Abstract
Ternary Al2O3-ZrO2-Y2O3 samples with a eutectic composition were prepared using the rapid quenching method, with some samples further annealed at 1300°C for 30 min and then slow cooled. The microstructural evolution was observed with XRD, SEM, and TEM. The SEM and TEM observations of the ternary samples agreed with the XRD. The rapid quenched sample was an amorphous phase with a small amount of crystalline phase mixed in. Observations showed that the rapid quenched and annealed sample was completely crystalline with a granular structure and well defined crystals of 40-60 nm in size.
Get full access to this article
View all access options for this article.
References
1.
Waku
Y.
,
Nakagawa
N.
,
Wakamoto
T.
,
Ohtsubo
H.
,
Shimizu
K.
and
Kohtoku
Y.
Nature , 1997 , 389 , 49 .
2.
Parthasarathy
T. A.
,
Mah
T. Y.
and
Matson
L. E.
J. Am. Ceram. Soc. , 1993 , 76 , 29 .
3.
Waku
Y.
,
Ohtsubo
H.
,
Nakagawa
N.
and
Koutoku
Y.
J. Mater. Sci , 1996 , 31 , 4663 .
4.
Waku
Y.
,
Nakagawa
N.
,
Ohtsubo
H.
,
Ohsora
Y.
and
Kohtoku
Y.
J. Jpn Inst. Mater. , 1995 , 59 , 71 .
5.
Yoshikawa
A.
,
Epelbaum
B.M.
,
Fukuda
T.
,
Suzuki
K.
and
Waku
Y.
Jpn J. Appl. Phys. , 1999 , 38 , L55 .
6.
Schmid
F.
and
Viechnicki
D.
J. Mater. Sci , 1970 , 5 , 470 .
7.
Bourban
S.
,
Karapatis
N.
,
Hopmann
H.
and
Kurz
W.
Acta Mater. , 1997 , 45 , 5069 .
8.
Ando
T.
and
Shiohara
Y.
J. Am. Ceram. Soc. , 1991 , 74 , 410 .
9.
Fischer
G. R.
,
Manfredo
L. J.
,
McNally
R. N.
and
Do-man
R. C.
J. Mater. Sci , 1981 , 16 , 3447 .
10.
Echigoya
J.
,
Takabayashi
Y.
,
Suto
H.
and
Ishigame
M.
J. Mater. Set Lett. , 1986 , 5 , 150 .
11.
Amano
T.
and
Yamaguchi
M.
Solar Energy Mater. Solar Cells , 2001 , 66 , 579 –583 .
12.
Sai
H.
,
Yugami
H.
,
Nakamura
K.
,
Nakagawa
N.
,
Ohtsubo
H.
and
Maruyama
S.
Jpn J. Appl. Phys. , 2000 , 39 , 1957 –1961 .
13.
Nakagawa
N.
,
Ohtsubo
H.
,
Waku
Y.
and
Yugami
H.
J. Eur. Ceram. Soc. , 2005 , 25 , 1285 –1291 .
14.
Lee
J. H.
,
Yoshikawa
A.
and
Fukuda
T.
J. Eur. Ceram. Soc. , 2005 , 25 , 1351 –1354 .
15.
Dynys
F. W.
and
Sayir
A.
J. Eur. Ceram. Soc. , 2005 , 25 , 1293 –1299 .
16.
Larrea
A.
and
Orera
V. M.
J. Cryst. Growth , 2007 , 300 , 387 –393 .
17.
Han
Y. H.
,
Nagata
M.
,
Uekawa
N.
and
Kakegawa
K.
Brit. Ceram. Trans. , 2004 , 103 , 219 –222 .
18.
Lakiza
S. M.
and
Lopato
L. M.
Stable and metastable phase relations in the system alumina and zirconia and yttria ’, J. Am. Ceram. Soc. , 1997 , 80 , (4 ), 893 –902 .
19.
Cullity
B. D.
and
Stock
S. R.
Elements of X-ray diffraction ’, 3rd edn, Chap . 5 ; 2001 , London , Prentice Hall .