Proposed ductile fracture toughness parameters from tensile tests have been successfully used to determine the post-weld heat treatment temperature for an alloy 800/(9Cr-1Mo) steel dissimilar metal weld joint that is optimum with respect to accelerated aging, which simulates service conditions. This approach proved superior to using microstructural analysis, microhardness profiles, and conventional tensile properties.
Get full access to this article
View all access options for this article.
References
1.
BHADURIA. K., VENKADESANS., RODRIGUEZP., and MUKUNDAP. G.: Int. J. Pressure Vessels Piping, 1994, 58, 251–265.
2.
BHADURIA. K., GOWRISANKARI., SEETHARAMANV., VENKADESANS., and RODRIGUEZR: Mater. Sci. Technol.,1988, 4, 1020–1029.
3.
BHADURIA. K.: ‘Metallurgical studies for the development, characterization, and evaluation of an improved transition metal joint for steam generators’, PhD thesis, Indian Institute of Technology, Kharagpur, India, 1990.
4.
BHADURIA. K., SEETHARAMANV., and VENKADESANS.: Z. Metallkd.,1989, 80, 630–634.
5.
BHADURIA. K. and VENKADESANS.: Z. Metallkd.,1991, 82, 135–138.
6.
BHADURIA. K., VENKADESANS., RODRIGUEZP., and MUKUNDAP. G.: Mater. Sci. Technol.,1991, 7, 1051–1056.
7.
BHADURIA. K., VENKADESANS., RODRIGUEZP., and MUKUNDAP. G.: Mater. High Temp.,1992, 10, 45–50.
8.
BHADURIA. K., SRINIVASANG., GILLT. P. S., and MANNANS. L.: Int. J. Pressure Vessels Piping, 1995, 61, 25–33.
9.
TURNELLA. J. and MARSHP. G.: Met. Constr.,1985, 17, 237–241.
10.
RAYS. K., BHADURIA. K., and RODRIGUEZP.: J. Nucl. Mater.,1993, 200, 70–77.
11.
BHADURIA. K., RAYS. K., and RODRIGUEZP.; Mater. Sci. Technol.,1993, 9, 1133-1136.
12.
RODRIGUEZP.: Trans. Indian Inst. Met.,1993, 46, 267–296.
13.
RAYS. K., BHADURIA. K., and RODRIGUEZR: Int. J. Pressure Vessels Piping, 1994, 57, 331–333.
14.
RAYS. K., BHADURIA. K., and RODRIGUEZP.: Trans. Indian Inst. Met.,1993, 46, 71–75.