The modification of wood with methylolated melamine formaldehyde resin belongs to the group of impregnation modifications. In the course of this study, Koto sapwood samples were impregnated with methylolated melamine formaldehyde resin solutions in a full cell vacuum pressure process. The samples were cured at a maximum temperature of 120°C for 24 h. To characterise the modification, the solution uptake and weight percent gain of the samples were calculated. The fixation of the melamine as parameter for the degree of curing was examined by C/N analysis. Areal UV-microspectrophotometry scans of ultra-thin transverse sections of an untreated control and samples impregnated with methylolated melamine formaldehyde resin at 240 nm were recorded. Additionally, photometric point measurements with a spot size of 1 μm−2 in the range 230 and 350 nm were conducted. UV-microspectrophotometry was proven as suitable technique for the quantitative analysis of wood modified with methylolated melamine formaldehyde resin.
BollmusS. 2011. Biologische und technologische Eigenschaften von Buchenholz nach einer Modifizierung mit 1,2-dimethylol-4,5-dihydroxyethylenurea (DMDHEU). PhD. Georg-August-University of Göttingen, Göttingen, Germany.
2.
BellmannH. 1955. Über den Einfluss der Tüpfelkapillaren und Micellarinterstizien auf die Mechanik von Imprägniervorgängen mit Lösungen. Mitteilungen der Bundesforschungsanstalt für Forst- und Holzwirtschaft. Haller in Komm, Berlin, Germany.
3.
DevallencourtC, SaiterJM and CapitaineD. 2000. Reactions between melamine formaldehyde resin and cellulose: influence of pH.J. Appl. Polym. Sci., 78(11), pp. 1884–96.
4.
FergusBJ and GoringDAI. 1970a. The distribution of lignin in birch wood determined by ultraviolet microscopy.Holzforschung, 24(4), pp. 118–24.
5.
FergusBJ and GoringDAI. 1970b. The location of guaiacyland syringyl lignins in birch xylem tissue.Holzforschung, 24(4), pp. 113–24.
6.
FrankensteinC, SchmittU and KochG. 2006. Topochemical studies on modified lignin distribution in the xylem of poplar (Populus spp.) after wounding.Ann. Bot., 97(2), pp. 195–204.
7.
GindlW, DessipriE and WimmerR. 2002. Using UV-microscopy to study diffusion of melamine-urea-formaldehyde resin in cell walls of spruce wood.Holzforschung, 56(1), pp. 103–107.
8.
GindlW, Zargar-YaghubiF and WimmerR. 2003. Impregnation of softwood cell walls with melamine-formaldehyde resin.Bioresource Technol., 87(3), pp. 325–30.
9.
HagstrandPO, KlasonC, SvenssonL and LundmarkS. 1999. Rheokinetical behavior of melamine-formaldehyde resins.Polym Eng Sci., 39(10) , pp. 2019–29.
10.
HansmannC, DekaM, WimmerR and GindlW. 2006. Artificial weathering of wood surfaces modified by melamine formaldehyde resins.Holz Roh Werkst., 64(3), pp. 198–203.
11.
Inoue, M., Ogata, S., KAwai, S., Rowell, R. M. and Norimoto, M. 1993.Dimensional stability, mechanical properties, and color changes of a low-molecular-weight melamine formaldehyde resin impregnated wood.Mokuzai Gakkaishi, 39(2), pp. 181–89.
12.
JafféHH and OrchinM. 1962. Theory and application of ultraviolet spectroscopy. New York: John Wiley and Sons.
13.
KleistG and SchmittU. 1999. Evidence of accessory compounds in vessel walls of Sapelli heartwood (Entandrophragma cylindricum) obtained by transmission electron microscopy.Holz Roh Werkst., 57(2), pp. 93–95.
14.
LukowskyD. 1999. Holzschutz mit Melaminharzen. PhD. University of Hamburg, Hamburg, Germany.
15.
MarkovIV. 2006. Crystal growth for beginners: fundamentals of nucleation, crystal growth and epitaxy. London: World Scientific.
16.
MiroyF., EymardP. and PizziA.1995. Wood hardening by methoxyl melamine.Holz Roh Werkst, 53(4), p.276.
17.
PittmanCUet al. 1994. Wood enhancement treatments I. Impregnation of southern yellow pine with melamine-formaldehyde and melamine-ammeline-formaldehyde resins.J Wood Chem Technol, 14(4), pp. 577–603.
18.
RappAO. 1999. Physikalische und biologische Vergütung von Vollholz durch Imprägnierung mit wasserverdünnbaren Harzen. PhD. University of Hamburg, Hamburg, Germany.
19.
RappAO and PeekRD. 1999. Melaminharzimprägniertes sowie mit Wetterschutzlasur oberflächenbehandeltes und unbehandeltes Vollholz während zweijähriger Freilandbewitterung.Holz Roh Werkst, 57(5), pp. 331–39.
20.
RoscaI, GsoelsI, RätzschM and SchmidtH. 2003. Short-duration impregnation of wood with melamine resin. In: Proceedings of the First European Conference on Wood Modification, Ghent, Belgium, April 2003, Ghent University.
21.
SailerM, RappAO and LeithoffH. 2000. Improved resistance of Scots pine and spruce by application of an oil-heat treatment. The International Research Group on Wood Protection, IRG/WP 00-40162.
22.
SintKMet al. 2013. Impregnation of Bombax ceiba and Bombax insigne wood with a N-methylol melamine compound.Wood Sci Technol, 47(1), pp. 43–58.
23.
StammAJ. 1964. Wood and cellulose science. New York: The Ronald Press Company.
24.
WallströmL and LindbergKAH. 2000. The diffusion, size and location of added silver grains in the cell walls of Swedish pine, Pinus sylvestris. Wood Sci Technol, 34(5), pp. 403–15.
25.
WardropAB and DaviesGW. 1961. Morphological factors relating to the penetration of liquids in wood.Holzforschung, 15(5), pp. 129–41.
26.
WepnerF. 2006. Entwicklung eines Modifizierungsverfahrens für Buchenfurniere auf Basis von zyklischen N-Methylol-Verbindungen. PhD. Gerog-August-University Göttingen, Göttingen, Germany.
27.
ZimmerK, LarnøyE and HøiboO. 2012. Assessment of fluid flow paths and distribution in conifers.Wood Research, 57(1), pp. 1–14.