The powder spreading process is usually performed at preheating temperature in powder-bed-based additive manufacturing (AM). Thus, the powder flowability characterisation at preheating temperature is important for powder spreading processes. However, devices for traditional powder flowability characterising methods are mainly designed for specific conditions at room temperature and cannot consider the effect of temperature on powder flowability. In this work, an experimental platform with a heated rotating drum was set up and a high-speed camera was used to record powder avalanche processes in a heated rotating drum for the powder flowability characterisation at preheating temperature. Nylon and stainless steel powder flowability at different temperatures was assessed by the statistical analysis of avalanche angle, avalanche time, arithmetic mean deviation and surface linearity of powder surface profile. Four parameters provide a good characterisation of powder flowability. The results can provide guidance for the powder flowability characterisation method at preheating temperature in AM.
HearnW, HarlinP, HryhaE.Development of powder bed fusion – laser beam process for AISI 4140, 4340 and 8620 low-alloy steel. Powder Metall. 2022: 1–13. doi:10.1080/00325899.2022.2134083
3.
MengW, XiaohuiY, ZhangW, . Additive manufacturing of a functionally graded material from Inconel625 to Ti6Al4V by laser synchronous preheating. J Mater Process Technol. 2020;275:116368. doi:10.1016/j.jmatprotec.2019.116368
4.
AraiS, TsunodaS, YamaguchiA, . Effects of short-glass-fiber content on material and part properties of poly (butylene terephthalate) processed by selective laser sintering. Addit Manuf. 2018;21:683–693. doi:10.1016/j.addma.2018.04.019
5.
ZhangJ, TanY, XiaoX, . Comparison of roller-spreading and blade-spreading processes in powder-bed additive manufacturing by DEM simulations. Particuology. 2022;66:48–58. doi:10.1016/j.partic.2021.07.005
6.
Beakawi Al-HashemiHM, Baghabra Al-AmoudiOS.A review on the angle of repose of granular materials. Powder Technol. 2018;330:397–417. doi:10.1016/j.powtec.2018.02.003
7.
VlachosN, ChangITH.Investigation of flow properties of metal powders from narrow particle size distribution to polydisperse mixtures through an improved Hall-flowmeter. Powder Technol. 2011;205(1-3):71–80. doi:10.1016/j.powtec.2010.08.067
8.
CarsonJW, WilmsH.Development of an international standard for shear testing. Powder Technol. 2006;167(1):1–9. doi:10.1016/j.powtec.2006.04.005
9.
KoynovS, GlasserB, MuzzioF.Comparison of three rotational shear cell testers: powder flowability and bulk density. Powder Technol. 2015;283:103–112. doi:10.1016/j.powtec.2015.04.027
10.
SchüsseleA, Bauer-BrandlA.Note on the measurement of flowability according to the European pharmacopoeia. Int J Pharm. 2003;257(1-2):301–304. doi:10.1016/S0378-5173(03)00142-X
11.
SpieringsA, VoegtlinM, BauerT, . Powder flowability characterisation methodology for powder-bed-based metal additive manufacturing. Prog Addit Manuf. 2016;1(1-2):9–20. doi:10.1007/s40964-015-0001-4
12.
TanY, ZhangJ, LiX, . Comprehensive evaluation of powder flowability for additive manufacturing using principal component analysis. Powder Technol. 2021;393:154–164. doi:10.1016/j.powtec.2021.07.069
13.
MarchettiL, Hulme-SmithC.Flowability of steel and tool steel powders: a comparison between testing methods. Powder Technol. 2021;384:402–413. doi:10.1016/j.powtec.2021.01.074
14.
TomasettaI, BarlettaD, PolettoM.Correlation of powder flow properties to interparticle interactions at ambient and high temperatures. Particuology. 2014;12:90–99. doi:10.1016/j.partic.2013.02.002
15.
TomasettaI, BarlettaD, PolettoM.The high temperature annular shear cell: a modified ring shear tester to measure the flow properties of powders at high temperature. Adv Powder Technol. 2013;24(3):609–617. doi:10.1016/j.apt.2012.11.007
16.
MaarupC, HjulerK, Dam-JohansenK.High temperature cement raw meal flowability. Powder Technol. 2014;253:686–690. doi:10.1016/j.powtec.2013.12.040
17.
KrantzM, ZhangH, ZhuJ.Characterization of powder flow: static and dynamic testing. Powder Technol. 2009;194(3):239–245. doi:10.1016/j.powtec.2009.05.001
18.
CapozziL, SivoA, BassiniE.Powder spreading and spreadability in the additive manufacturing of metallic materials: a critical review. J Mater Process Technol. 2022;308:117706. doi:10.1016/j.jmatprotec.2022.117706
19.
PleassC, JothiS.Influence of powder characteristics and additive manufacturing process parameters on the microstructure and mechanical behaviour of Inconel 625 fabricated by selective laser melting. Addit Manuf. 2018;24:419–431. doi:10.1016/j.addma.2018.09.023
20.
MellmannJ.The transverse motion of solids in rotating cylinders – forms of motion and transition behavior. Powder Technol. 2001;118(3):251–270. doi:10.1016/S0032-5910(00)00402-2
21.
PirardS, LumayG, VandewalleN, . Motion of carbon nanotubes in a rotating drum: the dynamic angle of repose and a bed behavior diagram. Chem Eng J. 2009;146(1):143–147. doi:10.1016/j.cej.2008.09.015
22.
RippM, RippergerS.Influence of temperature on the flow properties of bulk solids. Chem Eng Sci. 2010;65(13):4007–4013. doi:10.1016/j.ces.2010.03.046
23.
RuggiD, LupoM, SofiaD, . Flow properties of polymeric powders for selective laser sintering. Powder Technol. 2020;370:288–297. doi:10.1016/j.powtec.2020.05.069
24.
LiuX, ZhouS, SpechtE.Avalanche time of granular flows in rotary kilns. Chem Eng Technol. 2010;33(6):1029–1033. doi:10.1002/ceat.200900533
25.
SevilleJPK, WillettCD, KnightPC.Interparticle forces in fluidisation: a review. Powder Technol. 2000;113(3):261–268. doi:10.1016/S0032-5910(00)00309-0
26.
XieH.The role of interparticle forces in the fluidization of fine particles. Powder Technol. 1997;94(2):99–108. doi:10.1016/S0032-5910(97)03270-1
27.
RuggiD, BarrèsC, CharmeauJ, . A quantitative approach to assess high temperature flow properties of a PA 12 powder for laser sintering. Addit Manuf. 2020;33:101143. doi:10.1016/j.addma.2020.101143