Polycrystalline samples of lanthanum modified bismuth titanate ceramics with composition Bi3·25La0·75Ti3O12 (BLT) were prepared at three different sintering temperatures (1050, 1100 and 1150°C) using M-PVA gel ignition technique. The samples were characterised for structural and electrical properties. A significant amount of as burnt BLT powder was found to be crystalline in nature having a yellowish colour. Very fine BLT nanoparticles were characterised by TEM analysis. Single phase with orthorhombic crystal structure was observed for all the samples, confirmed by X-ray analysis. Dielectric properties were studied as a function of frequency and temperature. More than 95% relative density was observed for all the three sintered samples. The sample sintered at 1100°C showed highest dielectric constant and relative density and lowest loss.
ChuMW, GanneM, CaldesMT, BrohanL: ‘X-ray photoelectron spectroscopy and high resolution electron microscopy studies of Aurivillius compounds: Bi4−xLaxTi3O12 (x = 0, 0.5, 0.75, 1.0, 1.5, and 2.0)’, J. Appl. Phys., 2002, 91, 3178–3187.
2.
CummingsSE, CrossLE: ‘Electrical and optical properties of ferroelectric Bi4Ti3O12’, J. Appl. Phys., 1968, 39, 2268–2274.
3.
HardyA, MondelaersD, VanhoylandG, van BaelMK, MullensJ, van PouckeLC: ‘The formation of ferroelectric bismuth titanate (Bi4Ti3O12) from an aqueous metal–chelate gel’, J. Sol–Gel Sci. Technol., 2003, 26, 1103–1107.
4.
ParkBH, KangBS, BuSD, NohTW, LeeJ, JoW: ‘Lanthanum-substituted bismuth titanate for use in non-volatile memories’, Nat. Lett., 1999, 401, 682–685.
5.
WatanabeT, FunakuboH, OsadaM, NoguchiY, MiyayamaM: ‘Effect of cosubstitution of La and V in Bi4Ti3O12 thin films on the low-temperature deposition’, Appl. Phys. Lett., 2002, 80, 100–102.
6.
BèaH, BibesM, FusihS, WycziskF, ForgetA, LebeugleD, ColsonD, ViretM: ‘Influence of parasitic phase on the properties of BiFeO3 epitaxial thin film’, Appl. Phys. Lett., 2005, 87, 072508.
7.
SimõesAZ, StojanovicBD, RamirezMA, CavalheiroAA, LongoE, VarelaJA: ‘Lanthanum-doped Bi4Ti3O12 prepared by the soft chemical method: Rietveld analysis and piezoelectric properties’, Ceram. Int., 2008, 34, 257–261.
8.
JiangAQ, LiHG, ZhangLD: ‘Dielectric study in nanocrystalline Bi4Ti3O12 prepared by chemical co-precipitation’, J. Appl. Phys., 1998, 83, 4878–4883.
9.
HornJA, ZhangSC, SelvarajU, MessingGL, Trolier-McKinstryS: ‘Templated grain growth of textured bismuth titanate’, J. Am. Ceram. Soc., 1999, 82, 921–926.
10.
KongLB, MaJ, ZhuW, TanOK: ‘Preparation of Bi4T3O12 via a high-energy ball milling process’, Mater. Lett., 2001, 51, 108–114.
11.
HardyA, MondelaersD, van BaelMK, MullensJ, van PouckeLC, VanhoylG, D'HaenJ: ‘Synthesis of (Bi,La)4Ti3O12 by a new aqueous solution-gel route’, J. Eur. Ceram. Soc., 2004, 24, 905–909.
12.
RoyS, BysakhS, GoswamiMLN, JanaD, SubrahmanyamJ: ‘Single-step synthesis of ultrafine PLZT from polymer gel precursor: synthesis, consolidation and dielectric properties’, Chem. Mater., 2007, 19, 2622–2629.
13.
RoyS, BysakhS, SubrahmanyamJ: ‘Metastable face-centered cubic lead zirconate titanate (PZT) and lead lanthanum zirconate titanate (PLZT) nanocrystals synthesized by auto-ignition of metal–polymer gel’, J. Mater. Res., 2008, 23, 719–724.
14.
RoyS, SinghS, KumarP: ‘Structural and dielectric properties of PMN-PT (65/35) bulk ceramics synthesized by metal–polymer gel auto ignition route’, Integr. Ferroelectr., 2010, 119, 82–88.
15.
RoyS: ‘Nanostructured PZT synthesized from metal–polyvinyl alcohol gel: studies on metal–polymer interaction’, J. Appl. Polym. Sci., 2008, 110, 2693–2697.
16.
AhnCW, LeeHJ, KangSH, KimW, ChoiMS, LeeJS, KimHW, JinBM: ‘Structure dependence of the ferroelectric properties of Bi3.25Ln0.75Ti 3O12 (Ln = La, Nd, Sm, Dy) ceramics’, J. Electroceram., 2008, 21, 847–850.
17.
RoyS, BysakhS: ‘Ultrafine PZT based ceramics synthesized by auto-ignition of metal–polymer gel: enhanced sinterablity and higher remnant polarization’, Mater. Chem. Phys., 2011, 126, 948–954.
18.
SimõesAZ, QuinelatoC, RiesA, StojanovicBD, LongoE, VarelaJA: ‘Preparation of lanthanum doped Bi4Ti3O12 ceramics by the polymeric precursor method’, Mater. Chem. Phys., 2006, 98, 481–485.
19.
MalJ, ChoudharyRNP: ‘Diffuse phase transitions in Li modified PLZT ceramics’, Phase Transit., 1997, 62, 119–133.
OkazakiK: ‘Developments in fabrication of piezoelectric ceramics’, Ferroelectrics, 1982, 41, 77–96.
22.
HiroshimaTT K, KimuruT: ‘Effects of microstructure and composition on the Curie temperature of lead barium niobate solid solutions’, J. Am. Ceram. Soc., 1996, 79, 3235–3242.
23.
KimuraT, MiyamotoS, YamaguchiT: ‘Microstructure development and dielectric properties of potassium strontium niobate ceramics’, J. Am. Ceram. Soc., 1990, 73, 127–130.