A technique is presented for relating the size and spatial distributions of inclusions on fracture faces produced by microvoid coalescence with those in the bulk material by considering the volumes from which inclusions of different sizes taking part in the fracture are drawn. It is demonstrated that in the simplest case, inclusions are drawn into the fracture from a distance proportional to their diameter.
RUSSJ. C.: in discussion, ASTM STP453, 1969, p. 30.
3.
SprrzigW. A.: ‘Correlations between fractographic features and plane-strain fracture toughness in an ultrahigh-strength steel’, ibid., p. 90.
4.
PASSOJAD. E. and HILLD. C.: Metall. Trans., 1974, 5, (8), 1851.
5.
HILLD. C. and PASSOJAD. E.: Weld. J., 1974, 53, (11), 481s.
6.
BROEKD.: Eng. Fracture Mech., 1973, 5, (1), 55.
7.
IIANNERZN. E. and J.F.. LOWERY: Metal Construction, 1975, 7, (1), 21.
8.
L.L.—J. CHIN: Weld. J., 1969, 48, (7), 290s.
9.
PASSOJAD. E. and HILLD. C.: ‘Quantitative relations between microstructure and fracture surface features in mild steel’, Symposium on Fractography, ASTM 78th Annual Meeting, Montreal, June 1975.
10.
ASHBYM. F. and EBELINGR.: Trans. Met. Soc. AIME, 1966, 236, 1396.
11.
SCHEILF.: Z. anorg. Chem., 1931, 201, 259.
12.
STEELA. C.: Welding Research Internat., 1971, 1, (3).
13.
WIDGERYD. J.: PhD Thesis, Univ. Cambridge, 1974.
14.
KOTTLERF.: J. Franklin Inst., 1950, 250, (10), 339 and (11), 419.
15.
KENDALLH. G. and STUARTA.: ‘The advanced theory of statistics’,Vol. 2, 168. 1960: London(Charles Griffin).
16.
GURLANDJ. and PLATEAUJ.: Trans. ASM, 1963, 56, 442.