ZrB2 based composites containing 10 vol.-% carbon nanotubes (CNTs) are synthesised by spark plasma sintering at temperatures ranging from 1600 to 18008C and at an applied pressure of 25 MPa. The effects of sintering temperature on densification behaviour, microstructural evolutions and mechanical properties are presented. Results indicate that ZrB2-CNT composites fabricated at 16508C have the optimal combination of dense microstructure and properties. The fracture toughness is sensitive to the temperature change and reaches 7.2 MPa m1/2 for the CNT toughened ZrB2 ceramics, which is higher than the measured result for monolithic ZrB2 (3.3 MPa m1/2). The crack deflection and CNT pullout are the dominant toughening mechanisms.
JalalyM., BafghiM. Sh., TamizifarM. and GotorF. J.: ‘Mechanosynthesis of nanocrystalline ZrB2-based powders by mechanically induced self-sustaining reaction method’, Adv. Appl. Ceram., 2013, 112, 383–388. doi: 10.1179/1743676113Y.0000000091
2.
HeR. J., ZhangR. B., ZhuX. L., WeiK., QuZ. L., PeiY. M. and FangD. N.: ‘Improved green strength and green machinability of ZrB2–SiC through gelcasting based on a double gel network’, J. Am. Ceram. Soc., 2014, 97, 2401–2404. doi: 10.1111/jace.13076
3.
WangZ., WuZ. J. and ShiG. D.: ‘Fabrication, mechanical properties and thermal shock resistance of a ZrB2-graphite ceramic’, Int. J. Refract. Met. Hard Mater., 2011, 29, 351–355. doi: 10.1016/j.ijrmhm.2010.12.014
4.
HeR. J., ZhangX. H., HuP., HanW. B. and HongC. Q.: ‘Preparation of YAG gel coated ZrB2–SiC composite prepared by gelcasting and pressureless sintering’, Composites B, 2013, 54B, 307–312. doi: 10.1016/j.compositesb.2013.05.039
5.
WangZ., WuZ. J. and ShiG. D.: ‘Effect of annealing treatment on mechanical properties of a ZrB2–SiC–graphite ceramic’, Mater. Sci. Eng. A, 2011, A528, 2870–2874.
6.
OrlovskayaN., StadelmannR., LugovyM., SubbotinV., SubhashG., NeubertM., AnezirisC. G., GrauleT. and KueblerJ.: ‘Mechanical properties of ZrB2–SiC ceramic composites: room temperature instantaneous behaviour’, Adv. Appl. Ceram., 2013, 112, 9–16. doi: 10.1179/1743676112Y.0000000042
7.
GuoS. Q., NishimuraT., MizuguchiT. and KagawaY.: ‘Mechanical properties of hot-pressed ZrB2–MoSi2–SiC composites’, J. Eur. Ceram. Soc., 2008, 28, 1891–1898. doi: 10.1016/j.jeurceramsoc.2008.01.003
8.
KhanraA. K. and GodkhindiM. M.: ‘Effect of Ni additives on pressureless sintering of SHS ZrB2’, Adv. Appl. Ceram., 2005, 104, 273–276. doi: 10.1179/174367606X69898
9.
WangZ., WangS., ZhangX. H., HuP., HanW. B. and HongC. Q.: ‘Effect of graphite flake on microstructure as well as mechanical properties and thermal shock resistance of ZrB2–SiC matrix ultrahigh temperature ceramics’, J. Alloys Compd, 2009, 484, 390–394. doi: 10.1016/j.jallcom.2009.04.109
10.
ZhangK. and ChoiH. J.: ‘Fabrication and viscoelastic characteristics of amino-functionalized multi-walled carbon nanotube/poly (methyl methacrylate) nanocomposites’, Compos. Struct., 2015, 125, 170–175. doi: 10.1016/j.compstruct.2015.02.023
11.
BianL. and ZhaoH.: ‘Elastic properties of a single-walled carbon nanotube under a thermal environment’, Compos. Struct., 2015, 121, 337–343. doi: 10.1016/j.compstruct.2014.11.032
12.
ChangC. W., TsengJ. M., HorngJ. J. and ShuC. M.: ‘Thermal decomposition of carbon nanotube/Al2O3 powders by DSC testing’, Compos. Sci. Technol., 2008, 68, 2954–2959. doi: 10.1016/j.compscitech.2007.11.011
13.
CorralE. L., WangH., GarayJ., MunirZ. and BarreraE. V.: ‘Effect of single-walled carbon nanotubes on thermal and electrical properties of silicon nitride processed using spark plasma sintering’, J. Eur. Ceram. Soc., 2011, 31, 391–400. doi: 10.1016/j.jeurceramsoc.2010.10.020
14.
FahrenholtzW. G. and HilmasG. E.: ‘Refractory diborides of zirconium and hafnium’, J. Am. Ceram. Soc., 2007, 90, 1347–1364. doi: 10.1111/j.1551-2916.2007.01583.x
15.
ScitiD., SilvestroniL. and NygrenM.: ‘Spark plasma sintering of Zr- and Hf-borides with decreasing amounts of MoSi2 as sintering aid’, J. Eur. Ceram. Soc., 2008, 28, 1287–1296. doi: 10.1016/j.jeurceramsoc.2007.09.043
16.
MizuguchiT., GuoS. Q. and KagawaY.: ‘Transmission electron microscopy characterization of spark plasma sintered ZrB2 ceramic’, Ceram. Int., 2010, 36, 943–946. doi: 10.1016/j.ceramint.2009.10.025
17.
Fine ceramics (advanced ceramics, advanced technical ceramic) – test method for flexural of monolithic ceramics at room temperature, GB/T6569-2006, General Administration of Quality Supervision, Inspection and Quarantine (AQSIQ) & Standardization Administration (SA) of China, 2006.
18.
Fine ceramics (advanced ceramics advanced technical ceramics) – test method for fracture toughness of monolithic ceramics at room temperature by single edge precracked beam (SEPB) method, General Administration of Quality Supervision, Inspection and Quarantine (AQSIQ) & Standardization Administration (SA) of China, 2009.
19.
KalishD., CloughertyE. V. and KrederK.: ‘Strength, fracture mode, and thermal stress resistance of HfB2 and ZrB2’, J. Am. Ceram. Soc., 1969, 52, 30–36. doi: 10.1111/j.1151-2916.1969.tb12655.x
20.
MunirZ. A.: ‘The effect of external electric fields on the nature and properties of materials synthesized by self-propagating combustion’, Mater. Sci. Eng. A, 2000, A287, 125–137. doi: 10.1016/S0921-5093(00)00765-6
21.
MukhopadhyayA., VenkateswaranT. and BasuB.: ‘Spark plasma sintering may lead to phase instability and inferior mechanical properties: a case study with TiB2’, Scr. Mater., 2013, 69, 159–164. doi: 10.1016/j.scriptamat.2013.02.027
22.
WangW. M., FuZ. Y., WangH. and YuanR. Z.: ‘Influence of hot pressing sintering temperature and time on microstructure and mechanical properties of TiB2 ceramics’, J. Eur. Ceram. Soc., 2002, 22, 1045–1049. doi: 10.1016/S0955-2219(01)00424-1