Solid state phase transformations in Ti–Al–C and Ti–Al–Nb–C alloys

Abstract

Results are reported of an investigation of solid state transformations in a series of α₂ based alloys having an aluminium content of 26 at.-% with carbon up to 3 at.-%; two α₂ basedquaternary Ti–Al–Nb–C alloys with 5 and 12 at.-%Nb and 3 at.-%C were also studied. Ordering occurs in the ternary Ti–Al–C alloys and also in the 23Al–5Nb–3C alloy on quenchingfrom 1250°C. Additional carbide precipitation was not observed in the ternary Ti–Al–C alloys on reheating to 750°C. Additions of niobium resulted in the presence of the β phase at 1050°C in the 5%Nb alloy and at 1050 and 750°C in the 12%Nb alloy. In the quaternary Ti–Al–Nb–C alloys, (Ti, Nb)₃AlC was found to be the primary phase and was present in the microstructure over the temperature range studied. In the 21Al–12Nb–3C alloy, the ordered β phase transformed to α″₂ martensite on quenching from 1250;amp;#x00B0;C.