Thin films of titanium oxide were obtained by dip-coating, using the sol–gel method. TiO2 powder (Degussa, P25) and polyethylene glycol (PEG) were added to enhance the photocatalytic properties of resulting films. Effects of experimental variables on the photocatalytic properties of the coatings were evaluated based on the degradation efficiency of the reference dye (Methylene blue). The photocatalytic activity of resulting TiO2 coatings was improved with the loading of TiO2 powder (Degussa, P25) and PEG in the sols. The electron-hole pair photogeneration increases with the energy of irradiation and improves photocatalytic efficiency. Increasing coating thickness leads to a rough surface with more reaction sites. Photodegradation conversion of Methylene blue (Mb) decreases with an increase in the initial concentration of Mb.
SajjadnejadM., OmidvarH., JavanbakhtM., PooladiR. and MozafariA.: ‘Direct current electrodeposition of Zn and Zn–SiC nanocompositecoatings', Trans. IMF, 2014, 92, 227–232. doi: 10.1179/0020296714Z.000000000187
2.
SajjadnejadM., MozafariA., OmidvarH. and JavanbakhtM.: ‘Preparation and corrosion resistance of pulse electrodeposited Zn and Zn–SiC nanocomposite coatings', Appl. Surf. Sci., 2014, 300, 1–7. doi: 10.1016/j.apsusc.2013.12.143
3.
SajjadnejadM., GhorbaniM. and AfsharA.: ‘Microstructure-corrosion resistance relationship of direct and pulse current electrodeposited Zn–TiO2 nanocomposite coatings', Ceram. Int., 2015, 41, 217–224. doi: 10.1016/j.ceramint.2014.08.061
4.
OmidvarH., SajjadnejadM., StremsdoerferG., MeasY. and MozafariA.: ‘Characterization of NiBP-graphite composite coatings deposited by dynamic chemical plating', Anti-Corros. Methods Mater., 2015, 62, 116–122. doi: 10.1108/ACMM-11-2013-1320
5.
ArmanS. Y., OmidvarH., TabaianS. H., SajjadnejadM., FouladvandS. and AfsharS.: ‘Evaluation of nanostructured S-doped TiO2 thin films and their photoelectrochemical application as photoanode for corrosion protection of 304 stainless steel', Surf. Coat. Technol., 2014, 251, 162–169. doi: 10.1016/j.surfcoat.2014.04.020
6.
SharmaS. and PeriasamyC.: ‘A study on the electrical characteristic of n-ZnO/p-Si heterojunction diode prepared by vacuum coating technique', Superlattices Microstruct., 2014, 73, 12–21. doi: 10.1016/j.spmi.2014.05.011
7.
LiuC., LiJ. and DengS.: ‘Modification of nanosized anatase titanium dioxide by microwave irradiation', Mater. Sci. Technol., 2007, 22, 147–152.
8.
LinW., KaoL., LiW., HsuC. and HouK.: ‘Fabricating TiO2 photocatalysts by rf reactive magnetron sputtering at varied oxygen partial pressures', J. Mater. Eng. Perform., 2011, 20, 1063–1067. doi: 10.1007/s11665-010-9726-x
9.
FuT., ShenY., AlajmiZ., YangS., SunJ. and ZhangH.: ‘Sol–gel preparation and properties of Ag–TiO2 films on surface roughened Ti–6Al–4V alloy', Mater. Sci. Technol., 2015, 31, 501–505. doi: 10.1179/1743284714Y.0000000650
10.
LiuZ., LiuZ., WangY., LiY., QuL., YaJ. and HuangP.: ‘Photocatalysis of TiO2 nanoparticles supported on natural zeolite', Mater. Sci. Technol., 2012, 27, 267–271.
11.
LiuH., ChengX., YangJ., YanX. and ShH.: ‘Preparation and characterization of nucleus/shell TiO2/HAP complex nanophotocatalyst', J. Mater. Sci. Technol., 2007, 23, 123–126. doi: 10.1179/174328407X158541
12.
CongY., ZhangJ., ChenF., AnpoM. and HeD.: ‘Preparation, photocatalytic activity, and mechanism of nano-TiO2 co-doped with nitrogen and iron (III)', J. Phys. Chem. C, 2007, 111, 10618–10623. doi: 10.1021/jp0727493
13.
ZhuL., JoS. B., YeS., UllahK., MengZ. D. and OhW. C.: ‘A green and direct synthesis of photosensitized CoS2–graphene/TiO2 hybrid with high photocatalytic performance', J. Ind. Eng. Chem., 2015, 22, 264–271. doi: 10.1016/j.jiec.2014.07.019
14.
KhaksarE., AfaraniM. S. and SamimiA.: ‘In situ solvothermal crystallization of TiO2 nanostructure on alumina granules for photocatalytic wastewater treatment', J. Mater. Eng. Perform., 2014, 23, 92–100. doi: 10.1007/s11665-013-0723-8
15.
ZhangW., PeiX., BaiJ. and HeH.: ‘Calcination conditions on the properties of porous TiO2 film', J. Mater. Eng. Perform., 2014, 23, 1049–1054. doi: 10.1007/s11665-013-0833-3
16.
Medina-ValtierraJ., García-ServínJ., Frausto-ReyesC. and CalixtoS.: ‘The photocatalytic application and regeneration of anatase thin films with embedded commercial TiO2 particles deposited on glass microrods', Appl. Surf. Sci., 2006, 252, 3600–3608. doi: 10.1016/j.apsusc.2005.05.045
17.
