Study on self-heating metallic powder for the selective laser sintering process

Abstract

Fabricating metallic functional parts directly using the selective laser sintering (SLS) process is a promising technique which is engaging many researchers. Existing problems during direct fabrication of a metallic part using SLS are analysed. To solve the problems, a new self-heating metallic powder material for SLS direct rapid fabrication is developed. This new material can release a controllable amount of heat during its interaction with laser beam energy, resulting in a reduction of the requirement to use laser power during direct sintering of the metallic part, prolonging the time in the metallic liquid phase and improving the strength and precision of the SLS part. A self-propagating high-temperature synthesis (SHS) material is selected as a self-heating component. For this reason, interaction of the SHS material with CO₂ laser beam energy is researched, which proves that CO₂ laser beam energy can instantly ignite the SHS reaction. On the basis of these investigations, the effect of sintering the metallic powder material mixed with SHS material using a CO₂ laser is also researched. The results show that there is an optimal blending ratio of various materials in the new metallic powder material. Under the optimal blending ratio and SLS process parameters, this new metallic powder material can release a large amount of heat and the SHS reaction can be controlled within the laser sintering. This work shows that it is possible for the metallic part to be directly sintered using a small CO₂ laser power (less than 50 W), thus greatly reducing the dimensions, price and running expenditure of an SLS machine and making it suitable for many applications.

Keywords

selective laser sintering (SLS)self-propagating high-temperature synthesis (SHS)igniting time metallic powder material metallic part

References

Munir

Z. A.

The synthesis of high temperature materials by self-propagating combustion methods. Powder Metallurgy Technol., 1988, 1, 1–24.

Xing

Jiang

The development of SHS process and its application prospect in metallurgical industry. Shanghai Metals, 2002, 24 (1), 37–41.

Slocombe

Selective laser sintering of TiC-Al₂O₃ composite with self-propagating high-temperature synthesis. J. Mater. Processing Technol., 2001, 118, 173–178.

Chen

Study on new metal powder materials and their fabricating process for selective laser sintering [D]. Huazhong University of Science and Technology, P.R. China, 2002, p. 2.

Wang

Yuan

Igniting process model and analysis of self-propagating high-temperature synthesis. J. Chin. Ceramic Soc., 1994, 22 (5), 447–452.

Cao

Zheng

Chen

Laser Heating Process, 1995, p. 100 (Huazhong University of Science and Technology Press, Wuhan, P.R. China).

Barlow

J. W.

Beaman

J. J.

Badrinarayan Balasubramanian

A rapid mould-making system: Material properties and design considerations. Rapid Prototyping J., 1996, 2 (3), 4–15.

Gibson

Shi

Material properties and fabrication parameters in selective laser sintering process. Rapid Prototyping J., 1997, 3 (4), 129–136.