Composites of hydroxyapatite (HA) with 5 wt-% Ti–Fe reinforcing particles were pressureless sintered in vacuum at a temperature range between 950 and 1100°C. It was found that although the decomposition of HA and interaction between HA and Ti occurred, the desirable Ti phase still remained in the composites sintered at all temperatures. The outer Ti shell thickness of the distinctive core–shell Ti–Fe particles was observed to become larger as the sintering temperature increased. It was also found that minor pores appearing near the interface were beneficial to obtain appropriate interfacial bonding between HA matrix and Ti–Fe particles. The composite sintered at 1050°C exhibited superior flexural strength, fracture toughness, and fatigue resistance owing to the remained Ti phase and dense microstructure as well as good interfacial bonding.
BestS. M., PorterA. E., ThianE. S. and HuangJ.: ‘Bioceramics: past, present and for the future’, J. Eur. Ceram. Soc., 2008, 28, (7), 1319–1327.
2.
ZhouH. J. and LeeJ.: ‘Nanaoscale hydroxyapatite particles for bone tissue engineering’, Acta Biomater., 2011, 7, (7), 2769–2781.
3.
HenchL. L.: ‘Bioceramics from concept to clinic’, J. Am. Ceram. Soc., 1991, 74, (7), 1487–1510.
4.
LiJ., FartashB. and HerrnanssonL.: ‘Hydroxyapatite-alumina composites and bone-bonding’, Biomoterials, 1995, 16, (5), 417–422.
5.
DonnersJ. J. J. M., NolteR. J. M. and SommerdijkN. A. J. M.: ‘Dendrimer-based hydroxyapatite composites with remarkable materials properties’, Adv. Mater., 2003, 15, (4), 313–316.
6.
KailasanathanC., SelvakumarN. and NaiduV.: ‘Structure and properties of titania reinforced nano-hydroxyapatite/gelatin bio-composites for bone graft materials’, Ceram. Int., 2012, 38, (1), 571–579.
7.
ChuC., LinP., DongY., XueX., ZhuJ. and YinZ.: ‘Fabrication and characterization of hydroxyapatite reinforced with 20vol% Ti particles for use as hard tissue replacement’, J. Mater. Sci.: Mater. Med., 2002, 13, (10), 985–992.
8.
ThianE. S., LohN. H., KhorK. A. and TorS. B.: ‘Microstructures and mechanical properties of powder injection molded Ti–6Al–4V/HA powder’, Biomaterials, 2002, 23, (14), 2927–2938.
9.
NingC. Q. and ZhouY.: ‘In vitro bioactivity of a biocomposite fabricated from HA and Ti powders by powder metallurgy method’, Biomaterials, 2002, 23, (14), 2909–2915.
10.
WengJ., LiuX. G., ZhangX. D. and JiX. Y.: ‘Thermal decomposition of hydroxyapatite structure induced by titanium and its dioxide’, J. Mater. Sci. Lett., 1994, 13, (3), 159–161.
11.
YangY. Z., KimK. H., AgrawalC. M. and OngJ. L.: ‘Interaction of hydroxyapatite-titanium at elevated temperature in vacuum environment’, Biomaterials, 2004, 25, (15), 2927–2932.
12.
SongN., LiuY., ZhangY., TanY. N. and GroverL. M.: ‘Synthesis and characterisation of iron substituted apatite’, Adv. Appl. Ceram., 2012, 111, (8), 466–471.
13.
WeiW., LiuY., ZhouK. and HuangB.: ‘Effect of Fe addition on sintering behaviour of titanium powder’, Powder Metall., 2003, 46, (3), 246–250.
KwehS. W. K., KhorK. A. and CheangP.: ‘The production and characterization of hydroxyapatite (HA) powders’, J. Mater. Process. Technol., 1999, 89–90, 373–377.
16.
DowlingN. E.: ‘Mechanical behaviour of materials: Engineering materials for deformation, fracture, and fatigue’, 570–617; 1993, Englewood Cliffs, NJ, Prentice-Hall Inc.
17.
KruzicJ. J. and RitchieR. O.: ‘Determining the toughness of ceramics from Vickers indentations using the crack-opening displacements: an experimental study’, J. Am. Ceram. Soc., 2003, 86, (8), 1433–1436.
18.
DuttaS. K., MukhopadhyayA. K. and ChakrabortyD.: ‘Assessment of strength by young's modulus and porosity: a critical evaluation’, J. Am. Ceram. Soc., 1988, 71, (11), 942–947.
19.
WaghA. S., SinghJ. P. and PoeppelR. B.: ‘Dependence of ceramic fracture properties on porosity’, J. Mater. Sci., 1993, 28, (13), 3589–3593.
SunX. D. and YeomansJ.: ‘Optimization of a ductile-particle-toughened ceramic’, J. Am. Ceram. Soc., 1996, 79, (10), 2705–2717.
22.
GattoA.: ‘Critical evaluation of indentation fracture toughness measurements with Vickers indenter on ceramic matrix composite tools’, J. Mater. Proc. Tech., 2006, 174, (1), 67–73.