To investigate the excess hydrolysis of titanium alkoxides, TiO2 powders were fabricated from titanium tetraisopropoxide using 6∶1 and 100∶1 H2O/Ti (r) ratios. The powders were dried and fired at a range of temperatures (⩽800°C). Hydroxylation and organic content in powders were characterised using attenuated total reflectance Fourier transform infrared spectroscopy (FTIR), laser Raman microspectroscopy and elemental microanalysis; surface area and pore size distribution were evaluated using N2 gas adsorption; phase composition was analysed using X-ray diffraction (XRD) and laser Raman microspectroscopy; and crystallite size was evaluated by XRD, TEM and SEM. Results showed near complete hydrolysis in a predominantly aqueous medium (r = 100), resulting in precipitated crystalline powders exhibiting brookite and anatase, which begin to transform to rutile below 500°C. The powders precipitated in a predominantly organic medium (r = 6) underwent partial hydrolysis, were highly porous and exhibited an amorphous structure, with the crystallisation of anatase occurring at ∼300°C and the transformation to rutile beginning at 500–600°C.
BalasubramanianG, DionysiouDD, SuidanMT, BaudinI, LanJM: ‘Evaluating the activities of immobilized TiO2 powder films for the photocatalytic degradation of organic contaminants in water’, Appl. Catal. B: Environ., 2004, 47B, (2), 73–84.
2.
ByrneJA, EgginsBR, BrownNMD, McKinneyB, RouseM: ‘Immobilisation of TiO2 powder for the treatment of polluted water’, Appl. Catal. B: Environ., 1998, 17B, (1–2), 25–36.
3.
HurJ, KohY: ‘Bactericidal activity and water purification of immobilized TiO2 photocatalyst in bean sprout cultivation’, Biotechnol. Lett., 2002, 24, (1), 23–25.
FujiharaK, OhnoT, MatsumuraM: ‘Splitting of water by electrochemical combination of two photocatalytic reactions on TiO2 particles’, J. Chem. Soc., Faraday Trans., 1998, 94, 3705–3709.
6.
FujishimaA, HondaK: ‘Electrochemical photolysis of water at a semiconductor electrode’, Nature, 1972, 238, (5358), 37–38.
7.
NiM, LeungM, LeungD, SumathyK: ‘A review and recent developments in photocatalytic water-splitting using TiO2 for hydrogen production’, Renew. Sustain. Energy Rev., 2007, 11, 401–425.
8.
LucaV, OsborneM, SizgekD, GriffithC, AraujoPZ: ‘Photodegradation of methylene blue using crystalline titanosilicate quantum-confined semiconductor’, Chem. Mater., 2006, 18, (26), 6132–6138.
9.
ManessPC, SmolinskiS, BlakeDM, HuangZ, WolfrumEJ, JacobyWA: ‘Bactericidal activity of photocatalytic TiO2 reaction: toward an understanding of its killing mechanism’, Appl. Environ. Microbiol., 1999, 65, (9), 4094.
10.
WeiC, LinWY, ZainalZ, WilliamsNE, ZhuK, KruzicAP, SmithRL, RajeshwarK: ‘Bactericidal activity of TiO2 photocatalyst in aqueous media: toward a solar-assisted water disinfection system’, Environ. Sci. Technol., 1994, 28, (5), 934–938.
11.
AbeR, SayamaK, DomenK, ArakawaH: ‘A new type of water splitting system composed of two different TiO2 photocatalysts (anatase, rutile) and a IO3−/I− shuttle redox mediator’, Chem. Phys. Lett., 2001, 344, (3–4), 339–344.
12.
FotouGP, VemuryS, PratsinisSE: ‘Synthesis and evaluation of titania powders for photodestruction of phenol’, Chem. Eng. Sci., 1994, 49, (24), 4939–4948.
13.
BacsaRR, KiwiJ: ‘Effect of rutile phase on the photocatalytic properties of nano-crystalline titania’, Appl. Catal. B: Environ., 1998, 16B, 19–29.
14.
ReverchonE, CaputoG, CorreraS, CestiP: ‘Synthesis of titanium hydroxide nanoparticles in supercritical carbon dioxide on the pilot scale’, J. Supercrit. Fluids, 2003, 26, (3), 253–261.
15.
KobayakawaK, MurakamiY, SatoY: ‘Visible-light active N-doped TiO2 prepared by heating of titanium hydroxide and urea’, J. Photochem. Photobiol. A: Chem., 2005, 170A, (2), 177–179.
16.
JeanJ, RingT: ‘Nucleation and growth of monosized titania powders from alcohol solution’, Langmuir, 1986, 2, (2), 251–255.
17.
