Tensile Behavior of Pultruded Fiber-Reinforced Polymer Laminates with Bonded and Bolted Splice Joints

Abstract

This paper presents an experimental investigation on double-lap joints of grit-blasted surface finish fiber-reinforced polymer (FRP) splice plates bonded and bolted to FRP laminates. Eighteen coupon joint specimens were tested under tensile loading with varying types of FRP splice plates and FRP laminates. Four types of bolts were evaluated: FRP bolts, high corrosion-resistant steel (HCRS) bolts, stainless steel (SS) bolts, and SS bolts wrapped with glass FRP (GFRP) (referred to as “SF” bolts). The test results indicated that double-lap splice joints, which incorporated HCRS bolts, epoxy adhesive, and grit-blasted surface finish FRP splice plates, provided strong bonds with FRP laminates. The grit-blasted surface finish of the FRP splice plates and the epoxy adhesive contributed to improving joint stiffness and strength. The specimens with FRP bolts showed brittle behavior and failed at relatively low ultimate load. The failures of those specimens were debonding of epoxy layers followed by shearing of the FRP bolts. The specimens with steel bolts (i.e., HCRS, SS, and SF bolts), however, exhibited ductile behavior and failed at a much higher ultimate load than did the FRP bolt specimens. Typical failure modes of the steel bolt specimens were fracturing of the FRP laminate (resulting from fiber rupture or kink, shear-out, and delamination failure of the GFRP plies and bearing failure of FRP materials near the edge of bolt holes in the load direction), bearing failure of the FRP splice plates, epoxy debonding, and yielding of bolts. Although FRP wraps may enhance the durability of the SS bolts, the use of SF bolts may significantly affect the failure mode of the splice joints.

Get full access to this article

View all access options for this article.

References

Nguyen

, Mutsuyoshi

, Asamoto

, and Matsui

. Structural Behavior of Hybrid FRP Composite I-Beam. Journal of Construction and Building Materials, Vol. 24, No. 6, June 2010, pp. 956–969. https://doi.org/10.1016/j.conbuildmat.2009.11.022.

Nguyen

, Mutsuyoshi

, and Zatar

. Hybrid FRP-UHPFRC Composite Girders: Part 1—Experimental and Numerical Approach. Journal of Composite Structures, Vol. 125, 2015, pp. 631–652. https://doi.org/10.1016/j.compstruct.2014.10.038.

Nguyen

, Zatar

, and Mutsuyoshi

. Hybrid FRP-UHPFRC Composite Girders: Part 2—Analytical Approach. Journal of Composite Structures, Vol. 125, 2015, pp. 653–671. https://doi.org/10.1016/j.compstruct.2014.12.001.

Nguyen

, Mutsuyoshi

, and Zatar

. Push-Out Tests for Shear Connections Between UHPFRC Slabs and FRP Girder. Journal of Composite Structures, Vol. 118, 2014, pp. 528–547. https://doi.org/10.1016/j.compstruct.2014.08.003.

Nguyen

, Zatar

, and Mutsuyoshi

. Hybrid Fiber-Reinforced Polymer Girders Topped with Segmental Precast Concrete Slabs for Accelerated Bridge Construction. Transportation Research Record: Journal of the Transportation Research Board, No. 2407, 2014, pp. 83–93. https://dx.doi.org/10.3141/2407-08.

Nguyen

, Mutsuyoshi

, and Zatar

. Flexural Behavior of Hybrid Composite Beams. Transportation Research Record: Journal of the Transportation Research Board, No. 2332, 2013, pp. 53–63. https://dx.doi.org/10.3141/2332-06.

Turvey

G. J.

, and Cerutti

. Flexural Behaviour of Pultruded Glass Fibre Reinforced Polymer Composite Beams with Bolted Splice Joints. Journal of Composite Structures, Vol. 119, 2015, pp. 543–550. https://doi.org/10.1016/j.compstruct.2014.09.013.

Turvey

G. J.

, and Cerutti

. Effects of Splice Joint Geometry and Bolt Torque on the Serviceability Response of Pultruded Glass Fibre Reinforced Polymer Composite Beams. Journal of Composite Structures, Vol. 131, 2015, pp. 490–500. https://doi.org/10.1016/j.compstruct.2015.05.030.

Camanho

P. P.

, and Matthews

F. L.

. Stress Analysis and Strength Prediction of Mechanically Fastened Joints in FRP: A Review. Journal of Composites Part A, Vol. 28, No. 6, 1997, pp. 529–547. https://doi.org/10.1016/S1359-835X(97)00004-3.

10.

Thoppul

S. D.

, Finegan

, and Gibson

R. F.

. Mechanics of Mechanically Fastened Joints in Polymer–Matrix Composite Structures: A Review. Journal of Composites Science and Technology, Vol. 69, No. 3-4, 2009, pp. 301–329. https://doi.org/10.1016/j.compscitech.2008.09.037.

11.

Mottram

J. T.

, and Zheng

. State-of-the-Art Review on the Design of Beam-to-Column Connections for Pultruded Frames. Journal of Composite Structures, Vol. 35, No. 4, 1996, pp. 387–401. https://doi.org/10.1016/S0263-8223(96)00052-9.

12.

Girão Coelho

A. M.

, and Mottram

J. T.

. A Review of the Behaviour and Analysis of Bolted Connections and Joints in Pultruded Fibre Reinforced Polymers. Journal of Materials and Design, Vol. 74, 2015, pp. 86–107. https://doi.org/10.1016/j.matdes.2015.02.011.

13.

Kelly

Quasi-Static Strength and Fatigue Life of Hybrid (Bonded/Bolted) Composite Single-Lap Joints. Journal of Composite Structures, Vol. 72, No. 1, 2006, pp. 119–129. https://doi.org/10.1016/j.compstruct.2004.11.002.

14.

, and Mallick

P. K.

. Fatigue of Hybrid (Adhesive/Bolted) Joints in SRIM Composites. International Journal of Adhesion and Adhesives, Vol. 21, No. 2, 2001, pp. 145–159. https://doi.org/10.1016/S0143-7496(00)00047-6.

15.

Nguyen

, and Mutsuyoshi

. Structural Behavior of Double-lap Joints of Steel Splice Plates Bolted/Bonded to Pultruded Hybrid CFRP/GFRP Laminates. Journal of Construction and Building Materials, Vol. 30, 2012, pp. 347–359. https://doi.org/10.1016/j.conbuildmat.2011.12.001.

16.

Mutsuyoshi

, Nguyen

, Zatar

, and Ishihama

. Flexural Behavior of Pultruded Hybrid Fiber-Reinforced Polymer I-Beams with Bonded-and-Bolted Splice Joints. Transportation Research Record: Journal of the Transportation Research Board, No. 2592, 2016, pp. 45–55. http://dx.doi.org/10.3141/2592-06.

17.

Hart-Smith

L. J.

Design and Empirical Analysis of Bolted or Riveted Joints. In Joining Fibre-Reinforced Plastics ( Matthews

F. L.

, ed.), Springer, Netherlands, 1987, pp. 227–269.

18.

Hai

N. D.

Structural Performance of Hybrid FRP Composite Beams. PhD dissertation. Saitama University, Saitama City, Japan, 2010.