Corrosion of the head-neck junction of the femoral component in total hip arthroplasty has been associated with symptomatic adverse local tissue reactions, trunion fracture and elevated serum metal ions. An analysis of risk factors and treatment strategies for corrosion at this interface is lacking in the literature. We therefore performed a systematic review of AAOS proceedings, MEDLINE and EMBASE databases, and included our own case series. A total of 24 articles representing 776 cases of head-neck corrosion met inclusion criteria. The combination of large femoral head sizes and small taper dimensions comprised the majority of published corrosion cases. Revision to ceramic head and ceramic/polyethylene liner was the most commonly utilised treatment. Coating precipitation, mixed alloy coupling and head-neck modulus mismatch collectively appear to contribute to the corrosive process.
KopAMSwartsECorrosion of a hip stem with a modular neck taper junction: a retrieval study of 16 cases.J Arthroplasty. 2009;24(7):1019–1023.
2.
JacobsJJUrbanRMGilbertJLLocal and distant products from modularity.Clin Orthop Relat Res. 1995;(319):94–105.
3.
CollierJPMayorMBWilliamsIRSurprenantVASurprenantHPCurrierBHThe tradeoffs associated with modular hip prostheses.Clin Orthop Relat Res. 1995;(311):91–101.
4.
FrickaKBHoHPeaceWJEnghCAJrMetal-on-metal local tissue reaction is associated with corrosion of the head taper junction.J Arthroplasty. 2012;27(8 Suppl):26–31.e1.
5.
CooperHJDella ValleCJBergerRACorrosion at the head-neck taper as a cause for adverse local tissue reactions after total hip arthroplasty.J Bone Joint Surg Am. 2012;94(18):1655–1661.
6.
PansardESevere corrosion after malpositioning of a metallic head over the Morse taper of a cementless hip arthroplasty. A case report.Orthop Traumatol Surg Res. 2012;98(2):247–250.
7.
ChanaREspositoCCampbellPAWalterWKWalterWLMixing and matching causing taper wear: corrosion associated with pseudotumour formation.J Bone Joint Surg Br. 2012;94(2):281–286.
8.
LindgrenJUBrismarBHWikstromACAdverse reaction to metal release from a modular metal-on-polyethylene hip prosthesis.J Bone Joint Surg Br. 2011;93(10):1427–1430.
9.
AntoniouJZukorDJMwaleFMinarikWPetitAHukOLMetal ion levels in the blood of patients after hip resurfacing: a comparison between twenty-eight and thirty-six-millimeter-head metal-on-metal prostheses.J Bone Joint Surg Am. 2008;90Suppl 3:142–148.
10.
BalBSVandeluneDGurbaDMJastyMHarrisWHPolyethylene wear in cases using femoral stems of similar geometry, but different metals, porous layer, and modularity.J Arthroplasty. 1998;13(5):492–499.
11.
BollandBJCullifordDJLangtonDJMillingtonJPArdenNKLathamJMHigh failure rates with a large-diameter hybrid metal-on-metal total hip replacement: clinical, radiological and retrieval analysis.J Bone Joint Surg Br. 2011;93(5):608–615.
12.
BonnaigNSFreibergRAFreibergAATotal hip arthroplasty with ceramic-on-ceramic bearing failure from third-body wear.Orthopedics. 2011;34(2):132.
13.
BottiTPGentJMartellJMManningDWTrunion fracture of a fully porous-coated femoral stem. Case report.J Arthroplasty. 2005;20(7):943–945.
14.
GoldbergJRGilbertJLJacobsJJBauerTWPaproskyWLeurgansSA multicenter retrieval study of the taper interfaces of modular hip prostheses.Clin Orthop Relat Res. 2002;2002(401):149–161.
15.
HartAJHexterASkinnerJA study of taper corrosion in 111 current generation large diameter metal-on-metal hip components. 2012 Annual Meeting of the American Academy of Orthopaedic Surgeons.San Francisco: AAOS2012.
16.
Huot CarlsonJCVan CittersDWCurrierJHBryantAMMayorMBCollierJPFemoral stem fracture and in vivo corrosion of retrieved modular femoral hips.J Arthroplasty. 2012;27(7):1389–1396.e1381.
