The resistance offered by three ceramic materials of varying strength that have been subjected to explosive loading has been investigated by depth-of-penetration testing. Each material was completely penetrated by a tungsten carbide cored projectile and the residual penetration into a ductile aluminium alloy backing material was measured. The resulting ballistic performance of each damaged ceramic was found to be similar implying that the resistance offered to the projectile by the damaged ceramic is not dependent on the intrinsic strength properties of the intact material. This was taken as evidence that the important controlling parameter for enhancing the ballistic performance of a damaged ceramic material was not the strength of the ceramic but rather the fragment morphology.
HolmquistTJ, JohnsonGR: ‘Response of silicon carbide to high velocity impact’, J. Appl. Phys., 2002, 91, 5858–5866.
2.
JohnsonGR, HolmquistTJ: ‘Some observations on the strength of failed ceramic’, Ceram. Eng. Sci. Proc., 2006, 26, (7), 3–10.
3.
LankfordJ: ‘The role of dynamic material properties in the performance of ceramic armor’, Int.J. Appl. Ceram. Technol., 2004, 1, (3), 205–210.
4.
AndersonCE, BehnerT, OrphalDL, NichollsAE, TempletonDW: ‘Time-resolved penetration into pre-damaged hot-pressed silicon carbide’, Int. J. Impact Eng., 2008, 35, (8), 661–673.
5.
ChocronS, DannemannKA, NichollsAE, WalkerJD, AndersonCE: ‘A constitutive model for damaged and powder silicon carbide’, Ceram. Eng. Sci. Proc., 2005, 26, (7), 35–42.
6.
HorsfallI, EdwardsMR, HallasMJ: ‘The ballistic and physical properties of highly fractured alumina’, Adv. Appl. Ceram., 2010, 109, (8), 498–503.
7.
DannemannKA, NichollsAE, ChocranS, WalkerJD: ‘Compression testing and response of SiC-N ceramics: intact, damaged and powder’, Ceram. Eng. Sci. Proc., 2005, 26, (7), 109–116.
8.
WalleySM: ‘Historical review of high strain rate and shock properties of ceramics relevant to their application in armour’, Adv. Appl. Ceram., 2010, 109, (8), 446–466.
9.
WoodwardRL, BaxterBJ: ‘Ballistic evaluation of ceramics: influence of test conditions’, Int. J. Impact Eng., 1994, 15, 119–124.
10.
RobersonC, HazellPJ: ‘Resistance of silicon carbide to penetration by a tungsten carbide cored projectile’, Ceram. Trans., 2003, 151, 165–174.
HazellPJ, RobersonC, MoutinhoM: ‘The design of mosaic armour: the influence of tile-size on the ballistic performance’, Mater. Des., 2008, 29, (8), 1497–1503.
13.
HazellPJ, FellowsNA, HetheringtonJG: ‘A note on the behind armour effects from perforated alumina/aluminium targets’, Int. J. Impact Eng., 1998, 21, 589–595.
14.
RayD, FlindersR, AndersonA, CutlerR: ‘Effect of room-temperature hardness and toughness on the ballistic performance of SiC-based ceramics’, Ceram. Eng. Sci. Proc., 2005, 26, (7), 131–142.
15.
AndersonCE, Royal-TimmonsSA: ‘Ballistic performance of confined 99.5%-Al203 ceramic tiles’, Int. J. Impact Eng., 1997, 19, 703–713.
16.
FranzenRR, OrphalDL, AndersonCE: ‘The influence of experimental design on depth-of-penetration (DOP) test results and derived ballistic efficiencies’, Int. J. Impact Eng., 1997, 19, (8), 727–737.
17.
JamesB: ‘The influence of material properties of alumina on ballistic performance’, Proc. 15th Int. Symp. on ‘Ballistics’, May 1995, Jerusalem, Israel, (ADPA), 3–9.
18.
HohlerV, WeberK, ThamR, JamesB, BarkerA, PickupI: ‘Comparative analysis of oblique impact on ceramic composite systems’, Int. J. Impact Eng., 2001, 26, 333–344.
19.
RosenbergZ, YeshurunY, BlessSJ, OkajimaK:‘A new definition of ballistic efficiency of brittle materials based on the use of thick backing plates’ in ‘Impact loading and dynamic behaviour of materials’(, ChiemC Y, et al.), 491–498; 1988, Oberursel, DGM Informationsgesellschaft mbH.
20.
RosenbergZ, YeshurunY: ‘The relation between ballistic efficiency and compressive strength of ceramic tiles’, Int. J. Impact Eng., 1988, 7, (3), 357–362.
21.
WoodwardRL, GoochWA, O'DonnellRG, PerciballiWJ, BaxterBJ, PattieSD: ‘A study of fragmentation in the ballistic impact of ceramics’, Int. J. Impact Eng., 1994, 15, (5), 605–618.
22.
HazellPJ: ‘Measuring the strength of brittle materials by depth-of-penetration testing’, Adv. Appl. Ceram., 2010, 109, (8), 504–510.
23.
HearstJR, LynchCS: ‘Measurement of in situ strength using projectile penetration’, Int. J. Rock Mech. Min. Sci. Geomech. Abstr., 1994, 31, (3), 243–251.
KaurS, CutlerRA, ShettyDK: ‘Short-crack fracture toughness of silicon carbide’, J. Am. Ceram. Soc., 2009, 92, (1), 179–185.
26.
EdwardsMR, MathewsonA: ‘The ballistic properties of tool steel as a potential improvised armour plate’, Int. J. Impact Eng., 1997, 19, (4), 297–309.
27.
SapreS: ‘Measuring the material resisting force during projectile penetration’, Explosives Ordnance Engineering (EOE) MSc thesis, Cranfield Defence and Security, Cranfield University, Shrivenham, UK, July 2009.
28.
CurranDR, SeamanL, CooperT, ShockeyDA: ‘Micromechanical model for comminution and granular flow of brittle material under high strain rate application to penetration of ceramic targets’, Int. J. Impact Eng., 1993, 13, (1), 53–83.
29.
LuoH, ChenW: ‘Damage effects on the dynamic response of hot-pressed SiC-N’, Ceram. Eng. Sci. Proc., 2005, 26, (7), 117–122.
30.
MadhuaV, RamanjaneyuluK, Balakrishna BhatT, GuptaNK: ‘An experimental study of penetration resistance of ceramic armour subjected to projectile impact’, Int. J. Impact Eng., 2005, 32, 337–350.