The current work evaluates the wear and frictional performance of ultrahigh molecular weight polyethylene (UHMWPE) and high density polyethylene (HDPE) sliding against different metal counterfaces, stainless steel(SS), mild steel (MS) and aluminium (Al), under dry contact condition. The experiments were conducted using pin on disc machine at different sliding distances (0–40·32 km), 15 N applied load and 2·8 m s^–1 sliding velocity. Interface temperatures and frictional forces were measured simultaneously during the sliding, while specific wear rates were determined for every 1·68 km sliding distance. Based on the optical microscopy of the worn surface and wear track, frictional and wear results were analysed and discussed. The experimental results showed that the type of counterface material significantly influences both frictional and wear performances of the selected polymers. This was mainly due to the film transfer characteristics. Higher temperature and friction coefficient for UHMWPE and HDPE were evident when sliding took place against Al counterface. Sliding the polymers against stainless steel showed low friction coefficients compared to other counterfaces.

28:T420,

For several years different types of nanoparticles have been considered and studied as potential friction modifying lubricant additives. Some nanoparticles can reduce the friction coefficient by 30–70%, depending on the base oil and the experimental conditions. In the present study, an experimental analysis on tribological properties of inorganic fullerene-like metal dichalcogenides was performed in comparison with MoS₂ 2H layered structures. Tribological tests were carried out on a pin on disc tribometer in ambient air. Several contact conditions are analysed in order to realise boundary and mixed lubrication regimes. The experimental study was performed on a mineral base oil, and particle concentration effects were analysed. Antifriction properties were evaluated by measuring the friction coefficient and are presented as generalised Stribeck diagrams. Inorganic fullerene-like WS₂ and MoS₂ nanoparticles present interesting friction reduction properties when tested in boundary and mixed lubrication.

29:T78a,