A series of tests are reported which support the proposal that fatigue crack growth rates are retarded by crack closure at low values of applied mean stress intensity. In particular, the evidence presented indicates that closure occurs most readily at the specimen's free surfaces. This leads to dramatic changes in crack front profile under certain loading conditions.
Get full access to this article
View all access options for this article.
References
1.
GoodmanJ.Mechanics applied to engineering1899 (Longman, Green and Co., London).
2.
GerberW.‘Bestimmung der zulossigen spannungen in eisen constructionen’, Z. Bayer Arch. Ing. Ver.18746, 101.
3.
RobertsR.ErdoganF.‘The effect of mean stress on fatigue crack propagation in plates under extension and bending’, Trans. Am. Soc. mech. Engrs, J. bas. Engng1967 89, 885.
4.
FormanR. G.KearneyV. E.EngleR. M.‘Numerical analysis of crack propagation in cyclic-loaded structures’, Trans. Am. Soc. mech. Engrs, J. bas. Engng. 459.
5.
PearsonS.‘The effect of mean stress on fatigue crack propagation in half-inch (12.7 mm) thick specimens of aluminium alloys of high and low fracture toughness’, Engng Fract. Mech.19724, 9.
6.
EvansP. R. V.OwenN. B.MccartneyL. N.‘Mean stress effects on fatigue crack growth and failure in a rail steel’, Engng Fract. Mech. 1974 6, 183.
ElberW.‘The significance of fatigue crack closure’, Damage tolerance in aircraft structures A.S.T.M. STP 486 (1971) p. 230.
9.
RiceJ. R.‘Mechanics of crack tip deformation and extension by fatigue’, Fatigue crack propagation A.S.T.M. STP 415 (1967) p. 247.
10.
CrookerT. W.KrauseD. J.SullivanA. M.‘Effects of constant amplitude loading parameters on fatigue crack growth in HY-130 steel’, N.R.L. Memorandum Report 2822 (Naval Research Laboratory, Washington, D.C., U.S.A.).
11.
RichardsC. E.LindleyT. C.‘The influence of stress intensity and microstructure on fatigue crack propagation in ferritic materials’, Engng Fract. Mech.19724, 951.
12.
GriffithsJ. R.MogfordI. L.RichardsC. E.‘The influence of mean stress on fatigue crack propagation in a ferritic weld metal’, Metal Sci. J.19715, 150.
13.
RitchieR. O.KnottJ. F.‘Mechanisms of fatigue crack growth in low alloy steel’, Acta Met.197321, 639.
14.
AdamsN. J. I.‘Fatigue crack closure at positive stresses’, Engng Fract. Mech.19724, 543.
15.
HoC. L.BuckO.MarcusH. L.‘Application of strip model to crack tip resistance and crack closure phenomena’, Progress in flaw growth and fracture toughness testing A.S.T.M. STP 536 (1973) p. 5.
16.
SihT. T.WeiR. P.‘A study of crack closure in fatigue’, Engng Fract. Mech.19746, 19.
17.
LindleyT. C.RichardsC. E.‘The influence of crack closure and plastic zone geometry on fatigue crack propagation’, 5–431/A Int. Conf. Fracture, Munich 1973.
18.
IrvingP. E.RobinsonJ. L.BeeversC. J.‘A study of the effects of mechanical and environmental variables on fatigue crack closure’, Engng Fract. Mech.19757, 619.
19.
PitoniakF. J.GrandtA. F.MontulliL. T.PackmanP. F.‘Fatigue crack retardation and closure in polymethylmethacrylate’, Engng Fract. Mech.1974, 6, 663.
20.
A.S.T.M ‘Standard specification for nickel-chromiummolybdenum alloy steel plates, quenched and tempered for pressure vessels’, A.S.T.M. designation A 543–65, A.S.T.M. Book of Standards (1965) p. 834.
21.
WalkerE. F.MayM. J.‘Compliance functions for various types of test specimen geometry’, B.I.S.R.A. report MG/E/307/67.
22.
B.S.I.‘Procedure for plane strain fracture toughness testing’, British Standard Draft for Development 3 (1971).
23.
BrownW. F.SrawleyJ. E.‘Plane strain crack toughness testing of high strength metallic materials’, A.S.T.M. STP 410 (1969) p. 73.
24.
WadeE. H. R.LeeG. M. C.‘An ultrasonic fatigue crack growth monitor and load controller’, J. Strain Analysis197510, 159.
25.
EisenstadtR.FullerW. D.‘Generation of crack propagation data on notched rotating beam specimens by means of interrupted stressing technique’, Trans. Am. Soc. mech. Engrs, J. bas. Engng197092, 183.