YoldasBE: ‘Hydrolysis of titanium alkoxide and effects of hydrolytic polycondensation parameters’, J. Mater. Sci., 1986, 21, (3), 1087–1092.
18.
BarringerEA, BowenHK: ‘High-purity, monodisperse TiO2 powders by hydrolysis of titanium tetraethoxide. 1. Synthesis and physical properties’, Langmuir, 1985, 1, (4), 414–420.
19.
MahshidS, AskariM, GhamsariMS: ‘Synthesis of TiO2 nanoparticles by hydrolysis and peptization of titanium isopropoxide solution’, J. Mater. Process. Technol., 2007, 189, (1–3), 296–300.
20.
OskamG, NelloreA, PennRL, SearsonPC: ‘The growth kinetics of TiO2 nanoparticles from titanium (IV) alkoxide at high water/titanium ratio’, J. Phys. Chem. B, 2003, 107B, (8), 1734–1738.
BradleyDC, MehrotraRC, RothwellI, SinghA: ‘Alkoxo and aryloxo derivatives of metals’; 2001, Academic Press. San Diego, CA, USA.
23.
ChenYF, LeeCY, YengMY, ChiuHT: ‘The effect of calcination temperature on the crystallinity of TiO2 nanopowders’, J. ryst. Growth, 2003, 247, (3–4), 363–370.
24.
HagueDC, MayoMJ: ‘Controlling crystallinity during processing of nanocrystalline titania’, J. Am. Ceram. Soc., 1994, 77, (7), 1957–1960.
25.
StummW, MorganJJ: ‘Aquatic chemistry’; 1970, Chichester, John Wiley & Sons, Hoboken, NJ, USA.
26.
MahshidS, AskariM, Sasani GhamsariM, AfsharN, LahutiS: ‘Mixed-phase TiO2 nanoparticles preparation using sol–gel method’, J. Alloys Compd, 2009, 478, (1–2), 586–589.
27.
SongKC, PratsinisSE: ‘Synthesis of bimodally porous titania powders by hydrolysis of titanium tetraisopropoxide’, J. Mater. Res., 2000, 15, (11), 2322–2329.
28.
KimJ, Chang SongK, PratsinisSE: ‘The effect of hydrolysis temperature on synthesis of bimodally nanostructured porous titania’, J. Nanopart. Res., 2000, 2, (4), 419–424.
29.
BischoffBL, AndersonMA: ‘Peptization process in the sol–gel preparation of porous anatase (TiO2)’, Chem. Mater., 1995, 7, (10), 1772–1778.
30.
SongKC, PratsinisSE: ‘Control of phase and pore structure of titania powders using HCl and NH4OH catalysts’, J. Am. Ceram. Soc., 2001, 84, (1), 92–98.
31.
KominamiH, IshiiY, KohnoM, KonishiS, KeraY, OhtaniB: ‘Nanocrystalline brookite-type titanium (IV) oxide photocatalysts prepared by a solvothermal method: correlation between their physical properties and photocatalytic activities’, Catal. Lett., 2003, 91, (1), 41–47.
32.
SclafaniA, HerrmannJM: ‘Comparison of the photoelectronic and photocatalytic activities of various anatase and rutile forms of titania’, J. Phys. Chem., 1996, 100, 13655–13661.
BakardjievaS, StenglV, SzatmaryL, SubrtJ, LukacJ, MurafaN, NiznanskyD, CizekK, JirkovskyJ, PetrovaN: ‘Transformation of brookite-type TiO2 nanocrystals to rutile: correlation between microstructure and photoactivity’, J. Mater. Chem., 2006, 16, (18), 1709–1716.
35.
HurumDC, AgriosAG, GrayKA, RajhT, ThurnauerMC: ‘Explaining the enhanced photocatalytic activity of Degussa P25 mixed-phase TiO2 using EPR’, J. Phys. Chem. B, 2003, 107B, (19), 4545–4549.
36.
LiuG, WangL, YangHG, ChengHM, LuGQM: ‘Titania-based photocatalysts – crystal growth, doping and heterostructuring’, J. Mater. Chem., 2009, 20, (5), 831–843.
37.
GribbAA, BanfieldJF: ‘Particle size effects on transformation kinetics and phase stability in nanocrystalline TiO2’, Am. Mineral., 1997, 82, (7–8), 717–728.
38.
KlugHP, AlexanderLE: ‘X-ray diffraction procedures: for polycrystalline and amorphous materials’, Vol. 1, 2nd edn, 992; 1974, Weinheim, Wiley-VCH, Weinheim, Germany.
39.
PattersonA: ‘The Scherrer formula for X-ray particle size determination’, Phys. Rev., 1939, 56, (10), 978.
40.
