Effects of pearlite formation on mechanical properties of austempered ductile iron

Abstract

Mechanical property measurements are described for a ductile iron alloyed with Mn, Mo, and Cu in the fully austempered condition, andfor irons with various amounts of pearlite introduced by isothermal transformation at 550°C after austenitising at 920°C for 120 min and before austempering at 370°C for 60 min. The ultimate tensile strength, 0·2% proof strength, elongation, impact energy, and hardness all decrease as the amount of pearlite in the structure increases. A smaller amount of pearlite can be tolerated in the alloyed iron compared with an unalloyed iron before itfails to satisfy the standard.