Abstract
The mechanical properties of several austenitic steels containing γ′ precipitate have been studied. A large increase in proof stress occurs during ageing as a result of particle growth at almost constant volume fraction of precipitate. Up to the peak proof stress, dislocations are paired owing to the high antiphase-domain boundary energy and this, in conjunction with Friedel's theory relating effective particle spacing to particle strength, satisfactorily accounts for the increasing proof stress. The value of the antiphase-domain boundary energy is higher at higher Ti/Al ratios. Misfits between 0 and 0·4% have no influence on yield strength. Large particles are by-passed by Orowan looping irrespective of misfit. During the looping process a transition from paired to single dislocations occurs that reduces the fall in stress with increasing particle size. Stable Orowan loops give rise to a back-stress that is detectable at low strains. This causes work-hardening by the Fisher, Hart, and Pry mechanism. Alloys with high Ti/Al ratios show more marked work-hardening associated with more debris in the slip planes. This is apparently a result of the by-passing of particles by cross-slip, which gives rise to complex slip interactions. However, except at very large particle sizes slip continues to be planar.
Get full access to this article
View all access options for this article.