Constitution of Ni 3 Al–Ni 3 Mo–Ni 3 W section of Ni–Al–Mo–W system

Abstract

The isothermal section of the Ni–Al–Mo–W system has been studied at 75 at.-%Ni at temperatures of 1523 and 1273 K. Constitutional data have been determined using electron probe microanalysis, X-ray diffraction, and microscopical examination. The alloys studied lay in the range 12·5–15 at.-%Al, 2·5–7·5 at.-%Mo, and 2·5–7·5 at.-% W. The phases present at 1523 K were γ, γ′, and α (based on the Mo–W continuous series of solid solutions); at 1273 K, NiMo(δ′) was also encountered. The γ/γ′ mismatch values lay in the range −0·03 to −0·75%. In the as-solidified state, the alloys consisted predominantly of γ-phase containing γ′-precipitates formed in the solid state.