SpurrRA, MyersH: ‘Quantitative analysis of anatase–rutile mixtures with an X-ray diffractometer’, Anal. Chem., 1957, 29, (5), 760–762.
41.
LiJG, IshigakiT, SunX: ‘Anatase, brookite, and rutile nanocrystals via redox reactions under mild hydrothermal conditions: phase-selective synthesis and physicochemical properties’, J. Phys. Chem. C, 2007, 111C, (13), 4969–4976.
42.
SocratesG: ‘Infrared and Raman characteristic group frequencies: tables and charts’; 2004, Weinheim, Wiley.
43.
MeagherEP, LagerGA: ‘Polyhedral thermal expansion in the TiO2 polymorphs; refinement of the crystal structures of rutile and brookite at high temperature’, Can. Mineral., 1979, 17, (1), 77.
44.
JiangH, RühleM, LaverniaE: ‘On the applicability of the X-ray diffraction line profile analysis in extracting grain size and microstrain in nanocrystalline materials’, J. Mater. Res., 1999, 14, (02), 549–559.
45.
HanaorDAH, SorrellCC: ‘Review of the anatase to rutile phase transformation’, J. Mater. Sci., 2011, 46, (4), 855–874.
46.
LowellS, ShieldsJE: ‘Powder surface area and porosity’; 1991, New York, Chapman and Hall, London, UK.
47.
CondonJB: ‘Surface area and porosity determinations by physisorption: measurements and theory’; 2006, Amsterdam, Elsevier.
48.
KingeryWD, BowenHK, UhlmannDR: ‘Introduction to ceramics’, 2nd edn; 1976, New York, Wiley-Interscience.
49.
ChenJ, GaoL, HuangJ, YanD: ‘Preparation of nanosized titania powder via the controlled hydrolysis of titanium alkoxide’, J. Mater. Sci., 1996, 31, (13), 3497–3500.
50.
DingXZ, QiZZ, HeYZ: ‘Effect of hydrolysis water on the preparation of nano-crystalline titania powders via a sol–gel process’, J. Mater. Sci. Lett., 1995, 14, (1), 21–22.
51.
OvenstoneJ, YanagisawaK: ‘Effect of hydrothermal treatment of amorphous titania on the phase change from anatase to rutile during calcination’, Chem. Mater., 1999, 11, (10), 2770–2774.
52.
HyoungGL, ZuoJM: ‘Growth and phase transformation of nanometer sized titanium oxide powders produced by the precipitation method’, J. Am. Ceram. Soc., 2004, 87, (3), 473–479.
53.
HuY, TsaiHL, HuangCL: ‘Effect of brookite phase on the anatase-rutile transition in titania nanoparticles’, J. Eur. Ceram. Soc., 2003, 23, (5), 691–696.
54.
PennRL, BanfieldJF: ‘Formation of rutile nuclei at anatase twin interfaces and the phase transformation mechanism in nanocrystalline titania’, Am. Mineral., 1999, 84, (5–6), 871–876.
55.
LakshmiS, RenganathanR, FujitaS: ‘Study on TiO2-mediated photocatalytic degradation of methylene blue’, J. Photochem. Photobiol. A: Chem., 1995, 88A, (2–3), 163–167.
56.
ZhangQ, GaoL, GuoJ: ‘Effect of hydrolysis conditions on morphology and crystallization of nanosized TiO2 powder’, J. Eur. Ceram. Soc., 2000, 20, (12), 2153–2158.
57.
DingX, LiX: ‘Correlation between anatase to rutile transformation and grain growth in nanocrystalline titania powders’, J. Mater. Res., 1998, 13, (9), 2556–2559.
58.
IidaY, OzakiS: ‘Grain growth and phase transformation of titanium oxide during calcination’, J. Am. Ceram. Soc., 1961, 44, (3), 120–127.
59.
ZhangYH, RellerA: ‘Phase transformation and grain growth of doped nanosized titania’, Mater. Sci. Eng. C, 2002, C19, (1–2), 323–326.
60.
HanaorD, MichelazziM, ChenuJ, LeonelliC, SorrellCC: ‘The effects of firing conditions on the properties of electrophoretically deposited titanium dioxide films on graphite substrates’, J. Eur. Ceram. Soc., 2011, 31, (15), 2877–2885.
61.
ZhangQ, GaoL, GuoJ: ‘Effects of calcination on the photocatalytic properties of nanosized TiO2 powders prepared by TiCl4 hydrolysis’, Appl. Catal. B: Environ., 2000, 26B, 207–215.
62.
TianG, FuH, JingL, XinB, PanK: ‘Preparation and characterization of stable biphase TiO2 photocatalyst with high crystallinity, large surface area, and enhanced photoactivity’, J. Phys. Chem. C, 2008, 112C, (8), 3083–3089.