Analysis of surface conditioning methods on core-veneer bond strength of CAD/CAM zirconia restorations

Abstract

BACKGROUND:

The increased strength of zirconia has resulted in its widespread application in clinical dentistry. Nevertheless, the fracture of veneering porcelains remains one of the key reasons of failure.

OBJECTIVE:

The objective of this study was to compare and analyze the influence of surface conditioning methods on the core-veneer bond strength of zirconia restorations.

METHODS:

Thirty specimens of zirconia core with sizes 10 $\times$ 5 $\times$ 5 mm were layered with porcelain of sizes 5 $\times$ 3 $\times$ 3 mm. On the basis of different surface conditioning methods, four groups were made: Group I: abrasion with airborne alumina particles of 110 $\mu$ m size, Group II: sandblasting with silica coated alumina particles of 50 $\mu$ m in size, Group III (modified group): alteration with a coating of zirconia powder prior to sintering, and Group IV (control group): metal core specimens. The shear force of all specimens was tested using a universal testing machine with a 0.5 mm/min crosshead speed. One-way analysis of variance (ANOVA) and Tukey’s post hoc pair wise comparison ( $p=$ 0.05) were performed to analyze the shear bond strength. A scanning electron microscope was used to assess the fractured specimens.

RESULTS:

A statistically significant difference was noted between the groups. The mean value of shear bond strength was 40.25 MPa for Group I, 41.93 MPa for Group II, 48.08 MPa for Group III and 47.01 MPa for Group IV.

CONCLUSIONS:

The modified zirconia group and control group demonstrated a significantly higher mean bond strength than that of Group I, where airborne particle abrasion was used. The scanning electron microscope showed that cohesive fracture in the porcelain veneers was the main problem of failure in altered zirconia. The modified zirconia specimens in Group III demonstrated significantly improved values of shear bond strength.