Fatigue cracks in titanium alloys are often found to initiate at faceted alpha grains. In the very high cycle fatigue regime, crack initiation tends to shift from the surface towards the interior of the material, and more initiation facets can be found on the fracture surface. In this study, fatigue tests were performed on drawn and heat-treated Ti–6Al–4V wires. Only a few samples fractured due to interior initiation. The facets at the initiation sites of these samples were not flat, but had markings on the nano-scale, and were highly inclined. A possible explanation for these aspects is the crystallographic texture of the wire, and a reflection is made on the suggested mechanisms of facet formation.
This paper is part of a Themed Issue on Euromech 570: Interface-dominated materials.
BoyerR. R.: ‘An overview on the use of titanium in the aerospace industry’, Mater. Sci. Eng. A – Struct. Mater. Prop. Microstruct. Process., 1996, 213, (1–2), 103–114. doi: 10.1016/0921-5093(96)10233-1
2.
Marines-GarciaI., ParisP. C., TadaH., BathiasC., and LadosD.: ‘Fatigue crack growth from small to large cracks on very high cycle fatigue with fish-eye failures’, Eng. Fract. Mech., 2008, 75, (6), 1657–1665. doi: 10.1016/j.engfracmech.2007.05.015
3.
ZuoJ. H., WangZ. G., and HanE. H.: ‘Effect of microstructure on ultra-high cycle fatigue behavior of Ti–6Al–4V’, Mater. Sci. Eng. A – Struct. Mater. Prop. Microstruct. Process., 2008, 473, (1–2), 147–152. doi: 10.1016/j.msea.2007.04.062
4.
HamadaM. and UmezawaO.: ‘Evaluation of subsurface fatigue crack life in forged Ti–6Al–4V alloys at cryogenic temperatures’, ISIJ Int., 2009, 49, (1), 124–131. doi: 10.2355/isijinternational.49.124
5.
KazymyrovychV.: ‘Very high cycle fatigue of engineering materials: a literature review’; 2009, Karlstad, Sweden, Karlstad University Studies.
6.
BathiasC.: ‘There is no infinite fatigue life in metallic materials’, Fatigue Fract. Eng. Mater. Struct., 1999, 22, (7), 559–565. doi: 10.1046/j.1460-2695.1999.00183.x
7.
JhaS. K., SzczepanskiC. J., GoldenP. J., PorterW. J., and JohnR.: ‘Characterization of fatigue crack-initiation facets in relation to lifetime variability in Ti–6Al–4V’, Int. J. Fatigue, 2012, 42, 248–257. doi: 10.1016/j.ijfatigue.2011.11.017
8.
FuruyaY. and TakeuchiE.: ‘Gigacycle fatigue properties of Ti–6Al–4V alloy under tensile mean stress’, Mater. Sci. Eng. A – Struct. Mater. Prop. Microstruct. Process., 2014, 598, 135–140. doi: 10.1016/j.msea.2014.01.019
9.
AtrensA., HoffelnerW., DuerigT. W., and AllisonJ. E.: ‘Subsurface crack initiation in high cycle fatigue in Ti6Al4V and in a typical martensitic stainless-steel’, Scr. Metall., 1983, 17, (5), 601–606. doi: 10.1016/0036-9748(83)90385-X
10.
NealD. F. and BlenkinsopP. A.: ‘Internal fatigue origins in alpha–beta titanium-alloys’, Acta Metall., 1976, 24, (1), 59–63. doi: 10.1016/0001-6160(76)90147-4
11.
OgumaH. and NakamuraT.: ‘The effect of microstructure on very high cycle fatigue properties in Ti–6Al–4V’, Scr. Mater., 2010, 63, (1), 32–34. doi: 10.1016/j.scriptamat.2010.02.043
12.
