The degradation of Co-Cr-Mo ASTM F75-92 hip implants after a harvesting period of 8 1/2 months in sheep was investigated. Hip prostheses and tissue samples were obtained from a medical study involving total hip arthroplasty of the cemented type in 12 sheep. Upon euthanasia, the explants were retrieved for analyses of the surfaces and evidence of degradation, while tissue samples from the interface regions were harvested for chemical analysis and evidence of Co, Cr, and Mo contents. Clear evidence of wear and corrosion was detected. Results also indicated that the modes of metal transport through the poly(methyl methacrylate) bone cement play an important role as the surface degradation mechanisms of the metal. The results are being discussed in terms of electrochemical and triboelectrochemical behaviour of the Co-Cr-Mo alloy.
WilliamsD. F.The properties and clinical uses of cobalt-chromium alloys In Biocompatibility of clinical implant materials (Ed. WilliamsD. F.), Vol. 1, 1981, pp. 96–126 (CRC Press, Boca Raton, Florida).
2.
FrakerA. C.Corrosion of metallic implants and prosthetic devices In Corrosion—metals handbook (Ed. KorbL. J.), Vol. 13, 9th edition, 1987, pp. 1324–1335 (ASM International, Metals Park, Ohio).
3.
CrookP.Corrosion of cobalt-base alloys In Corrosion—metals handbook (Ed. KorbL. J.), Vol. 13, 9th edition, 1987, pp. 658–668 (ASM International, Metals Park, Ohio).
4.
BundyK. J.Corrosion and other electrochemical aspects of biomaterialsCrit. Rev. Biomed. Engng, 1994, 22, 139–251.
5.
ZitterH.PlenkH.JrThe electrochemical behavior of metallic implant materials as an indicator of their biocompatibilityJ. Biomed Mater. Res., 1987, 21, 881–896.
6.
KrugerJ.Fundamental aspects of the corrosion of metallic implants In Corrosion and degradation of implant materials, ASM STP 684 (Eds SyrrettB. C.AcharyaA.), 1979, pp. 107–127 (ASTM International, Philadelphia, Pennsylvania).
7.
SüryP.Corrosion behaviour of cast and forged implant materials for artificial joints, particularly with respect to compound designCorros. Sci., 1977, 17, 155–169.
8.
SüryP.SemlitschM.Corrosion behaviour of cast and forged cobalt-based alloys for double-alloy joint endoprosthesesJ. Biomed. Mater. Res., 1977, 12, 723–741.
9.
GoldbergJ. R.BuckleyC. A.JacobsJ. J.GilbertJ. L.Corrosion testing of modular hip implants In Modularity of orthopedic implants (Eds MarloweD. E.ParrJ. E.MayorM. B.), ASTM STP 1301, 1997, pp. 157–176 (ASTM International, Philadelphia, Pennsylvania).
10.
RostokerW.PretzelC. W.Couple corrosion among alloys for skeletal prosthesesJ. Biomed. Mater. Res., 1974, 8, 407–419.
11.
Szklarska-SmialowskaZ.Pitting corrosion of metals, 1986 (National Association of Corrosion Engineers, Houston, Texas).
12.
GoldbergJ. R.GilbertJ. L.Electrochemical response of CoCrMo to high speed fracture of its metal oxide using an electrochemical scratch test methodJ. Biomed. Mater. Res., 1997, 37, 421–431.
13.
HallR. M.UnsworthA.Friction in hip prosthesesBiomaterials, 1997, 18, 1017–1026.
JemmelyP.MischlerS.LandoltD.Electrochemical modelling of passivation phenomena in tribocorrosionWear, 2000, 237, 63–76.
16.
MischlerS.DebaudS.LandoltD.Wear accelerated corrosion of passive metals in tribocorrosion systemsJ. Electrochem. Soc., 1998, 145, 750–758.
17.
KovacsP.DavidsonJ. A.DaigleK.Correlation between the metal ion concentration and the fretting waer volume of orthopaedic implant metals In Particulate debris from medical implants: mechanisms of formation and biological consequences, ASTM STP 1144 (Ed. St JohnK. R.), 1992, pp. 160–176 (ASTM, Philadelphia, Pennsylvania).
18.
BlackJ.Systemic effects of biomaterialsBiomaterials, 1984, 5, 11–18.
19.
TrinidadeM. C. D.LindM.SunD.SchurmanD. J.GoodmanS. B.SmithR. L.In vitro reaction to orthopaedic biomaterials by macrophages and lymphocytes isolated from patients undergoing revision surgeryBiomaterials, 2000, 22, 253–259.
20.
HallabN. J.MikecaK.JacobsJ. J.A triple assay technique for the evaluation of metal induced, delayed-type hypersensitivity responses in patients with or receiving total joint arthroplastyJ. Biomed. Mater. Res., 2000, 53, 480–489.