17.
KhairMMNamDDiCarloESuEAseptic lymphocyte dominated vasculitis-associated lesion resulting from trunnion corrosion in a cobalt-chrome unipolar hemiarthroplasty.J Arthroplasty. 2013;28(1):196.e11-14.
18.
LangtonDJJamesonSSJoyceTJAccelerating failure rate of the ASR total hip replacement.J Bone Joint Surg Br. 2011;93(8):1011–1016.
19.
MaoXTayGHGodboltDBCrawfordRWPseudotumor in a well-fixed metal-on-polyethylene uncemented hip arthroplasty.J Arthroplasty. 2012;27(3):e13–e17.
20.
MeftahMNicolaouNRodriguezJAMetal allergy response to femoral head-neck corrosion after total hip replacement.Curr Orthop Pract. 2010;21(5):530–533.
21.
UnnanuntanaAChenDXUnnanuntanaAWrightTMTrunnion fracture of the anatomic medullary locking a plus femoral component.J Arthroplasty. 2011;26(3):e13–e16.
22.
CookRBBollandBJWhartonJATilleySLathamJMWoodRJPseudotumour formation due to tribocorrosion at the taper interface of large diameter metal on polymer modular total hip replacements.J Arthroplasty. 2013;28(8):1430–1436.
23.
LangtonDJSidaginamaleRLordJKNargolAVJoyceTJTaper junction failure in large-diameter metal-on-metal bearings.Bone Joint Res. 2012;1(4):56–63.
24.
MatthiesAKRacasanRBillsPMaterial loss at the taper junction of retrieved large head metal-on-metal total hip replacements.J Orthop Res. 2013;31(11):1677–1685.
25.
NassifNANawabiDHStonerKElpersMWrightTPadgettDETaper design affects failure of large-head metal-on-metal total hip replacements.Clin Orthop Relat Res. 2014;472(2):564–571.
26.
ScullyWFTeenySMPseudotumor associated with metal-on-polyethylene total hip arthroplasty.Orthopedics. 2013;36(5):e666–e670.
27.
AtwoodSAPattenEWBozicKJPruittLARiesMDCorrosion-induced fracture of a double-modular hip prosthesis: a case report.J Bone Joint Surg Am. 2010;92(6):1522–1525.
28.
JacobsJJGilbertJLUrbanRMCorrosion of metal orthopaedic implants.J Bone Joint Surg Am. 1998;80(2):268–282.
29.
GarbuzDSTanzerMGreidanusNVMasriBADuncanCPThe John Charnley Award: Metal-on-metal hip resurfacing versus large-diameter head metal-on-metal total hip arthroplasty: a randomized clinical trial.Clin Orthop Relat Res. 2010;468(2):318–325.
30.
GilbertJLBuckleyCAJacobsJJBertinKCZernichMRIntergranular corrosion-fatigue failure of cobalt-alloy femoral stems. A failure analysis of two implants.J Bone Joint Surg Am. 1994;76(1):110–115.
31.
UrbanRHallDGilbertJDella ValleCGalanteJJacobsJHave Fretting and Corrosion Been Reduced in Contemporary Head/Neck Modular Junctions? 2012 Annual Meeting of the American Academy of Orthopaedic Surgery.San Francisco: AAOS2012.
32.
JacobsJModularity Corrosion. Orthopaedic Research Society Annual Meeting.San Antonio: Orthoaedic Research Society2013.
33.
BrownSAFlemmingCAKawalecJSFretting corrosion accelerates crevice corrosion of modular hip tapers.J Appl Biomater. 1995;6(1):19–26.
34.
WeisseBAffolterCStutzATerrasiGPKöbelSWeberWInfluence of contaminants in the stem-ball interface on the static fracture load of ceramic hip joint ball heads.Proc Inst Mech Eng H. 2008;222(5):829–835.
35.
WuttkeVWitteHKempfKOberbachTDelfosseDInfluence of various types of damage on the fracture strength of ceramic femoral heads.Biomed Tech (Berl). 2011;56(6):333–339.
36.
BergmannGGraichenFRohlmannAHip joint loading during walking and running, measured in two patients.J Biomech. 1993;26(8):969–990.