The formation and growth of voids on the grain boundaries of a Nimonic 105 superalloy subjected to high temperature and stress has been followed using small-angle neutron scattering. The size of the voids increases with treatment time and is well correlated with the creep. The volume and surface fractions of the voids are evaluated.
MST/140
Get full access to this article
View all access options for this article.
References
1.
DAVIESP. W., DENNISONJ. P., and SIDEYD.: J. Inst. Met.,1973, 101, 153–161.
2.
BURTH., DENNISONJ. P., and WILSHIREB.: Met. Sci.,1979, 13, 295–300.
3.
DYSONB. F. and McLEANM.: Acta Metall., 1983, 31, 17–37.
4.
MILLERR. J. R., MESSOLORASS., STEWARTR. J., and KOSTORZG.: J. Appl. Crystallogr.,1978, 11, 583–588.
5.
PIZZIP. and WALTHERH.: J. Appl. Crystallogr.,1974, 7, 230–330.
6.
SAEGUSAT., WEERTMANJ. R., COHENJ. B., and ROTHM.: J. Appl. Crystallogr.,1978, 11, 602–604.
7.
PAGER., WEERTMANJ. R., and ROTHM.: Scr. Metall.,1980, 14, 773–777.
8.
PAGER., WEERTMANJ. R., and ROTHM.: Acta Metall., 1982, 30, 1357–1366.
9.
YOOM. H., OGLEJ. C., BORIEB. S., LEEE. M., and HENDRICKSR. W.: Acta Metall., 1982, 30, 1733–1742.
10.
ARGONA. S., CHENI.-W., and [AUC. C.: in ‘Creep—fatigue—environment interactions’, (ed. DellouxR. M. and StoloffN. S.), 46; 1980, Warrendale, Pa, Metallurgical Society of AIME.
11.
COCKSA. C. F. and ASHBYM. F.: Frog. Mater. Sci., 1982, 27, 189–244.
12.
GOODSS. H. and BROWNI. H.: Acta Metall., 1979, 27, 1–15.
13.
HAYHURSTD. R., TRAMPCZYNSKIW. A., and LECKIEF. A.: Acta Metall., 1982, 31, 1537–1542.
14.
SHAMT.-L. and NEEDLEMANA.: Acta Metall., 1983, 31, 919–926.
15.
H M.. YO0 and H. TRINKAUS: Metall. Trans.,1983, 14A, 547–561.
16.
NIXW. D., YUK. S., and WANGJ. s.: Metall. Trans.,1983, 14A, 563–570.