Most commercial dental composites contain liquid dimethacrylate monomers (including BIS-GMA or variations of it) and silica-containing compositions as inorganic reinforcing filler particles coated with methacrylate-functional silane coupling agents to bond the resin to the filler. They also contain initiators, accelerators, photo-initiators, photosensitizers, polymerization inhibitors, and UV absorbers.

Durability is a major problem with posterior composites. The typical life-span of posterior composites is from three to 10 years, with large fillings usually fewer than five years. Polymerization shrinkage and inadequate adhesion to cavity walls are remaining problems. Some pulp irritation can occur if deep restorations are not placed over a protective film. Some have advocated the use of glass-ionomer cement as a lining under resin composite restorations in dentin.

The concept of glass-ionomer cements (GICs) was introduced to the dental profession in the early 1970's. Current GICs may contain poly(acrylic acid) or a copolymer. Higher-molecular-weight copolymers may also be used to improve the physical properties of some GICs. Stronger and less-brittle hybrid materials have been produced by the addition of watersoluble compatible polymers to form light-curing GIC formulations.

The ion-leachable aluminosilicate glass powder, in an aqueous solution of a polymer or copolymer of acrylic acid, is attacked by the hydrated protons of the acid, causing the release of aluminum and calcium ions. Salt bridges are formed, and a gel matrix surrounds the unreacted glass particles. The matrix is adhesive to mineralized tissues. Provisions must be made for maintenance of the water balance of restorations for the first 24 hours. A varnish to seal newly-placed restorations is provided by most manufacturers. The introduction of metal powder to GICs significantly improved abrasion resistance.