NallaR. K., BoyceB. L., CampbellJ. P., PetersJ. O., and RitchieR. O.: ‘Influence of microstructure on high-cycle fatigue of Ti–6Al–4V: bimodal vs. lamellar structures’, Metall. Mater. Trans. A – Phys. Metall. Mater. Sci., 2002, 33, (3), 899–918. doi: 10.1007/s11661-002-0160-z
13.
JhaS. K. and ChandranK. S. R.: ‘An unusual fatigue phenomenon: duality of the S–N fatigue curve in the beta-titanium alloy Ti–10V–2Fe–3Al’, Scr. Mater., 2003, 48, (8), 1207–1212. doi: 10.1016/S1359-6462(02)00565-1
14.
UmezawaO. and NagaiK.: ‘Fatigue, cyclic deformation and microstructure. Subsurface crack generation in high-cycle fatigue for high strength alloys.’, ISIJ Int., 1997, 37, (12), 1170–1179. doi: 10.2355/isijinternational.37.1170
15.
TakeuchiE., FuruyaY., NagashimaN., and MatsuokaS.: ‘The effect of frequency on the giga-cycle fatigue properties of a Ti–6Al–4V alloy’, Fatigue Fract. Eng. Mater. Struct., 2008, 31, (7), 599–605. doi: 10.1111/j.1460-2695.2008.01257.x
16.
OgumaH. and NakamuraT.: ‘The effect of stress ratios on very high cycle fatigue properties of Ti-6AI-4V’, in ‘Advances in fracture and failure prevention, Pts 1 and 2’, (ed. KishimotoK.), 1227–1232; 2004, Zurich-Uetikon, Trans Tech.
17.
McEvilyA. J., NakamuraT., OgumaH., YamashitaK., MatsunagaH., and EndoM.: ‘On the mechanism of very high cycle fatigue in Ti–6Al–4V’, Scr. Mater., 2008, 59, (11), 1207–1209. doi: 10.1016/j.scriptamat.2008.08.012
18.
HeinzS., BalleF., WagnerG., and EiflerD.: ‘Analysis of fatigue properties and failure mechanisms of Ti6Al4V in the very high cycle fatigue regime using ultrasonic technology and 3D laser scanning vibrometry’, Ultrasonics, 2013, 53, (8), 1433–1440. doi: 10.1016/j.ultras.2013.03.002
19.
BathiasC., DrouillacL., and Le FrancoisP.: ‘How and why the fatigue S–N curve does not approach a horizontal asymptote’, Int. J. Fatigue, 2001, 23, 143–151. doi: 10.1016/S0142-1123(01)00123-2
20.
YokoyamaH., UmezawaO., NagaiK., and SuzukiT.: ‘Fatigue, cyclic deformation and microstructure. Distribution of internal crack initiation sites in high-cycle fatigue for titanium alloys.’, ISIJ Int., 1997, 37, (12), 1237–1244. doi: 10.2355/isijinternational.37.1237
21.
PatonN. E., WilliamsJ. C., ChesnuttJ. C., and ThompsonA. W., ‘The effects of microstructure on the fatigue and fracture of commercial titanium alloys’, in Specialists meeting on alloy design for fatigue and fracture resistance: papers presented at the ‘40th meeting of the structures and materials panel in Brussels’, Belgium, 13–19 April 1975. 1976, 1976, London, London Agard.
22.
LambrighsK., WeversM., VerlindenB., and VerpoestI.: ‘A fracture mechanics approach to fatigue of heavily drawn steel wires’, 11th Int. Conf. on ‘Mechanical behavior of materials (ICM11)’, Como, Italy, 2011, 10, 3259–3266.
23.
SteeleR. K. and McEvilyA. J.: ‘High-cycle fatigue behavior of Ti–6Al–4V alloy’, Eng. Fract. Mech., 1976, 8, (1), 31–37. doi: 10.1016/0013-7944(76)90075-8
24.
