Observation of the unconventional properties and material behaviour expected in the nanometre grain size range necessitates the fabrication of fully dense bulk nanostructured ceramics. This is achieved by the application of ceramic nanoparticles and suitable densification conditions, both for the green and sintered compacts. Various sintering and densification strategies were adopted, including pressureless sintering, hot pressing, hot isostatic pressing, microwave sintering, sinter forging, and spark plasma sintering. The theoretical aspects and characteristics of these processing techniques, in conjunction with densification mechanisms in the nanocrystalline oxides, were discussed. Spherical nanoparticles with narrow size distribution are crucial to obtain homogeneous density and low pore-to-particle-size ratio in the green compacts, and to preserve the nanograin size at full densification. High applied pressure is beneficial via the densification mechanisms of nanoparticle rearrangement and sliding, plastic deformation, and pore shrinkage. Low temperature mass transport by surface diffusion during the spark plasma sintering of nanoparticles can lead to rapid densification kinetics with negligible grain growth.
BurggraafA. J., WinnubstA. J. A. and VeweijH.: In ‘Third Euro-ceramics’, (eds. P. Duran and J. F. Fernandez), Vol. 3, 561–576; 1993, Spain, Faenza Editrice Iberica S.L.
2.
CocksA. C. F.: Acta Metall. Mater., 1994, 42, 2191–2210.
3.
AndrievskiR. A.: J. Mater. Set, 1994, 29, 614–631.
4.
GrozaJ. R. and DowdingR. J.: NanoStrue. Mater., 1996, 7, 749–768.
5.
MayoM. J.: Inter. Mater. Rev., 1996, 41, 85–115.
6.
KingeryW. D. and FrancoisB.: In ‘Sintering and related phenomena’, (eds. G. C. Kuczynski, N. A. Hooton and C. F. Gibbon), 471–498; 1967, New York, Gordon and Breach.
7.
BannisterM. J.: In ‘Sintering and related phenomena’, (eds. G. C. Kuczynski, N. A. Hooton and C. F. Gibbon), 581–605; 1967, New York, Gordon and Breach.
8.
SlamovichE. B. and LangeF. F.: J. Am. Ceram. Soc., 1993, 76, 1584–1590.
9.
AkashA. and MayoM. J.: J. Am. Ceram. Soc., 1999, 82, 2948–2952.
10.
WakaiF., AkatsuT. and ShinodaY.: Acta Mater., 2006, 54, 793–805.
11.
ShihW. Y., ShihW-H. and AksayI.: J. Mater. Res., 1995, 10, 1000–1015.
12.
MatijevicE.: In ‘Ultrastructure processing of advanced ceramics’, (eds. J. D. Mackenzie, and D. R. Ulrich), 429–442; 1988, New York, Wiley.
13.
LiJ.-G., IkegamiT., LeeJ.-H. and MoriT.: Acta Mater., 2001, 49, 419–426.
VesteghemH., LecomteA. and DaugerA.: J. Non-Cryst. Solids, 1992, 147&148, 503— 507.
32.
HirataY., NakamuraM., MiyamotoM., TanakaY. and WangX. H.: J. Am. Ceram. Soc., 2006, 89, 1883–1889.
33.
SrdicV. V., WintererM. and HahnH.: J. Ant Ceram. Soc., 2000, 83, 729–736.
34.
JorandY., TahaM., MissiaenJ. M. and MontanaroL.: J. Eur. Ceram. Soc., 1995, 15, 469–477.
35.
HahnH., LogasJ. and AverbackR. S.: J. Mater. Res., 1990, 3, 609–614.
36.
TrunecM. and MacaK.: J. Am. Ceram. Soc., 2007, 90, 2735–2740.
37.
KrellA. and KlimkeJ.: J. Am. Ceram. Soc., 2006, 89, 1985–1992.
38.
AzarM., PalmeroP., LombardiM., GamierV., MontanaroL., FantozziG. and ChevalierJ.: J. Eur. Ceram. Soc., 2008, 28, 1121–1128.
39.
FreimJ., McKittrickJ., KatzJ. and SickafusK.: NanoStrue. Mater., 1994, 4, 371–385.
40.
PeelameduR., BadzianA., RoyR. and MartukanitzR. P.: J. Am. Ceram. Soc., 2004, 87, 1806–1809.
41.
Garcia-GananC., Melendez-MartinezJ. J., Gomez-GarciaD. and Dominguez-RodriguezA.: J. Mater. Set, 2006, 41, 5231–5234.
42.
HarmerM. P. and BrookR. J.: J. Brit. Ceram. Soc., 1981, 80, 147–148.
43.
MostaghaciH. and BrookR. J.: J. Brit. Ceram. Soc., 1981, 80, 148–149.
44.
FengC., QiuH., GuoJ., YanD. and SchulzeW. A.: J. Mater. Synthes. Process., 1995, 3, 25–29.
45.
FengC., ShiE., GuoJ., YanD. and SchulzeW. A.: J. Mater. Synthes. Process., 1995, 3, 31–37.
46.
ChenD.-J. and MayoM. J.: J. Am. Ceram. Soc., 1996, 79, 906–912.
