Uni-directional torsion fatigue tests were carried out on heat-treated En 36A (nickel-chromium) alloy steel which had been given various surface treatments. Recarburization raised fatigue strength relative to the scaled and decarburized condition by 160 per cent. Pre-strained, polished or shot-peened surfaces produced increases in strength ranging from 16 to 60 per cent. The effects of hardening and residual stress are discussed.
Get full access to this article
View all access options for this article.
References
1.
WoodvineJ. G. R.‘The behaviour of case-hardened parts under fatigue stress’, Carnegie Schol. Mem.192413, 197.
2.
MooreH. F.KommersJ. B.The fatigue of metals1927, 160 (McGraw-Hill Book Co., New York).
3.
WiegandH.ScheinhorstR.‘Einfluss der einsatzhärtung auf die biege- und verdrehwechselfestigkeit von glatten und quergebohrten probestäben’, Arch. Eisenhüttenzv.193912, 445.
4.
WatkinsonJ.‘Effects of carbon restoration on fatigue strength of decarburized steel surfaces’, Coil Spring J.195437, 5.
5.
ColemanW. S.SimpsonM.‘Residual stresses in carburized steels’, Fatigue durability of carburized steel1957, 47 (American Society of Metals, Cleveland, Ohio). Roberts, J. G. and Mattson, R. L. ‘Fatigue durability of carburized steels’, ibid., 68.
6.
WatkinsonJ.‘The influence of some surface factors on the torsional fatigue strength of spring steels’, Proc. Int. Conf. Fatigue of Metals1956, 445 (Instn Mech. Engrs, London).
SigwartH.‘Influence of residual stresses on the fatigue limit’, Proc. Int. Conf. Fatigue of Metals1956, 272 (Instn Mech. Engrs, London).
9.
UedaT.‘On the investigation of internal stress in the case- hardened steel bar’, Tech. Rep. Osaka Univ., Japan19533, 21.
10.
BurnsD. J.1961‘Fatigue under triaxial stress’, Ph.D. Thesis, University of Bristol.
11.
FrithP. H.‘Fatigue tests on crankshaft steels’, J. Iron St. Inst.1948159 (No. 2), 385.
12.
LoveR. J.‘The influence of surface conditions on the fatigue strength of steel’, Properties of metallic surfaces Inst. Metals Monogr. and Rep. Series No. 13, 174, 176 (Table 4).
13.
FinnernB.‘Einfluss der einsatzhärtung auf die wechselfestigkeit’, Industrieblatt1957 (No. 1), (Beilage härtereitechnik u. wärmebehandlung) HT 1; and Maschinenschaden 1957 (No. 7/8), 114.
FinnernB.‘Badnitrieren (weichnitrieren)—ein verfahren zur erhöhung der verschleiss- und wechselfestigkeit von bauteilen’, Maschinenschaden1959 (No. 7/8), 101.
16.
BruggerH.KrausG.‘Einfluss der zähigkeit auf die zeit- und dauerfestigkeit einsatzgehärteter teile’, and ‘Einfluss der zähigkeit auf das verhalten von einsatzstählen’, Arch. Eisenhüttenw.196132 (No. 9), 627 and (No. 8), 529.
17.
TauscherH.StecherE.‘Das verhalten der einsatzstähle bei dauerschwingbeanspruchung’, Maschinenbautech.196211 (No. 1), 37.