LindemannJ. and WagnerL.: ‘Mean stress sensitivity in fatigue of alpha, (alpha + beta) and beta titanium alloys’, Mater. Sci. Eng. A – Struct. Mater. Prop. Microstruct. Process., 1997, 234–236, 1118–1121. doi: 10.1016/S0921-5093(97)00347-X
25.
OnoY., YuriT., SumiyoshiH., MatsuokaS., and OgataT.: ‘Subsurface fracture in high-cycle fatigue at cryogenic temperatures in Ti–5% Al–2.5% Sn extra low interstitial alloy’, Mater. Trans., 2003, 44, (9), 1702–1705. doi: 10.2320/matertrans.44.1702
26.
IvanovaS. G., BiedermanR. R., and SissonR. D.: ‘Investigation of fatigue crack initiation in Ti–6Al–4V during tensile–tensile fatigue’, J. Mater. Eng. Perform., 2002, 11, (2), 226–231. doi: 10.1361/105994902770344312
27.
BridierF., VillechaiseP., and MendezJ.: ‘Slip and fatigue crack formation processes in an alpha/beta titanium alloy in relation to crystallographic texture on different scales’, Acta Mater., 2008, 56, (15), 3951–3962. doi: 10.1016/j.actamat.2008.04.036
BacheM. R.: ‘Processing titanium alloys for optimum fatigue performance’, Int. J. Fatigue, 1999, 21, 105–111. doi: 10.1016/S0142-1123(99)00061-4
30.
PilchakA. L., BhattacharjeeA., RosenbergerA. H., and WilliamsJ. C.: ‘Low delta K faceted crack growth in titanium alloys’, Int. J. Fatigue, 2009, 31, (5), 989–994. doi: 10.1016/j.ijfatigue.2008.03.036
31.
BantounasI., DyeD., and LindleyT. C.: ‘The role of microtexture on the faceted fracture morphology in Ti–6Al–4V subjected to high-cycle fatigue’, Acta Mater., 2010, 58, (11), 3908–3918. doi: 10.1016/j.actamat.2010.03.036
32.
Sarrazin-BaudouxC.: ‘Environmentally influenced fatigue crack path in titanium alloys’, Proc. of ‘Fatigue crack paths (FCP 2003)’, Parma, Italy, 2003.
33.
BacheM. R., EvansW. J., and McElhoneM.: ‘The effects of environment and internal oxygen on fatigue crack propagation in Ti–6Al–4V’, Mater. Sci. Eng. A – Struct. Mater. Prop. Microstruct. Process., 1997, 234-236, 918–922. doi: 10.1016/S0921-5093(97)00402-4
34.
PykaG., BurakowskiA., KerckhofsG., MoesenM., Van BaelS., SchrootenJ., and WeversM.: ‘Surface modification of Ti6Al4V open porous structures produced by additive manufacturing’, Adv. Eng. Mater., 2012, 14, (6), 363–370. doi: 10.1002/adem.201100344
35.
AkahoriT. and NiinomiM.: ‘Fracture characteristics of fatigued Ti–6Al–4V ELI as an implant material’, Mater. Sci. Eng. A – Struct. Mater. Prop. Microstruct. Process., 1998, 243, (1–2), 237–243. doi: 10.1016/S0921-5093(97)00807-1
36.
OgumaH.: ‘Very high cycle fatigue properties of Ti–6Al–4V alloy’, PhD thesis, Hokkaido University, Hokkaido, 2006, 152–157.
37.
KnobbeH., KosterP., ChristH. J., FritzenC. P., and RiedlerM.: ‘Initiation and propagation of short fatigue cracks in forged Ti6Al4V’, Fatigue 2010, 2010, 2, (1), 931–940.
38.
BantounasI., DyeD., and LindleyT. C.: ‘The effect of grain orientation on fracture morphology during high-cycle fatigue of Ti–6Al–4V’, Acta Mater., 2009, 57, (12), 3584–3595. doi: 10.1016/j.actamat.2009.04.018