21.
YangJ.MerrittK.Detection of antibodies against corrosion products in patients after Co-Cr total joint replacementsJ. Biomed. Mater. Res., 1994, 28, 1249–1258.
22.
TomásH.CarvalhoG. S.FernandesM. H.FreireA. P.AbrantesL. M.Effects of Co-Cr corrosion products and corresponding separate metal ions on human osteoblast-like cell culturesJ. Mater. Sci. Mater. Medicine, 1996, 7, 291–296.
23.
HowieD. W.RogersS. D.McGeeM. A.HaynesD. R.Biologic effects of cobalt chrome in cell and animal modelsClin. Orthop. Related Res., 1996, 329, Suppl., S217-S232.
24.
SavarinoL.GranchiD.CiapettiG.SteaS.DonatiM. E.ZinghiG.FontanesiG.RotiniR.MontanaroL.Effects of metal ions on white blood cells of patients with failed total joint arthroplastiesJ. Biomed. Mater. Res., 1999, 47, 543–550.
25.
LeeS. H.BrennanF. R.JacobsJ. J.UrbanR. M.RagasaD. R.GiantT. T.Human monocyte/macrophage response to cobalt-chromium corrosion products and titanium particles in patients with total joint replacementsJ. Orthop. Res., 1997, 5, 40–49.
26.
AspenbergP.Van der VisH.Migration, particles, and fluid pressure. A discussion of causes of prosthetic looseningClin. Orthop. Related Res., 1998, 352, 75–80.
27.
BlumenthalN. C.CosmaV.JaffeW.StuchinS.A new technique for quantitation of metal particulates and metal reaction products in tissues near implantsJ. Appl. Biomaterials, 1994, 5 (3), 191–193.
28.
CookS. D.BarrackR. L.BaffesG. C.ClemowA. J.SerekianP.DongN.KesterM. A.Wear and corrosion of modular interfaces in total hip replacementsClin. Orthop. Related Res., 1994, 298, 80–88.
29.
HukO. L.BansalM.BettsF.RimnacC. M.LiebermanJ. R.HuoM. H.SalvatiE. A.Polyethylene and metal debris generated by non-articulating surfaces of modular acetabular componentsJ. Bone Jt Surg., 1994, 76B (4), 568–574.
30.
SchmalzriedT. P.KwongL. M.JastyM.SelacekR. C.HaireT. C.O'ConnorD. O.BragdonC. R.KaboJ. M.MalcolmA. J.PathM. R. C.HarrisW. H.The mechanism of loosening of cemented acetabular components in total hip arthroplasty. Analysis of specimens retrieved at autopsyClin. Orthop. Related Res., 1992, 274, 60–78.
31.
UrbanR. M.JacobsJ. J.GilbertJ. L.GalanteJ. O.Migration of corrosion products from modular hip prostheses. Particle microanalysis and histopathological findingsJ. Bone Jt Surg., 1994, 76A (9), 1345–1359.
32.
ThornhillT. S.OzunaR. M.ShortkroffS.KellerK.SledgeC. B.SpectorM.Bio-chemical and histological evaluation of the synovial-like tissue around failed (loose) total joint replacement prostheses in human subjects and a canine modelBiomaterials, 1990, 11, 69–72.
33.
SavioJ. A.IIIOvercampL. M.BlackJ.Size and shape of biomaterial wear debrisClin. Mater., 1994, 15, 101–147.
34.
El-WarrakA. O.OlmsteadM. L.von RechenbergB.AuerJ. A.A review of aseptic loosening in total hip arthroplastyVet. Comp. Orthop. Traumatology, 2002, 14 (3), 115–124.
35.
GoldringS. R.SchillerA. L.RoelkeM.RourkeC. M.O'NeilD. A.HarrisW. H.The synovial-like membrane at the bone-cement interface in loose total hip replacements and its proposed role in bone lysisJ. Bone Jt Surg., 1983, 65A, 575–584.
36.
JohansonN. A.BulloughP. G.WilsonP. D.JrSalvatiE. A.RanawatC. S.The microscopic anatomy of the bone-cement interface in failed total hip arthroplastiesClin. Orthop. Related Res., 1987, 218, 643–648.
37.
XuJ. W.KonttinenY. T.LassusJ.NatahS.CeponisA.SolovievaS.Tumor necrosis factor-alpha (TNF-alpha) in loosening of total hip replacement (THR)Clin. Expl. Rheumatology, 1996, 14, 643–648.
38.
HorowitzS. M.PurdonM. A.Mechanisms of cellular recruitment in aseptic loosening of prosthetic joint implantsCalcified Tissue Int., 1995, 57, 301–305.
