Abstract
Abstract
Early failure of knee replacements is thought to be due to the combination of sterilization by gamma irradiation in air and the high cyclic stresses that they endure during use. Such failures are shown through delamination and permanent deformation of the ultra-high molecular weight polyethylene (UHMWPE) component.
This study investigated whether gas plasma sterilization, as an alternative to gamma irradiation in air, would give better performance after ageing in a knee replacement using a metal pin on polymer plate wear test. Fourier transform infrared (FTIR) analysis was performed on the components to assess oxidation levels and a finite element stress analysis model is presented to estimate strain at failure in the UHMWPE.
Delamination occurred in the majority of the gamma-irradiated plates but did not occur in any of the gas-plasma-sterilized plates. The FTIR analysis showed that the plates gamma irradiated in air were highly oxidized when compared with the gas-plasma-sterilized plates. Plastic strain at failure was determined for the gamma-irradiated plates and found to be less than 2.4-14 per cent.
Get full access to this article
View all access options for this article.