OshaniF., MarandiR., RasouliS. and FarhoudM. K.: ‘Photocatalytic investigations of TiO2–P25 nanocomposite thin films prepared by peroxotitanic acid modified sol–gel method', Appl. Surf. Sci., 2014, 311, 308–313. doi: 10.1016/j.apsusc.2014.05.059
18.
AndronicL., PerniuD. and DutaA.: ‘Synergistic effect between TiO2 sol–gel and Degussa P25 in dye photodegradation', J. Sol-Gel Sci. Technol., 2013, 66, 472–480. doi: 10.1007/s10971-013-3034-5
SuZ., ZhangL., JiangF. and HongnM.: ‘Formation of crystalline TiO2 by anodic oxidation of titanium', Prog. Nat. Sci.: Mater. Int., 2013, 23, 294–301. doi: 10.1016/j.pnsc.2013.04.004
21.
KotaniY., MatodaT., MatsudaA., KogureT., TatsumisagoM. and MinamiT.: ‘Anatase nanocrystal-dispersed thin films via sol–gel process with hot water treatment: Effects of poly (ethylene glycol) addition on photocatalytic activities of the films', J. Mater. Chem., 2001, 11, 2045–2048. doi: 10.1039/b103043b
22.
WangX., LiJ. G., KamiyamaH., MoriyoshiY. and IshigakiT.: ‘Wavelength-sensitive photocatalytic degradation of methyl orange in aqueous suspension over iron (III)-doped TiO2 nanopowders under UV and visible light irradiation', J. Phys. Chem. B, 2006, 110, 6804–6809. doi: 10.1021/jp060082z
23.
HanaorD. A. and SorrellC. C.: ‘Review of the anatase to rutile phase transformation', J. Mater. Sci., 2011, 46, 855–874. doi: 10.1007/s10853-010-5113-0
24.
SuC., HongB. Y. and TsengC. M.: ‘Sol–gel preparation and photocatalysis of titanium dioxide', Catal. Today, 2004, 96, 119–126. doi: 10.1016/j.cattod.2004.06.132
25.
SchattkaJ. H., ShchukinD. G., JiaJ., AntoniettiM. and CarusoR. A.: ‘Photocatalytic activities of porous titania and titania/zirconia structures formed by using a polymer gel templating technique', Chem. Mater., 2002, 14, 5103–5108. doi: 10.1021/cm021238k
26.
KočíK., ZatloukalováK., ObalováL., KrejčíkováS., LacnýZ., ČapekL., HospodkováA. and ŠolcováO.: ‘Wavelength effect on photocatalytic reduction of CO2 by Ag/TiO2 Catalyst', Chinese J. Catal., 2011, 32, 812–815. doi: 10.1016/S1872-2067(10)60199-4
27.
MatthewsR. W. and McEvoyS. R.: ‘Photocatalytic degradation of phenol in the presence of near-UV illuminated titanium dioxide', J. Photochem. Photobiol. A: Chem., 1992, 64, 231–246. doi: 10.1016/1010-6030(92)85110-G
28.
CaoY., ChenJ., HuangL., WangY., HouY. and LuY.: ‘Photocatalytic degradation of chlorfenapyr in aqueous suspension of TiO2', J. Mol. Catal. A: Chem., 2005, 233, 61–66. doi: 10.1016/j.molcata.2005.02.010
29.
DaneshvarN., SalariD. and KhataeeA.: ‘Photocatalytic degradation of azodye acid red 14 in water on ZnO as an alternative catalyst to TiO2', J. Photochem. Photobiol. A: Chem., 2004, 162, 317–322. doi: 10.1016/S1010-6030(03)00378-2
30.
LakshmiS., RenganathanR. and FujitaS.: ‘Study on TiO2 mediated photocatalytic degradation of methylene blue', J. Photochem. Photobiol. A: Chem., 1995, 88, 163–167. doi: 10.1016/1010-6030(94)04030-6
31.
PouliosI. and AetopoulouI.: ‘Photocatalytic degradation of the textile dye reactive orange 16 in the presence of TiO2 suspensions', Environ. Technol., 1999, 20, 479–487. doi: 10.1080/09593332008616843
32.
SoC., ChengM. Y., YuJ. and WongP.: ‘Degradation of azo dye Procion Red MX-5B by photocatalyticoxidation', Chemosphere, 2002, 46, 905–912. doi: 10.1016/S0045-6535(01)00153-9
33.
TangW. Z. and AnH.: ‘UV/TiO2 photocatalytic oxidation of commercial dyes in aqueous solutions', Chemosphere, 1995, 31, 4157–4170. doi: 10.1016/0045-6535(95)80015-D
34.
ChunH., YizhongW. and HongxiaoT.: ‘Destruction of phenol aqueous solution by photocatalysis or direct photolysis', Chemosphere, 2000, 41, 1205–1209. doi: 10.1016/S0045-6535(99)00539-1
35.
WuC. Y., LeeY. L., LoY. S., LinC. J. and WuC. H.: ‘Thickness-dependent photocatalytic performance of nanocrystalline TiO2 thin films prepared by sol–gel spin coating', Appl. Surf. Sci., 2013, 280, 737–744. doi: 10.1016/j.apsusc.2013.05.053