Infrared microspectroscopy is used to determine the solubility limits of a UV-curable polymer-dispersed liquid crystal (PDLC) system comprised of a low-molecular-weight liquid crystal (E7) and a photocurable monomer (NOA65). The LC is allowed to diffuse into the monomer by the contact method, and then the sample is subjected to curing. The morphology of the system after polymerizaton exhibits several distinct spatial regions, and the associated concentration gradients are measured. At an irradiation temperature of 30 °C, the concentration of LC in the matrix is found to be 27 ± 3%, and at a temperature of 100 °C, it is 65 ± 3%.
DoaneJ. W.VazN. A. and ZumerS, Appl. Phys. Lett.48, 269 (1986).
2.
WestJ. L., in Advances of Liquid Crystal Polymers, WeissR. A. and OberC. K, Eds., ACS Symposium series (American Chemical Society, Washington, D.C., 1990).
3.
SmithG. W., Phys. Rev. Lett.70, 198 (1993).
4.
HumeckiH. J., Practical Guide to Infrared Microspectroscopy (Marcel Dekker, New York, 1995).
5.
MesserschmidtR. G. and HarthcockM. A, Infrared Micro-spectroscopy: Theory and Applications (Marcel Dekker, New York, 1988).
6.
ChallaS. R.WangS. Q. and KoenigJ. L, Appl. Spectrosc., paper submitted for publication.
7.
SmithG. W., Mol. Cryst. Liq. Cryst.196, 89 (1991).
8.
ChallaS. R.WangS. Q. and KoenigJ. L, Appl. Spectrosc., paper submitted for publication.
9.
KoeflerL. and KoeflerA, Thermomikromethoden (Verlag Chemie, Weinheim, 1954).
10.
SigaudG.AchardM. F.HardouinF.MauzacM.RichardH. and GasparouxH, Macromolecules20, 578 (1987).
11.
SigaudG.AchardM. F.HardouinF. and GasparouxH, Molec. Cryst. Liq. Cryst.155, 443 (1988).
12.
SigaudG.AchardM. F.HardouinF.CoulonC.RichardH. and MauzacM, Macromolecules23, 5020 (1990).
13.
ChenFu-Lung and JamiesonA. M, Liq. Cryst.15, 171 (1993).
14.
LovingerA. J.AmundsonK. R. and DavisD. D, Chem. Mater.6, 1726 (1994).
15.
KyuT. and LeeJ, Technical Reports of ALCOM Symposium, Vol. VII (1995), p. 30.