DattaS, DuHL, Microscopy of glazed layers formed during high temperature sliding wear at 750°C. Wear. 2003;254:461–467. doi: 10.1016/S0043-1648(03)00134-0
19.
JiangJ, StottFH, StackMM. The role of triboparticulates in dry sliding wear. Tribol Int. 1998;31:245–256.
20.
GarbarII. Gradation of oxidational wear of metals. Tribol Int. 2002;35:749–755. doi: 10.1016/S0301-679X(02)00032-4
21.
RasoolG, StackMM. Wear maps for TiC composite based coatings deposited on 303 stainless steel. Tribol Int. 2014;74:93–102. doi: 10.1016/j.triboint.2014.02.002
22.
Md IdrissAN, MalequeMA, YaacobII, Microstructural aspects of wear behaviour of TiC coated low alloy steel. Mater Sci Technol. 2016;32:303–307. doi: 10.1080/02670836.2016.1142049
23.
EasterlingKE. Introduction to physical metallurgy of welding. London: Butterworth-Heinemann; 1992.
24.
SchneiderMF. Laser cladding with powder, effect of some machining parameters on clad properties [PhD thesis]. Enschede (The Netherlands): University of Twente; 1998.
SilcockJM, RaynorD, WilloughbyG. Effect of nitrogen content, titanium content and prior deformation on creep behaviour of nitrided austenitic steels. Metal Sci. 1977;11:551–562. doi: 10.1179/msc.1977.11.12.551
27.
BowkerJT, Ng-YeklimJ, MallisTF. Effect of weld thermal cycle on behaviour of Ti-Nb carbonitrides in HSLA steel. Mater Sci Technol. 1989;5:1034–1036. doi: 10.1179/mst.1989.5.10.1034
28.
KejianH, BakerTN. Zr-containing precipitates in a TiNb microalloyed HSLA steel containing 0.016 wt% Zr addition. Mater Sci Eng A. 1996;215:57–66. doi: 10.1016/0921-5093(96)10267-7
29.
SinghM, WiedemeierH. Estimation of thermal expansion behaviour of some refractory carbides and nitrides. J Mater Sci. 1997;32:5749–5751. doi: 10.1023/A:1018621801987
WangXH, SongSL, ZouZD, Fabricating TiC particles reinforced Fe-based composite coatings produced by GTAW multi-layers melting process. Mater Sci Eng A. 2006;441:60–67. doi: 10.1016/j.msea.2006.06.015
32.
BayerRG. Mechanical wear and fundamental testing. 2nd ed., revised and expanded. New York ( NY): Marcel Dekker; 2004.
33.
KumarS, BhattacharyyaA, MondalDK, Dry sliding wear behaviour of medium carbon steel against an alumina disk. Wear. 2011;270:413–421. doi: 10.1016/j.wear.2010.12.007
34.
RabinowiczE. The least wear. Wear. 1984;100:533–541. doi: 10.1016/0043-1648(84)90031-0
35.
AlamMO, HaseebASMA. Response of Ti–6Al–4V and Ti–24Al–11Nb alloys to dry sliding wear against hardened steel. Tribol Int. 2002;35:357–362. doi: 10.1016/S0301-679X(02)00015-4