39.
JiranekW. A.MachandoM.JastyM.JevsevarD.WolfeH. J.GoldringS. R.Production of cytokins around loosened cemented acetabular components; analysis with immunohistochemical techniques and in situ hybridisationJ. Bone Jt Surg., 1993, 75A, 863–879.
40.
GoodmanS. B.HuieP.SongY.SchurmanD.MaloneyW.WoolsonS.Cellular profile and cytokine production at prosthetic interfaces; Study of tissues retrieved from revised hip and knee replacementsJ. Bone Jt Surg., 1998, 80B, 531–539.
41.
HukkanenM.CorbettS. A.PlattsL. A.KonttinenY. T.SantavirtaS.HughesS. P.Nitric oxide in local host reaction to total hip replacementClin. Orthop. Related Res., 1998, 352, 53–65.
42.
GranchiD.CiapettiG.SteaS.SavarinoL.FilippiniF.SudaneseA.ZinghiG.MontanaroL.Cytokine release in mononuclear cells of patients with Co-Cr hip prosthesisBiomaterials, 1999, 20 (12), 1079–1086.
43.
KadoyaY.KobayashiA.OhashiH.Wear and osteolysis in total joint replacementsActa Orthop. Scand., 1998, 278, Suppl., 1–16.
44.
KarrholmJ.BorssenB.LowenhielmG.SnorrasonF.Does early micromotion of femoral stem prostheses matter? 4–7-year stereoradiographic follow-up of 84 cemented prosthesesJ. Bone Jt Surg., 1994, 76B, 912–917.
45.
OlmsteadM. L.Canine cemented total hip replacements: State of the artJ. Small Anim. Practice, 1995, 36 (9), 395–399.
46.
El-WarrakA. O.OlmsteadM.ApeltD.DeissF.NoetzliH.ZlinskyK.HilbeM.Bertschar-WolfsbergerR.JohnsonA. L.AuerJ.Von RechenbergB.An animal model for interface tissue formation in cemented hip replacementsVet. Surg., 2004, 33 (5), 495–504.
47.
LewisG.MdlasiS.Correlation between impact strength and fracture toughness of PMMA-based bone cementsBiomaterials, 2000, 21, 775–781.
48.
OhashiK. L.DauskardtR. H.Effects of fatigue loading and PMMA precoating on the adhesion and subcritical debonding of prosthetic-PMMA interfacesJ. Biomed. Mater. Res., 2000, 51, 172–183.
49.
DowdJ. E.SchwendemanL. J.MacaulayW.DoyleJ. S.ShanbhagA. S.WilsonS.Aseptic loosening in uncemented total hip arthroplasty in a canine modelClin. Orthop. Related Res., 1995, 319, 106–121.
50.
BrunsD.OlmsteadM. L.LitskyA.Technique and results for total hip replacement in sheep: An experimental modelVet. Comp. Orthop. Traumatology, 1996, 9, 158–164.
51.
Swiss Federal Act on Animal Protection, 9 March 1978, and Swiss Animal Protection Ordinance, 27 May1981.
52.
ChauvyP. F.MadoreC.LandoltD.Variable length scale analysis of surface topography: Characterization of titanium surfaces for biomedical applicationsSurf. Coatings Technol., 1998, 110, 48–56.
53.
LiY.-S.WangK.HeP.HuangB. X.KovacsP.Surface-enhanced Raman spectroelectrochemical studies of corrosion films on implant Co-Cr-Mo alloy in biosimulating solutionsJ. Raman Spectrosc., 1999, 30, 97–103.
54.
HodgsonA. W. E.KurzS.VirtanenS.FervelV.OlssonC. O. A.MischlerS.Passive and transpassive behaviour of CoCrMo in simulated biological solutionsElectrochimica Acta, 2004, 49, 2167–2178.
55.
PourbaixM.Atlas d'équilibres électrochimique à 25°C, 1963 (Gauthier-Villars, Paris).
56.
SchafferA. W.PilgerA.EngelhardtC.ZweymuellerK.RuedigerH. W.Increased blood cobalt and chromium after hip replacementJ. Toxic. Clin. Toxic., 1999, 37, 839–844.
57.
BlackJ.MaitinE. C.GelmanH.MorrisD. M.Serum concentrations of chromium, cobalt and nickel after total hip replacement: A six month studyBiomaterials, 1983, 4, 160–164.
58.
MerrittK.BrownS. A.Distribution of cobalt-chromium wear and corrosion products and biologic reactionsClin. Orthop. Related Res., 1996, 329, Suppl., S233-S243.
59.
CzichosH.Tribology — a system approach to the science and technology of friction, lubrication and wear, 1978 (Elsevier, Amsterdam).