47.
KimB.-C., LeeJ.-H., KimJ.-J. and IkegamiT.: Mater. Lett., 2002, 52, 114–119.
48.
ChenI.-W. and WangX.-H.: Nature, 2002, 404, 168–171.
49.
WangX.-H., ChenP.-L. and ChenI.-W.: J. Am. Ceram. Soc., 2006, 89, 431–437.
50.
WangX.-H., DengX.-Y., BaoH.-L., ZhouH., QuW.-G., LiL.-T. and ChenI.-W.: J. Am. Ceram. Soc., 2006, 89, 438–443.
51.
PolotaiA., BreeceK., DickeyE., RandallC. and RagulyaA.: J. Am. Ceram. Soc., 2005, 88, 3008–3012.
52.
BinnerJ., AnnapooraniK., PaulA., SantacruzI. and VaidhyanathanB.: J. Eur. Ceram. Soc., 2008, 28, 973–977.
53.
BinnerJ. and VaidhyanathanB.: J. Eur. Ceram. Soc., 2008, DOI: 10.1016/j.jeurceramsoc. 2007, 12, 24.
54.
MorganP. E. D. and ScalaE.: In ‘Sintering and related phenomena’, (eds. G. C. Kuczynski, N. A. Hooton and C. F. Gibbon), 861–894; 1967, New York, Gordon and Breach.
55.
VasilosT. and RhodesE.: In ‘Ultraflne-grain ceramics’, (eds. J. J. Burke, N. L. Reed and V. Weiss), 137–172; 1970, New York, Syracuse University Press.
GallasM. R., HockeyB., PechenikA. and PiermariniG. J.: J. Am. Ceram. Soc., 1994, 77, 2107–2112.
62.
MishraR. J., LesherC. E. and MukherjeeA. K.: J. Am. Ceram. Soc., 1996, 79, 2989— 2992.
63.
ItataniK., YasudaR., Scott HowellF. and KishiokaA.: J. Mater. Set, 1997, 32, 2977— 2984.
64.
EhreD., GutmanasE. Y. and ChaimR.: J. Eur. Ceram. Soc., 2005, 25, 3579–3585.
65.
RingT. A.: ‘Fundamentals of ceramic powder processing and synthesis’, 866; 1996, San Diego, Academic Press.
66.
SkandanG., HahnH., KearB. H., RoddyM. and CannonW. R.: Mater. Lett., 1994, 20, 305–309.
67.
RahamanM. N.: ‘Ceramic processing and sintering’, 515–516; 2003, New York, Marcel Dekker.
68.
WeibelA., BouchetR., BouvierP. and KnauthP.: Acta Mater., 2006, 54, 3575–3583.
69.
LiaoS.-C., K. d. Pae and MayoW. E.: NanoStruct. Mater., 1995, 5, 319–325.
70.
LiaoS.-C., ChenY.-J., MayoW. E. and KearB. H.: NanoStruct. Mater., 1999, 11, 553— 557.
71.
UchicM., HofflerH. J., FlickW. J., TaoR., KurathP. and AverbackR. S.: Scripta Met. Mater., 1992, 26, 791–796.
72.
LiJ., YeY., ShenL., ChenJ. and ZhouH.: Mater. Set Eng. A. 2006, A390, 265–270.
73.
HagueD. C. and MayoM. J.: J. Am. Ceram. Soc., 1997, 80, 149–156.
74.
HagueD. C. and MayoM. J.: Mater. Set Eng. A, 1995, A204, 83–89.
75.
Barrera-SolanoC., EsquiviasL. and PineroM.: J. Eur. Ceram. Soc., 1998, 18, 1429–1438.
76.
BoutzM. M. R., WinnubstA. J. A., BurggraafA. J., NauerM. and CaryC.: In ‘Science and technology of zirconia V’, (eds. S. Badwal, J. Bannister and R. Hannink), 275–283; 1993, Lancaster, PA, Technomic Pub. Co.
77.
ChaimR.: J. Mater. Res., 1999, 14, 2508–2517.
78.
KwonO.-H., NordahlC. S. and MessingG. L.: J. Am. Ceram. Soc., 1995, 78, 491–494.
79.
NordahlC. S. and MessingG. L.: J. Am. Ceram. Soc., 1996, 79, 3149–3154.
80.
KwonS., NordahlC. S. and MessingG. L.: Mater. Manufac. Process., 1996, 11, 969—985.
81.
LeeY. I., LeeJ.-H., HongS.-H. and KimD.-Y.: Mater. Res. Bull, 2003, 38, 925–930.
82.
NohJ. H., HongK. S., JungH. S. and LeeJ-K.: J. Electroceram., 2006, 17, 913–917.
83.
RisbudS. H., ShanC.-H., MukherjeeA. K., KimM. J., BowJ. S. and HollR. A.: J. Mater. Res., 1995, 10, 237–239.
84.
MishraR. S., RisbudS. H. and MukherjeeA. K.: J. Mater. Res., 1998, 13, 86–89.
85.
MishraR. S. and MukherjeeA. K.: Mater. Sci. Eng. A, 2000, A287, 178–182.