A newer composition of self-flowing low cement brown fused alumina castable containing 971U type microsilica was developed. Optimum flow characteristics were achieved using water addition of 4·6 wt-%. This batch was sintered at different firing temperatures up to 1500°C. To understand the effect of both firing temperatures and corresponding phases, the present castable was characterised in terms of X-ray diffraction, scanning electron microscopy, bulk density (BD), apparent porosity (AP), water absorption (WA), cold crushing strength (CCS) and self-leveling flowability. The results revealed that gradual increase in firing temperature from 1100 through 1500°C caused low AP and WA, and high CCS properties due to the densification of the castable.
LeeW. E. and MooreR. E.: J. Am. Ceram. Soc., 1998, 81, 1385–410.
2.
LewisG.: In ‘Applications for traditional ceramics, refractories’, (ed. SchneiderS. J.), 895–918; 1991, Metals Park, OH, ASM International.
3.
StudartA. R. and PandolfelliV. C.: Am. Ceram. Soc. Bull, 2002, 81, 36–44.
4.
KrietzL. P., FisherR. E. and BeetzJ. G.: Ant Ceram. Soc. Bull, 1990, 69, 1690–1693.
5.
LeeW. E., VieiraW., ZhangS., Ghanbari AhariK., SarpoolakyH. and ParrC.: Int. Mater. Rev., 2001, 46, 145–167.
6.
BrachetF. G., AvisR., and ClavaudB.: Proc. Unified Int. Technical Conf. on ‘Refractories’, The German Refractories Association (GRA), Aachen, Germany, September1991, 186–188.
7.
DasS. K., SarkarR., MandalP. K. and MukherjeeS.: Am. Ceram. Soc. Bull, 2003, 82, 55–59.
8.
EvangelistaP. C. and ParrC.: Refrac. Appl. News, 2002, 7, 14–18.
9.
GerottoM. V., StudartA. R., InnocentiniM. D. M., PandolfelliV. C. and CaboS. S.: Am. Ceram. Soc. Bull., 2002, 81,40–47.
10.
MyhreeB. and HundereA. M.: Proc. 39th Int. Colloquium on ‘Refractories’, Verlag Stahleisen, Aachen, Germany, September1996, 184–188.
11.
StudartA. R., ZhongW. and PandolfelliV. C.: Am. Ceram. Soc. Bull., 1999, 78, 65–72.
12.
GerottoM. V., StudartA. R., PileggiR. G. and PandolfelliV. C.: Am. Ceram. Soc. Bull:, 2000, 79, 75–83.
MyhreB. and SandbergB.: Proc. Int. Semin. on ‘Monolithic refractory materials’, Presented at the International Seminar on Monolithic Refractory Materials, Tehran, Iran, Nov. 30 – Dec. 1, 1997, 133–140.
24.
MaterialsElkem ASA, PO Box 8126, Vaagsbygd, 4675Kristiansand, Norway.
25.
MyhreB.: Proc. XXIII Alafar Cong. on ‘Refractories’, Association Latinoamericana de Fabricantes de Refractarios (ALAFAR), Puerto Vallarta, Mexico, November1994, Asociacite Latinoamericana de Fabricantes de Refractarios, 160–171.
26.
PileggiR. G., StudartA. R. and PandolfelliV. C.: Am. Ceram. Soc. Bull, 2001, 80, 38–42.
27.
FrydaH., ScrivenerK., BierT. and EspinosaB.: Proc. Unified Int. Technical Conf. on ‘Refractories’, The American Ceramic Society (ACerS), New Orleans, USA, November1997, 1315–1323.
28.
ParrC., ValdeliévreB. and WöhrmeyerC.: Refrac. AppL News, 2002, 7, 17–23.
29.
de OliveriaI. R., StudartA. R., F. A. 0. Valenzuela and V. C. Pandolfelli: Certimica, 2003, 49, 11–16.
30.
ChakrabortyI. N.: Ceram. Int., 2004, 30, 487–490.
31.
InnocentiniM. D. M., PardoA. R. F. and PandolfelliV. C.: Proc. Unified Int. Technical Conf. on ‘Refractories’, The German Refractories Association (GRA), Berlin, Germany, September1999, 93–96.
32.
KriechbaumG. W., GnouckV., LaunchJ. O., StinnessenI., RoutschkaG. and van HeidjenJ. : Proc. XXXIX. Int. Feuerfest-Kolloquium on ‘Refractories’, Verlag Stahleisen, Aachen, Germany, September 1996, Forschungsgemeinschaft Feuerfest e.V, 211–218.
33.
FeldeborgH. and MyhreB.: Proc. Unified Int. Technical Conf. on ‘Refractories’, The German Refractories Association (GRA), Berlin, Germany, September1999, 90–92.
34.
MedvedovskiE.: Wear, 2001, 249, 821–828.
35.
EbadzadehT. and LeeW. E.: J. Eur. Ceram. Soc., 1998, 18, 837–848.
36.
ZawrahM. F. and KhalilN. M.: Ceram Int., 2001, 27, 689–694.