Alumina and zirconia were dispersed individually in aqueous media using Darvan C as the dispersant and at optimised pH condition. Based on sedimentation, rheology, yield stress, electrodeposition and zeta potential measurements, 2 wt-% of the dispersant and a pH of 10·5 were found to be the optimum condition for the codispersion of alumina and zirconia. Aqueous tape casting slurries with a solid loading of 32 wt-% were prepared under the optimised conditions of dispersion. Alumina–zirconia (50 : 50) composite tapes of 40 μm thickness and 56% green density were obtained.
MistierR. E. and TwinameE. R.: Tape casting-theory and practice; 1998, Westerville, OH, the American Ceramic Society.
3.
HotzaD. and GrielP.: Mater. Sci Eng. A, 1995, A202, 206–221.
4.
KristoffersonA.: Water-based tape casting of ceramics and fabrication of ceramic laminates, PhD thesis, Department of Ceramic technology, Chalmers University of Technology, Sweden, 1999.
5.
GutierrezC. A. and MorenoR.: Mater. Res. Bull., 2001, 36, 2059–2072.
6.
KrishnanB. and NatarajanR.: J. Mater. Set, 2005, 40, (20), 5511–5516.
7.
KrishnanB., SasidharanK. and NatarajanR.: Ferroelectrics, 2005, 327, 3–9.
8.
WangJ. and StevensR.: J. Mater. Sci., 1989, 24, 3421–3440.
9.
PlucknettK., CaceresC. H. and WillinsonD. S.: J. Am. Ceram. Soc., 1994, 77, (8), 2137–2144.
10.
RamanathanS., KrishnakumarK. P., DeP. K. and BanerjeeS.: J. Mater. Sci, 2004, 39, (10), 3339–3344.
11.
NavarroA., WhatmoreR. W. and AlcockJ. R.: J. Electroceram, 2004, 13, (1–3), 413–415.
12.
KimD. K. and KrivenW. M.: J. Am. Ceram. Soc., 2003, 86, (11), 1962–1964.
13.
LewisJ. A.: J. Am. Ceram. Soc., 2000, 83, (10), 2341–2359.
14.
MorenoR.: Ant Ceram. Soc. Bull., 1992, 71, (10), 1521–1531.
15.
OliveiraI. R., SepulvedaP. and PandolfelliV. C.: Am. Ceram. Soc. Bull., 2001, 80, (2), 47–53.
16.
DelisoE. M., CannonW. R. and RaoA. S.: in Advances in ceramics Vol. 24: science and technology of zirconia III’, (ed. S. Somiya et al.), 335—341; 1988, Westerville, OH, American Ceramic Society Inc.
17.
WernetJ. and FekeD. L.: J. Am. Ceram. Soc., 1994,77, (10), 2693–2698.
18.
VasanthakumariK. G. and NatarajanR.: Adv. Appl. Ceram., 2005, 104, (2), 73–78.
19.
ZupancieA., LapasinR. and KristoffersonA.: J. Eur. Ceram. Soc., 1998, 18, 467–477.
20.
RamakrishnanV., PradeepP. and MalghanS. G.: J. Am. Ceram. Soc, 1996, 79, (10), 2567–2576.
21.
IncorvatiC. M., LeeD. H., ReedJ. S. and CondrateR. A., Sr: Am. Ceram. Soc. Bull., 1997, 76, (9), 65–68.
22.
MaJ. T., XieZ. P., HuangY. and MiaoH. Z.: J. Mater. Set Lett., 2002, 21, 1163–1165.