The Causes of Femoral Head Roughening in Explanted Charnley Hip Prostheses

Abstract

The effect of particles of first, acrylic bone cement containing either barium sulphate or zirconium dioxide as X-ray contrast media, and secondly, particles of fresh cortical bone, on a surgical grade stainless steel surface against which polyethylene was rubbing, has been investigated. It was found that under physiological loads, particles of acrylic cement which have been embedded in the polyethylene bearing surface caused severe scratching of the stainless steel. Some scratches were found to have pronounced lips similar to those observed on the femoral heads of explanted Charnley hip prostheses. Cortical bone produced only slight damage to the stainless steel. In the case of the acrylic cements, the abrasive constituent was isolated and found to be clusters of particles of the X-ray contrast medium. Particles of acrylic cement are frequently observed embedded in the wear surfaces of explanated Charnley acetabular cups and these particles have also been found to contain clusters of X-ray contrast medium particles. It is therefore concluded that the damage to implanted stainless steel prostheses is predominantly caused by the X-ray contrast medium in the acrylic cement.

Get full access to this article

View all access options for this article.

References

Atkinson

J. R.

Dowson

Isaac

G. H.

Wroblewski

B. M.

(1985a) Laboratory wear tests and clinical observations of the penetration of femoral heads into acetabular cups in total replacement hip joints. Part II: A microscopical study of the surfaces of Charnley polyethylene acetabular sockets, Wear, 217–224.

Atkinson

J. R.

Dowson

Isaac

G. H.

Wroblewski

B. M.

(1985b) Laboratory wear tests and clinical observations of the penetration of femoral heads into acetabular cups in total replacement hip joints. Part III: Measurement of internal volume changes in explanted Charnley sockets after 2–16 years in vivo, and the determination of wear factors, Wear, 225–244.

Dowson

El Hady Diab

M. M.

Gillis

B. J.

Atkinson

J. R.

(1984) The influence of counterface topography on the wear of ultra high molecular weight polyethylene under wet or dry conditions, Proceedings of the International Symposium on Polymer Wear and Its Control, American Chemical Society, New York, pp. 226–232.

Dumbleton

J. H.

(1977) Elements of hip joint prosthesis reliability, J. Med. Engng Techn, 1(6), 341–346.

Griffith

M. J.

Seidenstein

Williams

Charnley

(1978) Socket wear in Charnley low friction arthroplasty of the hip, Clin. Orthop., 137, 37–47.

Hirsch

(1974) Clinical problems in total hip replacement, J. Biomed. Mater. Res. Symp., 5(2), 227–244.

Isaac

G. H.

Atkinson

J. R.

Dowson

Wroblewski

B. M.

(1986a) The role of cement in the long term performance and premature failure of Charnley low friction arthroplastics, Engng Med., 15, 19–22.

Isaac

G. H.

Atkinson

J. R.

Dowson

Wroblewski

B. M.

(1986b) The role played by the acrylic cement in determining the penetration rate of the femoral heads in the PE-sockets of Charnley hip prostheses, accepted for publication in the Proceedings of the UHMWPE as a Biomaterial Symposium, Gottingen.

Nairn

(1985) Private communication.

10.

Rostoker

Chao

E. Y. S.

Galante

J. O.

(1978) The appearances of wear on polyethylene – a comparison of in vivo and in vitro wear surfaces, J. Biomed. Mater. Res., 12, 317–335.

11.

Seedhom

B. B.

Wallbridge

N. C.

(1985) Walking activities and wear of prostheses, Ann. Rheum. Dis, 44, 838–843.

12.

Swanson

S. A. V.

(1978) The state of the art in joint replacement. Part III: Results, problems, and trends, J. Med. Engng Techn, 2(1), 16–20.

13.

Willert

H.-G.

Semelitsch

(1977) Reactions of the articular capsule to wear products of artificial joint prostheses, J. Biomed. Mater. Res., 11, 157–164.

14.

Wroblewski

B. M.

(1985) Direction and rate of socket wear in Charnley low friction arthroplasty, J. Bone Jt Surg., 67-B, 757–761.