The influence of hexamine formed as byproduct during the UF cure was ignored in the past. However, with the increasing interest on low formaldehyde emission boards, this issue has become more pertinent. Formaldehyde release from hexamine degradation is extensive and could limit the success of the development of low formaldehyde emission adhesives if the conventional latent catalysts remain in use.
In this study, formaldehyde released from recycled wood, hexamine and cured UF resin was assessed. Citric and oxalic acid, in solid form, were used as catalysts for UF resin in the production of particleboard. Mats with solid acids are less susceptible to resin pre-cure than with a latent catalyst. However, they can have higher formaldehyde emissions than latent catalyst. When both catalysts were used, combined with an ultra-low formaldehyde to urea molar ratio resin the internal bond was improved and formaldehyde content was below 4 mg per 100 g of oven dry board.
Anon. 2010. Wood handbook: wood as an engineering material. General Technical Report FPL-GTR-190, Madison, WI: U.S., Forest Products Laboratory. Department of Agriculture, Forest Service, Forest Products Laboratory
2.
BlairA, StewartP, ObergM, GaffeyW, WalrathJ, WardJ, BalesR, KaplanS and CubitD. 1986. Mortality among industrial-workers exposed to formaldehyde.J. National Cancer Inst. 76: 1071–1084.
3.
BoranS, UstaM and GümüşkayaE. 2011. Decreasing formaldehyde emission from medium density fiberboard panels produced by adding different amine compounds to urea formaldehyde resin.Int. J. Adhes. Adhes. 31: 674–678.
CostaN, PereiraJ, FerraJ, CruzP, MoreiraJ, MartinsJ, MagalhãesF, MartinsJ, MendesA and CarvalhoL. 2012b. The role of sucrose in amino polymers synthetized by the strongly acid process.J. Adhes. Sci. Technol. 27(7): 763–774.
6.
CostaN, PereiraJ, MartinsJ, FerraJ, CruzP, MagalhãesF, MendesA and CarvalhoL. 2012c. Alternative to latent catalysts for curing UF resins used in the production of low formaldehyde emission wood-based panels.Int. J. Adhes. Adhes. 33: 56–60.
7.
CostaN, MartinsD, PereiraJ, MartinsJ, FerraJ, CruzP, MendsA, MagalhãesF and CarvalhoL. 2013a. 13C NMR study of presence of uron structures in amino adhesives and relation with wood-based panels performance’.J. Appl. Polym. Sci. 130(6): 4500–4507.
8.
CostaN, AmaralS, AlvimR, NogueiraM, SchwanningerM and RodriguesJ. 2013b. Assessment of resin formulations and determination of the formaldehyde to urea molar ratio by near- and mid-infrared spectroscopy and multivariate data analysis.J. Appl. Polym. Sci. 128(1): 498–508.
9.
CostaN, PereiraJ, FerraJ, CruzP, MartinsJ, MagalhãesF, MendsA and CarvalhoL. 2013c. Scavengers for achieving zero formaldehyde emission on wood-based panels.Wood Sci. Technol. 47(6): 1261–1272.
10.
CostaN, PereiraJ, FerraJ, CruzP, MartinsJ, MagalhãesF, MendesA and CarvalhoL. 2013d. Sodium metabisulphite as a scavenger of air pollutants for wood-based building materials.Int. Wood Prod. J. 4(4): 242–247.
11.
DreyforsJM, JonesSB and SayedY. 1989. Hexamethylenetetramine – a review. Am. Industr.Hygiene Assoc. J. 50: 579–585.
12.
EomY.-G, KimJ.-S, KimS, KimJ.-A and KimH.-J. 2006. Reduction of formaldehyde emission from particleboards by Bio-Scavengers.Mokchae Konghak34: 29–41.
13.
FerraJM, MenaPC, MartinsJ, MendesAM, CostaMRN, MagalhaesFD and CarvalhoLH. 2010. Optimization of the synthesis of urea-formaldehyde resins using response surface methodology.J. Adhes. Sci. Technol. 24: 1455–1472.
14.
FerraJMM, HenriquesA, MendesAM, CostaMRN, CarvalhoLH and MagalhãesFD. 2012. Comparison of UF synthesis by alkaline-acid and strongly acid processes.J. Appl. Polym. Sci. 123: 1764–1772.
15.
GunnellsD and GriffinK. 1998. Catalyst systems. In: Bradfield, J. ed. Resin & Blending Seminar Proceedings, Portland, Oregon and Charlotte, North Carolina. Forest Products Society.
16.
HenriquesA, CruzP, MartinsJ, FerraJM, MagalhãesFD and CarvalhoLH. 2012a. Determination of formaldehyde/urea molar ratio in amino resins by near-infrared spectroscopy.J. Appl. Polym. Sci. 124: 2441–2448.
17.
HenriquesA, FerraJ, CruzP, MartinsJ, MagalhãesFD and CarvalhoL. 2012b. Viscosity determination of amino resins during synthesis using near-infrared spectroscopy.Int. Wood Products J. 3: 64–66.
18.
IARC. 2006. Formaldehyde, 2-Butoxyethanol and 1-tert-Butoxypropan-2-ol. In: Monographs on the Evaluation of Cancinogenic Risck to Humans: Volume 88, World Health Organization – International Agency for Research on Cancer.
19.
KimS, KimHJ, KimHS and LeeHH. 2006. Effect of bio-scavengers on the curing behavior and bonding properties of melamine-formaldehyde resins.Macromol. Mater. Eng. 291: 1027–1034.
20.
KimS. 2009. The reduction of indoor air pollutant from wood-based composite by adding pozzolan for building materials.Constr. Build. Mater. 23: 2319–2323.
21.
LebowPK and WinandyJE. 1999. Verification of a kinetics-based model for long-term effects of fire retardants on bending strength at elevated temperatures.Wood Fiber Sci. 31: 49–61.
22.
LevanSL and WinandyJE. 1990. Effects of fire retardant treatments on wood strength – a review.Wood Fiber Sci. 22: 113–131.
23.
MartinsJ, PereiraJ, PintoB, CoelhoC and CarvalhoL. 2007. Effect of recycled wood on formaldehyde release of particleboard. In: WKI, F ed. COST Action E49 Conference: Measurement and Control of VOC Emission from Wood-Based Panels, Braunschweig, Germany.
24.
MeyerB and BoehmeC. 1997. Formaldehyde emission from solid wood.Forest Products J. 47: 45–48.
25.
PaivaNT, HenriquesA, CruzP, FerraJM, CarvalhoLH and MagalhãesFD. 2012. Production of melamine fortified urea-formaldehyde resins with low formaldehyde emission.J. Appl. Polym. Sci. 124: 2311–2317.
26.
ParkBD, KangEC and ParkJY. 2008. Thermal curing behavior of modified urea-formaldehyde resin adhesives with two formaldehyde scavengers and their influence on adhesion performance.J. Appl. Polym. Sci. 110: 1573–1580.
27.
PizziA. 1983. Wood adhesives: chemistry and technology, Marcel Dekker.
28.
PizziA and MittalKL. 1994. Handbook of adhesive technology. New York: Marcel Dekker.
29.
RoffaelE. 2006. Volatile organic compounds and formaldehyde in nature, wood and wood based panels.Holz als Roh- und Werkstoff64: 144–149.
30.
SchaferM and RoffaelE. 2000. On the formaldehyde release of wood: Holz Als Roh-Und Werkstoff58: 259–264.
31.
ThoemenH. 2010. Wood-based panels – an introduction for specialists. Brunel University Press
32.
WalkerJF. 1944. Formaldehyde. New York: Waverly Press.